A production formula and preparation method of an elastic rotating body

A technology for producing formula and rotating body, applied in the field of production formula and preparation of elastic rotating body, can solve the problems of short service time, easy cracking, poor anti-aging performance, etc., and achieves hard to crack, smooth and round surface, good anti-aging performance. Effect

Active Publication Date: 2021-04-02
江苏恪铭智慧交通科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problem that the existing elastic rotating body has poor anti-aging performance and is easy to crack, so that the use time is short, the invention provides a production formula and preparation method of the elastic rotating body, which ensures that the elastic rotating body has good anti-aging performance. It is not easy to crack under force, which effectively prolongs the service life of the elastic rotating body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A production formula and preparation method of an elastic rotating body

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation method of the elastic rotating body of the present invention is carried out according to the following specific steps:

[0037](1) Internal mixing: POE, EPDM rubber, anti-shrinkage agent, filler, EVA, stearic acid, zinc stearate, zinc oxide, crosslinking agent, foaming agent, flow agent, masterbatch pigment Add it into the internal mixer for mixing and stirring, then put the stirred material into the internal mixer for 8 to 12 minutes at a temperature of 80-100°C, put it into the open mixer for uniform tableting, and then granulate. Among them, the kneading temperature is controlled within the range of 45-65°C, the kneading time is controlled within the range of 5-8 minutes, and the granulation temperature is controlled within the range of 80-100°C;

[0038] (2) Plasticizing processing: input the above granulated materials into the barrel of the injection machine for plasticizing processing, and the temperature is controlled within the range of 70-100°C;...

Embodiment 1

[0046] A production recipe of an elastic rotating body of the present invention, calculated by weight, includes the following specific components: ethylene-octene copolymer (POE) 15%, EVA 50%, EPDM rubber 15%, anti-shrinkage agent E20 -58 7.5%, talcum powder with particle size ≤200nm 2%, stearic acid 0.3%, zinc stearate 0.7%, zinc oxide 1.5%, dicumyl peroxide DCP 1%, azodicarbonamide AC Foaming agent 2%, fatty acid ester 2%, masterbatch pigment 3%, the total weight is 100%.

[0047] like figure 1 Shown, the preparation method of a kind of elastic rotating body of the present invention is carried out according to the following specific steps:

[0048] (1) Internal mixing: POE, EPDM rubber, EVA, anti-shrinkage agent E20-58, talcum powder, stearic acid, zinc stearate, zinc oxide, dicumyl peroxide DCP, azobis Add formamide AC foaming agent, fatty acid ester, and masterbatch into the internal mixer for mixing and stirring, and then mix the stirred materials with the internal mixe...

Embodiment 2

[0053] A production formula of an elastic rotating body of the present invention, calculated by weight, includes the following specific components: ethylene-octene copolymer (POE) 10%, EVA 60%, EPDM rubber 10%, anti-shrinkage agent E20 -58 5%, 2% talc powder with particle size ≤ 200nm, 1% calcium carbonate with particle size ≤ 200nm, 0.5% stearic acid, 1% calcium stearate, 2% zinc oxide, dicumyl peroxide DCP 0.7%, azodicarbonamide AC blowing agent 1.8%, fatty acid ester 2%, masterbatch pigment 4%, the total weight is 100%.

[0054] A kind of preparation method of elastic rotating body of the present invention is carried out according to the following specific steps:

[0055] (1) Internal mixing: POE, EPDM rubber, anti-shrinkage agent, talcum powder, calcium carbonate, EVA, stearic acid, calcium stearate, zinc oxide, dicumyl peroxide DCP, azobis Add the formamide AC foaming agent, fatty acid ester, and masterbatch into the internal mixer for mixing and stirring, and then mix t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a production formula and a preparation method of an elastic rotating body, belonging to the technical field of road traffic equipment. Its formula includes the following specific components: ethylene-octene copolymer (POE) 10-20%, EVA 40-60%, EPDM rubber 10-20%, anti-shrinkage agent 5-10%, filler 1- Weight Total is 100%. Mix and refine POE, EPDM materials and EVA materials, and add a variety of additives, so that the three materials can maintain their own properties and complement each other. It is dense and light in weight, which ensures good anti-aging performance of the elastic rotating body, and is not easy to crack when subjected to impact force, effectively prolonging the service life of the elastic rotating body.

Description

technical field [0001] The invention belongs to the technical field of road traffic equipment, and more specifically relates to a production formula and a preparation method of an elastic rotating body. Background technique [0002] With the rapid development of economy, automobiles are widely used as a convenient means of transportation. In my country, the speed limit of different roads is also different. For example, the general speed limit of urban roads is 40 kilometers per hour, the general speed of ordinary roads is 40-80 kilometers per hour, and the general speed limit of expressways is 60-120 kilometers per hour. Therefore, traffic accidents in urban areas are mostly rear-end collision accidents. On ordinary roads or expressways, traffic accidents occur frequently due to excessive speed of vehicles. On the guardrail, and these guardrails are made of concrete bricks or concrete blocks arranged at intervals and cross rails connecting adjacent blocks, or are composed of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L23/16C08K13/02C08K5/14C08K3/34C08K3/36C08K3/26C08J9/10B29B7/00B29C44/42B29C44/60
CPCB29B7/002B29C44/42B29C44/60C08J9/103C08J2203/04C08J2323/08C08J2423/08C08J2423/16C08K2003/265C08K2201/005C08L23/0853C08L2201/08C08L2203/14C08L2205/035C08L23/0815C08L23/16C08K13/02C08K5/14C08K3/34C08K3/26C08K3/36
Inventor 许运动
Owner 江苏恪铭智慧交通科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com