Springy-handle antiskidding matte lustering oil

A technology with hand feel and smoothness. It can be used in coatings, polyurea/polyurethane coatings, etc. It can solve the problems of high energy consumption, slow film forming speed and low efficiency, and achieve the effect of good hand feeling and fast film forming speed.

Inactive Publication Date: 2017-09-26
SUZHOU ZHONGYA INK
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional elastic touch paint has the characteristics of rich expressiveness, strong three-dimensional effect, good flexibility and strong plasticity, but the traditional elastic touch paint has slow film forming speed, high energy consumption, low efficiency and poor environmental friendliness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: A kind of elastic feel non-slip matte varnish is prepared from the following components by mass fraction: 10% vinyl chloride resin solution, 23% polyurethane resin, 30% acrylic resin, 1.5% wax powder, Focusing accelerator 1%, film-forming accelerator 2.5%, silicone 0.4%, n-propyl acetate 14.1%, isopropanol 2%, defoamer 0.5% and calcined kaolin 15%.

[0018] The massfraction of vinyl acetate resin in described vinyl acetate resin liquid is 20%, is that VP-10 vinyl acetate resin is dissolved in the mixed solution of n-propyl ester and isopropanol, the volume ratio of described n-propyl ester and isopropanol It is 4:1, and the viscosity of described vinyl chloride resin liquid is 200~300mPa·s; Described polyurethane resin is M6638 polyurethane resin; Described wax powder is 3620 polyethylene wax powder; Described acrylic resin is T-212 acrylic resin The film-forming accelerator is cellulose acetate butyrate; the organosilicon is L-51 organosilicon; the defoam...

Embodiment 2

[0019] Embodiment 2: A kind of elastic feel non-slip matte varnish is prepared from the following components by mass fraction: 10% vinyl chloride resin solution, 22% polyurethane resin, 30% acrylic resin, 1% wax powder, and Concentration accelerator 1.5%, film-forming accelerator 2.5%, silicone 0.5%, n-propyl acetate 15%, isopropanol 1%, defoamer 0.5% and calcined kaolin 16%.

[0020] Concrete component among the present embodiment is with embodiment 1.

Embodiment 3

[0021] Embodiment 3: a kind of elastic feel non-slip matte varnish is prepared from the following components by mass fraction: 12% vinyl chloride resin liquid, 25% polyurethane resin, 25% acrylic resin, 1.8% wax powder, Focusing accelerator 1.2%, film-forming accelerator 2.8%, silicone 0.2%, n-propyl acetate 15%, isopropanol 2.5%, defoamer 0.5% and calcined kaolin 14%.

[0022] Concrete component among the present embodiment is with embodiment 1.

[0023] The elastic feel non-slip matte varnish in any of the above-mentioned embodiments is prepared by the following preparation method: the vinyl acetate resin liquid, polyurethane resin, acrylic resin, film-forming accelerator, n-propyl acetate , isopropanol and calcined kaolin were put into a mixer and stirred thoroughly, then wax powder, adhesion promoter, silicone and defoamer were added and stirred again, and stirred at 1000 rpm for 1 hour to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses springy-handle antiskidding matte lustering oil. The springy-handle antiskidding matte lustering oil is prepared from the following ingredients in percentage by mass: 10% to 12% of vinyl chloride-vinyl acetate copolymer solution, 20% to 25% of polyurethane resin, 25% to 35% of acrylic resin, 1% to 2% of wax powder, 0.5% to 1.5% of adhesion promoter, 2% to 3% of film forming accelerant, 0.1% to 0.5% of organosilicone, 12% to 15% of n-propyl acetate, 1% to 3% of isopropanol, 0.1% to 1% of antifoamer and 13% to 20% of calcined kaolin. The springy-handle antiskidding matte lustering oil has the advantages of high film forming speed, aging resistance, scratch resistance and the like.

Description

technical field [0001] The invention relates to the technical field of varnish preparation, in particular to an elastic hand-feeling non-slip matte varnish. Background technique [0002] Glazing is an important means of post-press finishing, mainly by coating (or spraying, printing) a layer of transparent paint on the surface of the printed matter, and forming a thin and uniform coating on the surface of the printed matter after leveling, drying, calendering, and curing. The transparent bright layer is a process or technology that enhances the smoothness of the surface of the carrier and protects the fine decoration of printed graphics. Glazing can not only enhance the surface gloss and protect printed graphics, but also does not affect the recycling of paper. The traditional elastic touch paint has the characteristics of rich expressiveness, strong three-dimensional effect, good flexibility and strong plasticity, but the traditional elastic touch paint has slow film formin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D175/04C09D127/06C09D7/12C09D7/00
CPCC09D133/00C08L2201/08C08L2205/035C09D175/04C08L75/04C08L27/06C08K3/346C08L33/00
Inventor 张东明
Owner SUZHOU ZHONGYA INK
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com