Printing paint for self-luminous advertisements and preparation method thereof

A printing coating and self-illumination technology, applied in luminescent coatings, epoxy resin coatings, coatings, etc., can solve the problems of easy cracking of the coating film, weak weather resistance, poor adhesion, etc., and achieve good anti-sticking and anti-cracking The effect of strong resistance and small surface contact angle

Inactive Publication Date: 2017-09-08
HEFEI SIBOT SOFTWARE DEV CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing self-luminous coatings for the surface of billboards generally have the disadvantages of poor adhesion and weak weather resistance
Because billboards are exposed to the sun or rain for a long time, the wind and sun, and rain erosion, the coating film on the surface is easy to crack and fall off, especially at the bending part and other parts. In order to solve the problem of self-luminous coating For this shortcoming, it is necessary to develop self-luminous coating products with strong adhesion and good weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A printing coating for self-luminous advertisements, comprising the following raw materials in parts by weight: 25 parts of acrylic resin, 3 parts of rare earth luminescent powder, 10 parts of polyethylene wax, 5 parts of propyl acetate, 5 parts of epoxy resin, propylene glycol methyl ether acetic acid 2 parts of ester, 1 part of dimethyl carbonate, 2 parts of thickener, 2 parts of reactive diluent, 1 part of leveling agent, 2 parts of preservative, 20 parts of organic solvent, 1.5 parts of surface hydrophobic and anti-adhesive additive.

[0022] The inert solvent consists of diacetone alcohol, butyl ester and ethyl ester.

[0023] The mass ratio of the diacetone alcohol, butyl ester and ethyl ester is 2:5:1.

[0024] The reactive diluent is composed of trimethylolpropane triacrylate and tripropylene glycol diacrylate in a mass ratio of 3:2.

[0025] The organic solvent is selected from one or more of styrene, perchlorethylene, trichlorethylene, ethylene glycol ether a...

Embodiment 2

[0033] A printing coating for self-luminous advertisements, comprising the following raw materials in parts by weight: 30 parts of acrylic resin, 6 parts of rare earth luminescent powder, 15 parts of polyethylene wax, 10 parts of propyl acetate, 7 parts of epoxy resin, propylene glycol methyl ether acetic acid 6 parts of ester, 3 parts of dimethyl carbonate, 4 parts of thickener, 3 parts of reactive diluent, 7 parts of leveling agent, 4 parts of preservative, 25 parts of organic solvent, and 2.0 parts of surface hydrophobic and anti-adhesive additive.

[0034] Further, the inert solvent consists of diacetone alcohol, butyl ester and ethyl ester.

[0035] Further, the mass ratio of diacetone alcohol, butyl ester and ethyl ester is 2:6:1.

[0036] Further, the reactive diluent is composed of trimethylolpropane triacrylate and tripropylene glycol diacrylate in a mass ratio of 3:2.

[0037] Further, the organic solvent is selected from one or more of styrene, perchlorethylene, tr...

Embodiment 3

[0045] A printing paint for self-luminous advertisements, comprising the following raw materials in parts by weight: 35 parts of acrylic resin, 9 parts of rare earth luminescent powder, 20 parts of polyethylene wax, 15 parts of propyl acetate, 12 parts of epoxy resin, propylene glycol methyl ether acetic acid 8 parts of ester, 5 parts of dimethyl carbonate, 7 parts of thickener, 5 parts of reactive diluent, 10 parts of leveling agent, 6 parts of preservative, 30 parts of organic solvent, and 2.5 parts of surface hydrophobic and anti-adhesive additive.

[0046] Further, the inert solvent consists of diacetone alcohol, butyl ester and ethyl ester.

[0047] Further, the mass ratio of diacetone alcohol, butyl ester and ethyl ester is 3:7:1.

[0048] Further, the reactive diluent is composed of trimethylolpropane triacrylate and tripropylene glycol diacrylate in a mass ratio of 3:2.

[0049] Further, the organic solvent is selected from one or more of styrene, perchlorethylene, tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a printing paint for self-luminous advertisements. The printing paint comprises the following raw materials by weight: 25 parts of acrylic resin, 3 parts of rare earth luminescent powder, 10 parts of polyethylene wax, 5 parts of propyl acetate, 5 parts of epoxy resin, 2 parts of propylene glycol methyl ether acetate, 1 part of dimethyl carbonate, 2 parts of a thickening agent, 2 parts of an active diluent, 1 part of a leveling agent, 2 parts of a preservative, 20 parts of an organic solvent, an d1.5 parts of a surface hydrophobic anti-sticking assistant. According to the printing paint for self-luminous advertisements and a preparation method thereof provided by the invention, the prepared printing paint does not crack easily, has strong cracking resistance, can withstand whatever weather and the erosion of rainwater. The paint uses acrylic resin and rare earth luminescent powder as the carrier, adopts the organic solvent as the solvent, and is added with the surface hydrophobic anti-sticking assistant, and after the paint forms a film, the surface contact angle is small, and the adhesion resistance is good.

Description

technical field [0001] The invention belongs to the field of advertisement printing, and in particular relates to a printing coating for self-luminous advertisement and a preparation method thereof. Background technique [0002] Self-illuminating coatings use the principle of self-illumination. When there is light, the coating can store light for 1 hour to reach light energy saturation. When there is no light, the self-luminous coating uses the stored light energy to emit light for more than 12 hours. It has been widely used in outdoor billboards, traffic facility signs and other fields. [0003] However, the existing self-luminous coatings for the surface of billboards generally have the disadvantages of poor adhesion and weak weather resistance. Because billboards are exposed to the sun or rain for a long time, the wind and sun, and rain erosion, the coating film on the surface is easy to crack and fall off, especially at the bending part and other parts. In order to solv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D123/06C09D163/00C09D5/22C09D7/00
CPCC09D133/00C08L2205/03C09D5/22C08L23/06C08L63/00
Inventor 吴青明
Owner HEFEI SIBOT SOFTWARE DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products