Transformer preservative paint and preparation method thereof

A technology of anti-corrosion paint and transformers, which is applied in the field of transformers, can solve problems affecting the service life of transformers, and achieve the effects of improving anti-corrosion ability, good flexibility of paint film, and low cost

Inactive Publication Date: 2017-10-17
HEFEI TONGYOU ELECTRONICS TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Corrosion has become a major hidden danger to the operation safety of large transformers, affecting the service life of transformers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] This embodiment relates to a transformer anticorrosion paint, which includes the following raw materials in parts by weight: 30 parts of high-hardness water-based acrylic resin, 20 parts of polyurethane, 15 parts of red lead, 1 part of phenyl silicone oil, 5 parts of diethylenetriamine, ethyl acetate 3 parts, 4 parts of triphenyl phosphate, 2 parts of zinc borate, 5 parts of filler, 1 part of defoamer, 2 parts of dispersant, 2 parts of preservative, 4 parts of Houttuynia cordata, 1 part of thickener, deionized water 10 servings.

[0024] Wherein, the filler is a mixture of titanium dioxide and talc, and the mass ratio of the mixture of titanium dioxide and talc is 2:3.

[0025] Wherein, the defoamer is mineral oil.

[0026] Wherein, the dispersant is sodium lauryl sulfate.

[0027] Wherein, the thickener is methyl cellulose ether.

[0028] A method for preparing the transformer anticorrosion paint, comprising the steps of:

[0029] (1) Weigh high-hardness water-base...

Embodiment 2

[0034] This embodiment relates to a transformer anticorrosion paint, including the following raw materials in parts by weight: 50 parts of high-hardness water-based acrylic resin, 28 parts of polyurethane, 25 parts of red lead, 3 parts of phenyl silicone oil, 8 parts of diethylenetriamine, ethyl acetate 5 parts, 8 parts of triphenyl phosphate, 3 parts of zinc borate, 10 parts of filler, 2 parts of defoamer, 3 parts of dispersant, 4 parts of preservative, 8 parts of Houttuynia cordata, 3 parts of thickener, deionized water 20 servings.

[0035] Wherein, the filler is a mixture of titanium dioxide and talc, and the mass ratio of the mixture of titanium dioxide and talc is 2:3.

[0036] Wherein, the defoamer is aliphatic hydrocarbon.

[0037] Wherein, the dispersant is sodium lauryl sulfate.

[0038] Wherein, the thickener is hydroxyethyl cellulose ether.

[0039] A method for preparing the transformer anticorrosion paint, comprising the steps of:

[0040] (1) Weigh high-hard...

Embodiment 3

[0045] This embodiment relates to a transformer anticorrosion paint, including the following raw materials in parts by weight: 35 parts of high-hardness water-based acrylic resin, 22 parts of polyurethane, 18 parts of red lead, 1.8 parts of phenyl silicone oil, 6 parts of diethylenetriamine, ethyl acetate 3.4 parts, 5 parts of triphenyl phosphate, 2.1 parts of zinc borate, 7 parts of filler, 1.3 parts of defoamer, 2.2 parts of dispersant, 2.5 parts of preservative, 5 parts of Houttuynia cordata, 1.4 parts of thickener, deionized water 13 servings.

[0046] Wherein, the filler is a mixture of titanium dioxide and talc, and the mass ratio of the mixture of titanium dioxide and talc is 2:3.

[0047] Wherein, the defoamer is an emulsifier.

[0048] Wherein, the dispersant is sodium lauryl sulfate.

[0049] Wherein, the thickener is carboxymethyl cellulose ether.

[0050] A method for preparing the transformer anticorrosion paint, comprising the steps of:

[0051](1) Weigh high...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses transformer preservative paint which comprises the following raw materials in parts by weight: 30-50 parts of high-hardness aqueous acrylic resin, 20-28 parts of polyurethane, 15-25 parts of red lead, 1-3 parts of phenyl silicon oil, 5-8 parts of diethylenetriamine, 3-5 parts of ethyl acetate, 4-8 parts of triphenyl phosphate, 2-3 parts of zinc borate, 5-10 parts of packing, 1-2 parts of a defoaming agent, 2-3 parts of a dispersing agent, 2-4 parts of a preservative, 4-8 parts of houttuynia cordata, 1-3 parts of a thickening agent and 10-20 parts of deionized water. The transformer preservative paint disclosed by the invention is relatively small in raw material quantity, relatively low in cost, relatively simple in preparation process and very good in temperature resistance and corrosion resistance.

Description

technical field [0001] The invention belongs to the technical field of transformers, and in particular relates to a transformer anticorrosion paint and a preparation method thereof. Background technique [0002] In the production process of smelting and chemical industries, the emission of smoke and dust is relatively large, which has a serious corrosion effect on the metal shell of large transformers, especially the damage to the weak part of the transformer - the radiator. Corrosion has become a major hidden danger to the operation safety of large transformers, which affects the service life of transformers. It is economical and technically feasible to use paint protection for large-scale transformers in operation. The operation is relatively simple and can be carried out by taking advantage of power failures. Therefore, anti-corrosion paint is an important factor in transformer anti-corrosion. Contents of the invention [0003] The invention provides a transformer anti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D175/04C09D183/04C09D5/08C09D7/12
CPCC09D133/00C08K2003/2241C08K2003/387C08L2201/08C08L2203/206C08L2205/035C09D5/08C09D5/18C08L75/04C08L83/04C08K13/02C08K5/17C08K5/523C08K3/38C08K3/22C08K3/34
Inventor 李丹丹
Owner HEFEI TONGYOU ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products