Odorless environmentally-friendly type PVC (polyvinyl chloride) edge-banding strip and preparation method thereof

An edge banding and environmental protection technology, which is applied in the field of odorless and environment-friendly PVC edge banding and its preparation, can solve the problems of unfavorable human health, high odor of PVC edge banding, environmental pollution, etc., and achieve excellent adhesion and weather resistance Strong and compatible effect

Inactive Publication Date: 2017-09-26
XIONG YI PLASTIC PROD CO LTD
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the strong odor of traditional PVC edge banding, it has certain pollution to the environment, and long-term exposure is not conducive to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A kind of odorless and environment-friendly PVC edge banding strip, comprising the following raw materials in parts by weight:

[0048] PVC resin 75 parts

[0049] Nano active calcium carbonate 8 parts

[0050] 6 parts of odorless environmental protection plasticizer

[0051] Modification additive 3 parts

[0052] Deodorant 3 parts

[0053] Environmental calcium zinc composite stabilizer 2.5 parts

[0054] Internal lubricant 0.3 parts

[0055] 0.5 parts of external lubricant

[0056] UV absorber 0.1 parts

[0057] Antioxidant 0.2 part

[0058] Toner 0.5 parts.

[0059] The PVC resin is a SG-5 type PVC resin with a degree of polymerization of 1000; the nano-active calcium carbonate is a nano-active calcium carbonate with a particle size of 10 nm, modified by a silane coupling agent, and grafted with polyvinyl chloride. calcium.

[0060] The odorless and environment-friendly plasticizer consists of 1 part of soybean oil, 3 parts of dioctyl adipate and 2 parts of...

Embodiment 2

[0074] A kind of odorless and environment-friendly PVC edge banding strip, comprising the following raw materials in parts by weight:

[0075] PVC resin 85 parts

[0076] Nano active calcium carbonate 12 parts

[0077] 13 parts of odorless environmental protection plasticizer

[0078] Modification additive 10 parts

[0079] Deodorant 5.5 parts

[0080] Environmentally friendly calcium zinc composite stabilizer 3.5 parts

[0081] Internal lubricant 0.5 parts

[0082] 0.8 parts of external lubricant

[0083] UV absorber 0.3 parts

[0084] Antioxidant 0.5 parts

[0085] Toner 0.8 parts.

[0086] The PVC resin is a SG-5 type PVC resin with a polymerization degree of 1020; the nano-active calcium carbonate is a nano-active calcium carbonate with a particle size of 30nm, modified by a silane coupling agent, and grafted with polyvinyl chloride. calcium.

[0087] The odorless and environment-friendly plasticizer consists of 2 parts of soybean oil, 5 parts of dioctyl adipate ...

Embodiment 3

[0101] A kind of odorless and environment-friendly PVC edge banding strip, comprising the following raw materials in parts by weight:

[0102] PVC resin 100 parts

[0103] Nano active calcium carbonate 16 parts

[0104] Odorless environmental protection plasticizer 19 parts

[0105] Modification additive 19 parts

[0106] Deodorant 8 servings

[0107] Environmentally friendly calcium zinc composite stabilizer 4.5 parts

[0108] Internal lubricant 0.9 parts

[0109] 1.2 parts of external lubricant

[0110] UV absorber 0.5 parts

[0111] Antioxidant 0.8 parts

[0112] Toner 1.0 parts.

[0113] The PVC resin is a SG-5 type PVC resin with a polymerization degree of 1050; the nano-active calcium carbonate is a nano-active calcium carbonate with a particle size of 50nm, modified by a silane coupling agent, and grafted with polyvinyl chloride. calcium.

[0114] The odorless and environment-friendly plasticizer consists of 3 parts of soybean oil, 8 parts of dioctyl adipate a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of edge banding, in particular to an odorless environmentally-friendly type PVC (polyvinyl chloride) edge-banding strip and a preparation method thereof. The odorless environmentally-friendly type PVC edge-banding strip comprises the following raw materials in parts by weight: 75 to 125 parts of PVC resin, 8 to 25 parts of active nano-calcium carbonate, 6 to 32 parts of an odorless environmentally-friendly plasticizer, 3 to 33 parts of a modified aid, 3 to 13 parts of an odor eliminating agent, 2.5 to 6.5 parts of an environmentally-friendly calcium zinc composite stabilizer, 0.3 to 1.5 parts of an internal lubricating agent, 0.5 to 2.0 parts of an external lubricating agent, 0.1 to 0.8 part of an ultraviolet absorbent, 0.2 to 1.5 parts of an antioxidant and 0.5 to 1.5 parts of toner. The odorless environmentally-friendly type PVC edge-banding strip provided by the invention does not contain phthalate, heavy metals and other harmful substances, is environmentally-friendly and odorless, and has high weather resistance, high impact resistance and excellent comprehensive physical property.

Description

technical field [0001] The invention relates to the technical field of edge banding, in particular to an odorless and environment-friendly PVC edge banding and a preparation method thereof. Background technique [0002] Edge banding is a material for protecting, decorating and beautifying the section of furniture panels. Its main function is to seal the section of the panel so as to prevent the panel from being damaged by the environment and unfavorable factors (mainly moisture) during use. And prevent the volatilization of formaldehyde inside the board, and at the same time achieve the effect of making a piece of furniture show clear wood grain and colorful decoration. The existing edge banding is mainly made of polyvinyl chloride (PVC) edge banding, and the PVC edge banding is a thermoplastic coil made of PVC as the main raw material, adding additives, mixing and pressing together . The surface of PVC edge banding has patterns and patterns such as wood grain, marble, clo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L51/10C08L91/00C08L23/28C08L33/04C08L51/04C08L91/06C08L23/06C08L23/30C08K13/02C08K5/11C08K5/12C08K5/098C08K3/04C08K5/103C08K5/134C08K5/526C08K3/26C08F292/00C08F214/06
CPCC08L27/06C08F292/00C08K2003/265C08K2201/011C08L2201/08C08L2205/035C08L51/10C08L91/00C08L23/286C08L33/04C08L51/04C08L91/06C08L23/06C08L23/30C08K13/02C08K5/11C08K5/12C08K5/098C08K3/04C08K5/103C08K5/1345C08K5/526C08K3/26C08F214/06
Inventor 罗贵东李昌
Owner XIONG YI PLASTIC PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com