Organic matter coating method of mica powder used for cosmetics

A technology of mica powder and cosmetics, applied in the field of mica powder, which can solve the problems of inconspicuous ultraviolet shielding effect, clogged skin pores, and poor skin breathing, and achieve good antibacterial and ultraviolet shielding effects, easy cleaning, and enhanced ultraviolet shielding effect Effect

Inactive Publication Date: 2017-11-10
ANHUI HENGHAO SCI & TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to their good hydrophobicity, such cosmetics are difficult to clean and easy to remain. Long-term use can easily cause adverse effects such as clogged skin pores and poor skin breathing.
Not only that, due to the limitations of its production process, the existing mica powder for cosmetics often has defects such as rough hand feeling, poor gloss, low transparency, and inconspicuous ultraviolet shielding effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for compounding organic matter of mica powder for cosmetics proposed by the present invention comprises the following steps:

[0019] S1. According to the mass ratio of 1:4.5, after adding high-quality mica powder to water to make a suspension, add simethicone oil 0.5 times the total amount of mica powder and silane coupling agent 0.1 times to the ball mill respectively, and fully grind for 2 hours. Obtain grinding liquid A;

[0020] S2, add sulfuric acid to the grinding liquid A obtained in step S1, adjust the pH value of grinding liquid A to 5.5, then add the mass ratio of 0.07 times of the total amount of grinding liquid A to be 1.2:2 fatty amine salt and quaternary ammonium salt The compounding agent was stirred and mixed for 2 hours at a speed of 480r / min to obtain the mixed solution B;

[0021] S3. Heat the mixed solution B obtained in step S2 to 75°C, add ethanol solution to keep the alcohol content of the mixed solution B at 45%, add 0.25 times the tot...

Embodiment 2

[0024] A method for compounding organic matter of mica powder for cosmetics proposed by the present invention comprises the following steps:

[0025] S1. According to the mass ratio of 1:7, after adding high-quality mica powder to water to make a suspension, add simethicone oil 0.8 times the total amount of mica powder and silane coupling agent 0.3 times to the ball mill respectively, and fully grind for 1.8 hours , to obtain grinding liquid A;

[0026] S2, add hydrochloric acid to the grinding liquid A obtained in step S1, adjust the pH value of grinding liquid A to 5.8, then add the fatty amine salt and the quaternary ammonium salt of 0.05 times of the total amount of grinding liquid A in a mass ratio of 1:1.5 The compounding agent was stirred and mixed for 1.5 hours at a speed of 520r / min to obtain the mixed solution B;

[0027] S3. Heat the mixed solution B obtained in step S2 to 85° C., add ethanol solution for heat preservation until the alcohol content of the mixed sol...

Embodiment 3

[0030] A method for compounding organic matter of mica powder for cosmetics proposed by the present invention comprises the following steps:

[0031] S1. According to the mass ratio of 1:6.5, after adding high-quality mica powder to water to make a suspension, add simethicone oil 0.7 times the total amount of mica powder and silane coupling agent 0.2 times to the ball mill respectively, and fully grind for 1 hour. Obtain grinding liquid A;

[0032] S2, add phosphoric acid to the grinding liquid A obtained in step S1, adjust the pH value of grinding liquid A to 6, then add the mass ratio of 0.06 times of the total amount of grinding liquid A to be 1.4:3 fatty amine salt and quaternary ammonium salt The compound agent was stirred and mixed for 1 hour at a speed of 650r / min to obtain a mixed solution B;

[0033] S3. Heat the mixed solution B obtained in step S2 to 80° C., add ethanol solution to keep the alcohol content of the mixed solution B at 58%, add 0.32 times the total am...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an organic matter coating method of mica powder used for cosmetics. The organic matter coating method of mica powder used for cosmetics comprises the following steps: mixing dimethicone, a silane coupling agent and a suspension prepared from the mica powder, carrying out wet grinding, carrying out hydrophobic treatment on the mica powder, adding a cationic surfactant under a weak acidic condition, treating the mica powder, carrying out alcohol precipitation to remove impurities and adding nanometer titanium dioxide to effectively enhance the ultraviolet shielding effect of the mica powder. The obtained mica powder has the advantages of smooth hand feeling, good gloss, high transparence and obvious pearlescent effect, effectively avoids the defects of difficult cleaning and easy residual in the prior art, has the characteristics of waterproofing, lasting property, easiness in cleaning and no residual, has good bacterium preventing and ultraviolet shielding effects, has extremely good endophilicity and skin friendly property, is safe without irritation, can be widely applied to the field of cosmetics, and is worth promoting.

Description

technical field [0001] The invention relates to the technical field of mica powder, in particular to a method for compounding organic matter with mica powder for cosmetics. Background technique [0002] Mica powder is a non-metallic mineral containing various components, mainly SiO 2 , the content is generally around 49%, Al 2 o 3 The content is about 30%; mica powder has good elasticity, toughness, insulation, high temperature resistance, acid and alkali resistance, corrosion resistance, strong adhesion and other characteristics. Mica powder is an excellent additive, which is widely used in electrical appliances, welding electrodes, rubber, plastics, papermaking, paints, coatings, pigments, ceramics, cosmetics, new building materials and other industries. It has a wide range of uses. Due to its unique pearlescent effect, crystal transparency, silky luster and smooth texture, mica powder has excellent affinity and skin-adhesiveness with the skin. Mica powder is widely use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/40C09C3/04C09C3/06C09C3/08C09C3/12
CPCC09C1/405C09C3/006C09C3/04C09C3/06C09C3/08C09C3/12
Inventor 关洪勇万斌
Owner ANHUI HENGHAO SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap