Insulating coating material for power distribution cabinet and preparation method of insulating coating material

A technology for insulating coatings and power distribution cabinets, applied in coatings, anti-corrosion coatings, fire-resistant coatings, etc., can solve problems such as rising air temperature, unsuitable air convection, and reduced service life, and achieve moderate viscosity, anti-corrosion performance and chemical inertness Strong and elastic effect

Inactive Publication Date: 2017-09-01
合肥励仙电力工程有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the wide application of electricity in social production and human life and the rapid development of electronics and communication technology, the power distribution cabinet, as an integral part of the substation, is exposed to harsh outdoor weather all year round and is susceptible to aging and reduced service life due to ultraviolet radiation.
[0003] On the other hand, the installation methods of the distribution box are divided into two types: surface installation and concealed installation. The heat dissipation effect of the exposed distribution box is better than that of the concealed installation. Poor, causing the temperature of the surrounding air in the distribution box to rise due to the temperature rise of the low-voltage circuit breaker

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An insulating coating material for a power distribution cabinet of the present embodiment includes the following raw materials in parts by weight:

[0032] 75 parts of modified water-based polyurethane emulsion, 8 parts of water-based alkyd resin, 4 parts of diethylenetriamine, 10 parts of cyclohexanone, 12 parts of ethyl acetate, 2 parts of aluminate coupling agent, 15 parts of thermally conductive filler, processing aid 10 parts of agent, 14 parts of ore additive powder, 7 parts of anti-crack fiber.

[0033] The coupling agent in this example is aluminate coupling agent DL-411.

[0034] The thermally conductive filler in this embodiment is a mixture of aluminum nitride, glass powder, barium sulfate and titanium dioxide in a weight ratio of 3:2:2:0.5.

[0035] The processing aid in this embodiment is a tackifier, a dispersant, a curing agent, a leveling agent, and a defoamer, and is composed of a mixture according to a weight ratio of 2:1:2:1:0.5; the tackifier is sub...

Embodiment 2

[0043] An insulating coating material for a power distribution cabinet of the present embodiment includes the following raw materials in parts by weight:

[0044] 85 parts of modified water-based polyurethane emulsion, 10 parts of water-based alkyd resin, 8 parts of diethylenetriamine, 14 parts of cyclohexanone, 15 parts of ethyl acetate, 3 parts of aluminate coupling agent, 25 parts of thermally conductive filler, processing aid 12 parts of agent, 18 parts of ore additive powder, 9 parts of anti-cracking fiber.

[0045] The coupling agent in this example is aluminate coupling agent DL-411AF.

[0046] The thermally conductive filler in this embodiment is a mixture of aluminum nitride, glass powder, barium sulfate and titanium dioxide in a weight ratio of 3:2:2:0.5.

[0047] The processing aid in this embodiment is a tackifier, a dispersant, a curing agent, a leveling agent, and a defoamer, and is composed of a mixture according to a weight ratio of 2:1:2:1:0.5; the tackifier ...

Embodiment 3

[0055] An insulating coating material for a power distribution cabinet of the present embodiment includes the following raw materials in parts by weight:

[0056] 80 parts of modified water-based polyurethane emulsion, 9 parts of water-based alkyd resin, 6 parts of diethylenetriamine, 12 parts of cyclohexanone, 13 parts of ethyl acetate, 2.5 parts of aluminate coupling agent, 20 parts of thermally conductive filler, processing aid 11 parts of agent, 16 parts of ore additive powder, and 8 parts of anti-cracking fiber.

[0057] The coupling agent in this example is aluminate coupling agent DL-411.

[0058] The thermally conductive filler in this embodiment is a mixture of aluminum nitride, glass powder, barium sulfate and titanium dioxide in a weight ratio of 3:2:2:0.5.

[0059] The processing aid in this embodiment is a tackifier, a dispersant, a curing agent, a leveling agent, and a defoamer, and is composed of a mixture according to a weight ratio of 2:1:2:1:0.5; the tackifi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an insulating coating material for a power distribution cabinet. The insulating coating material is prepared from the following raw materials in parts by weight: 75-85 parts of a modified waterborne polyurethane emulsion, 8-10 parts of waterborne alkyd resin, 4-8 parts of diethylenetriamine, 10-14 parts of cyclohexanone, 12-15 parts of ethyl acetate, 2-3 parts of an aluminate coupling agent, 15-25 parts of a thermal conducting filler, 10-12 parts of a processing aid, 14-18 parts of an ore adding powder and 7-9 parts of anticracking fiber. The insulating coating material has excellent insulating property, film-forming property and mechanical property, good high temperature resistance, excellent antiseptic and moisture-proof properties, good anti-ultraviolet property and ageing resistance, relatively high adhesive force and relatively good heat-conducting property; and meanwhile, according to the preparation method of the insulating coating material, the material cost is relatively low, the raw materials are available and the process is simple, so that the insulating coating material has relatively high practical value and a good application prospect.

Description

technical field [0001] The invention relates to the technical field of electric power distribution cabinets, in particular to an insulating coating material for electric power distribution cabinets and a preparation method thereof. Background technique [0002] In recent years, with the continuous development of my country's national economy, the demand for electricity has shown a rapid growth trend. In order to meet the needs of industrial and agricultural products and people's daily life, substations with a voltage level of 110kV and above are gradually built in the central area of ​​the city. Due to the wide application of electricity in social production and human life and the rapid development of electronics and communication technology, the power distribution cabinet, as an integral part of the substation, is exposed to harsh outdoor weather all the year round, and is susceptible to aging and reduced service life caused by ultraviolet radiation. [0003] On the other h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D167/08C09D5/25C09D5/08C09D7/00C09D7/12
CPCC09D175/04C08K2003/2241C08K2003/282C08K2003/3045C08L2201/08C08L2203/206C08L2205/035C08L2205/16C09D5/08C09D5/18C08L67/08C08L77/00C08K13/06C08K9/04C08K7/14C08K5/17C08K3/28C08K3/40C08K3/30C08K3/22
Inventor 伍文慧
Owner 合肥励仙电力工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com