Novel environment-friendly polyvinyl chloride cable material

A polyvinyl chloride cable and polyvinyl chloride technology, applied in the field of polymer cable materials, can solve the problems of cable materials such as poor anti-aging and high temperature resistance, secondary pollution, etc., achieve a high degree of plasticization, reduce the content of chemical substances, Wide range of applications and effects

Inactive Publication Date: 2011-01-26
ZHENJIANG HUAYIN INSTR & ELECTRICAL EQUIP
View PDF6 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional polyvinyl chloride cable material, the formula is: 100 parts of polyvinyl chloride, 50-60 parts of dioctyl phthalate, 6-10 parts of compound stabilizer, 1-3 parts of lubricant, 20 parts of active light calcium carbonate -30 parts, the above-mentioned materials are prohibited due to the use of dioctyl phthalate DOP as the plasticizer and the basic lead salt used as the stabilizer. Dioctyl phthalate will produce secondary pollution after burning
[0003] In order to solve the above-mentioned technical problems, a new type of environmentally friendly polyvinyl chloride cable material has recently been disclosed in Chinese patent documents, the application number of which is "200810023864. , the polyvinyl chloride cable material is prepared from the following raw materials, and its formula is: 85-105 parts of polyvinyl chloride, 50-60 parts of plasticizer DINP, 6-7 parts of Ca-Zn composite stabilizer, lubricant (stearic acid or polyethylene wax) 1-2 parts, active light calcium carbonate 20-30 parts, although the cable material produced by this formula has certain environmental protection, the cable material produced by this formula has the performance of anti-aging and high temperature / low temperature resistance Poor, mechanical properties 100° heat aging 168h (tensile strength, elongation at break, etc.) changes within ± 20%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Raw materials: 100 parts of polyvinyl chloride WS-1300; 50 parts of plasticizer UN399; 10 parts of stabilizer CZ-756E (105); antimony trioxide (SB 2 o 3 ) 10 parts; epoxidized soybean oil 5 parts; bisphenol A antioxidant 1 part; polyethylene (PE) 1 part; active light calcium carbonate 30 parts; carbon black 1 part.

[0037] According to the total weight of 100kg, put polyvinyl chloride WS-1300, active light calcium carbonate and polyethylene (PE) into the mixer and mix them. When the temperature reaches 90 degrees, add plasticizer UN399 and stabilizer CZ -756E (105), epoxy soybean oil, bisphenol A antioxidant, carbon black, mix evenly at room temperature; unload the mixed material into the discharge section, and then add it to the twin-screw extruder for mixing , extrusion and granulation.

[0038] Performance test, under the condition of heat aging at 136°C for 168h, the change rate of mechanical properties (tensile strength, elongation at break) is 8%, and the oxyg...

Embodiment 2

[0040] Raw materials: 100 parts of polyvinyl chloride WS-1300; 45 parts of plasticizer UN399; 8 parts of stabilizer CZ-756E (105); antimony trioxide (SB 2 o 3 ) 9 parts; epoxidized soybean oil 5 parts; bisphenol A antioxidant 2 parts; polyethylene (PE) 1 part; active light calcium carbonate 30 parts; carbon black 1 part.

[0041] According to the total weight of 100kg, put polyvinyl chloride WS-1300, active light calcium carbonate and polyethylene (PE) into the mixer and mix them. When the temperature reaches 90 degrees, add plasticizer UN399, zinc oxide ( ZnO ), stabilizer CZ-756E (105), epoxy soybean oil, bisphenol A antioxidant, carbon black, mix evenly at room temperature; unload the mixed material into the discharge section, and then add it to the twin-screw Mixing in an extruder, extruding and granulating.

[0042] Performance test, under the condition of heat aging at 136℃ for 168h, the change rate of mechanical properties (tensile strength, elongation at break) is 1...

Embodiment 3

[0044] Raw materials: 100 parts of polyvinyl chloride WS-1300; 55 parts of plasticizer UN399; 9 parts of stabilizer CZ-756E (105); antimony trioxide (SB 2 o 3 ) 9 parts; epoxidized soybean oil 5 parts; bisphenol A antioxidant 2 parts; polyethylene (PE) 1 part; active light calcium carbonate 30 parts; carbon black 1 part.

[0045] According to the total weight of 100kg, put polyvinyl chloride WS-1300, active light calcium carbonate and polyethylene (PE) into the mixer and mix them. When the temperature reaches 90 degrees, add plasticizer UN399 and stabilizer CZ -756E (105), epoxy soybean oil, bisphenol A antioxidant, carbon black, mix evenly at room temperature; unload the mixed material into the discharge section, and then add it to the twin-screw extruder for mixing , extrusion and granulation.

[0046] Performance test, under the condition of heat aging at 136℃ for 168h, the change rate of mechanical properties (tensile strength, elongation at break) is 11%, and the oxyge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
oxygen indexaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention provides a novel environment-friendly polyvinyl chloride cable material. The material consists of polyvinyl chloride WS-1300, plasticizer UN399, stabilizer CZ-756E (105), epoxidized soybean oil, bisphenol A antioxygen, antimonous oxide (SB203), polyethylene (PE), activated light calcium carbonate and carbon black. The chemical substance content of the material is reduced by improving the formula of the cable material, so that the product has the advantages of effectively solving the problem of toxic gases releasing in polyvinyl chloride material heating and plastifying process, reducing the harm to the human bodies in the production process, resisting the temperature of between 40 and 105 DEG C, along with cleanness and environmental protection, light specific gravity, high plasticization degree, no deformation, fracture or aging, superior product performance, and wider application range and field.

Description

technical field [0001] The invention relates to a polymer cable material. Background technique [0002] Wire and cable refers to materials used for power, communication and related transmission purposes. With the development of society, wires and cables are more and more widely used in various fields, such as transportation, communication, construction, etc. Therefore, the demand for wires and cables is also getting higher and higher. Traditional polyvinyl chloride cable material, the formula is: 100 parts of polyvinyl chloride, 50-60 parts of dioctyl phthalate, 6-10 parts of compound stabilizer, 1-3 parts of lubricant, 20 parts of active light calcium carbonate -30 parts, the above-mentioned materials are prohibited due to the use of dioctyl phthalate DOP as the plasticizer and the basic lead salt used as the stabilizer. Dioctyl phthalate will produce secondary pollution after burning. [0003] In order to solve the above-mentioned technical problems, a new type of enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08K13/02C08K5/1515C08K3/22C08K3/26C08K3/04
Inventor 季忠银
Owner ZHENJIANG HUAYIN INSTR & ELECTRICAL EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap