Composite wax clearing agent
The technology of a wax remover and a metal chelating agent is applied in the directions of drilling compositions, chemical instruments and methods, etc., and can solve the problems of low safety performance, poor wax dissolving effect, and great harm to human body, and achieves high safety and is not easy to achieve. Fire, low toxicity effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0020] In parts by weight, select 5 parts of nano-titanium dioxide, 6 parts of quartz stone, 20 parts of diatomaceous earth, 5 parts of vermiculite, 3 parts of sodium α-alkenyl sulfonate, 5 parts of nonylphenol polyoxyethylene ether and 90 parts Parts of isobutanol, mixed and added to the ball mill, discharged after ball milling for 2 hours, to obtain a mixed slurry; in parts by weight, 30 parts of sodium dodecylbenzenesulfonate, 10 parts of 1,2-propylene glycol, 20 parts of 1 part of peanut oil, 5 parts of oleic acid, 0.4 part of triethanolamine and 120 parts of water, stirred and mixed with 2000r / min rotating speed for 30min, after stirring, a microemulsion was obtained; by parts by weight, 50 parts of microemulsion and 40 parts of mixed slurry and 4 parts of cornstarch were stirred and mixed for 50 minutes at a speed of 1000 r / min, and the compound wax remover was obtained after stirring.
example 2
[0022] In parts by weight, 3 parts of nano-titanium dioxide, 4 parts of quartz stone, 15 parts of diatomaceous earth, 3 parts of vermiculite, 1 part of sodium α-alkenyl sulfonate, 2 parts of nonylphenol polyoxyethylene ether and 70 parts were selected respectively. Parts of isobutanol, after mixing, add in the ball mill, discharge after ball milling for 1h, to get mixed slurry; by parts by weight, choose 20 parts of sodium lauryl sulfate, 5 parts of polyethylene glycol, 10 parts of sesame oil, 2 parts of linoleic acid, 0.2 part of edetate disodium and 100 parts of water were stirred and mixed for 20 minutes at a speed of 1500r / min, and a microemulsion was obtained after stirring; Mix the slurry and 2 parts of carrageenan, stir and mix at 800r / min for 30min, after stirring, you can get the compound wax remover.
example 3
[0024] In parts by weight, 4 parts of nano-titanium dioxide, 5 parts of quartz stone, 17 parts of diatomaceous earth, 4 parts of vermiculite, 2 parts of sodium α-alkenyl sulfonate, 3 parts of nonylphenol polyoxyethylene ether and 80 parts were selected respectively. Parts of isobutanol, after mixing, add in the ball mill, discharge after ball milling 1h, get mixed slurry; By weight, choose 25 parts of sorbitan monostearate, 7 parts of polypropylene glycol, 15 parts of olive oil respectively , 4 parts of ethoxylated castor oil, 0.3 part of tetrasodium edetate and 110 parts of water, stirred and mixed for 25 minutes with 1700r / min rotating speed, got microemulsion after stirring; The emulsion, 35 parts of mixed slurry and 3 parts of methyl hydroxyethyl cellulose were stirred and mixed at a speed of 900r / min for 40 minutes, and the composite wax remover was obtained after stirring.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com