A kind of hydrophobic polymer cement waterproof coating and preparation method thereof

A technology of waterproof coatings and polymers, applied in the direction of coatings, etc., can solve the problems of polymer cement waterproof coatings such as non-environmental protection, slow drying time, and poor water resistance, and achieve the effects of fast drying, good environmental protection, and improved flexibility

Active Publication Date: 2019-08-27
青岛东方雨虹建筑材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the embodiment of the present invention provides a hydrophobic polymer cement waterproof coating and its preparation method, the main purpose is to solve the technical problems of polymer cement waterproof coating not being environmentally friendly, high water absorption, poor water resistance and slow drying time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrophobic polymer cement waterproof coating and preparation method thereof
  • A kind of hydrophobic polymer cement waterproof coating and preparation method thereof
  • A kind of hydrophobic polymer cement waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] In parts by weight, each raw material is prepared according to the liquid material formula: 470 parts of the first type of styrene-acrylic emulsion (selected from Arkema 5181 emulsion, the glass transition temperature is -10 ° C), the second type of styrene-acrylic emulsion (selected from BASF 405 Emulsion, glass transition temperature is -19 ℃) 30 parts, lotus leaf hydrophobic agent 2 parts (selected from Aohan Chemical SC-011 lotus leaf effect hydrophobic agent), polyacrylic acid sodium salt 4 parts (selected from Dow 731A), poly 5 parts of ether defoamer (selected from BASF 2706), 0.5 parts of thickener (selected from Arkema 3800), 8 parts of deionized water;

[0043] In parts by weight, each raw material is prepared according to the powder formula: 300 parts of ordinary silicate 42.5 grade gray cement, 300 parts of 350 mesh quartz powder, 400 parts of 200 mesh wollastonite powder, polycarboxylate superplasticizer (selected from Dongfangyu Rainbow CR-818) 3 parts, ea...

Embodiment 2

[0048] In parts by weight, prepare each raw material according to the liquid material formula: 430 parts of the first type of styrene-acrylic emulsion (selected from Arkema 5181 emulsion, the glass transition temperature is -10 ° C), the second type of styrene-acrylic emulsion (selected from BASF 405 Emulsion, the glass transition temperature is -19 ℃) 70 parts, 3 parts of lotus leaf hydrophobic agent (selected from Aohan Chemical SC-011 lotus leaf effect hydrophobic agent), 6 parts of polyacrylic acid sodium salt (selected from Dow 731A), poly 5 parts of ether defoamer (selected from BASF 2706), 0.4 parts of thickener (selected from Arkema 3800), 12 parts of deionized water;

[0049] In parts by weight, each raw material is prepared according to the powder formula: 350 parts of ordinary silicate 42.5 grade gray cement, 300 parts of 350 mesh quartz powder, 350 parts of 200 mesh wollastonite powder, polycarboxylate superplasticizer (selected from Dongfangyu Rainbow CR-818) 4 pa...

Embodiment 3

[0054] In parts by weight, each raw material is prepared according to the liquid material formula: 400 parts of the first type of styrene-acrylic emulsion (selected from Arkema 5181 emulsion, the glass transition temperature is -10 ° C), the second type of styrene-acrylic emulsion (selected from BASF 405 Emulsion, the glass transition temperature is -19 ℃) 100 parts, 3 parts of lotus leaf hydrophobic agent (selected from Aohan Chemical SC-011 lotus leaf effect hydrophobic agent), 8 parts of polyacrylic acid sodium salt (selected from Dow 731A), poly 6 parts of ether defoamer (selected from BASF 2706), 0.6 parts of thickener (selected from Arkema 3800), 18 parts of deionized water;

[0055] In parts by weight, each raw material is prepared according to the powder formula: 400 parts of ordinary silicate 42.5 grade gray cement, 350 parts of 350 mesh quartz powder, 250 parts of 200 mesh wollastonite powder, polycarboxylate superplasticizer (selected from Dongfangyu Rainbow CR-818)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrophobic polymer cement waterproof coating and a preparation method thereof and relates to the technical field of building materials. The waterproof coating disclosed by the invention is prepared from a liquid material and a powder material, wherein the liquid material is prepared from the following components in parts by weight: 350-470 parts of the first kind of styrene-acrylic emulsion, 30-150 parts of the second kind of styrene-acrylic emulsion, 1-3 parts of lotus-leaf water repellent agent, 3-6 parts of dispersing agent, 3-6 parts of antifoaming agent, 4-20 parts of deionized water and 0.3-0.8 part of thickening agent; the powder material is prepared from the following components in parts by weight: 200-400 parts of ordinary Portland cement, 150-550 parts of wollastonite powder, 150-350 parts of quartz sand, 2-6 parts of water reducing agent and 1-3 parts of early strength agent; the glass transition temperature of the first kind of styrene-acrylic emulsion is minus 10 DEG C to minus 5 DEG C; the glass transition temperature of the second kind of styrene-acrylic emulsion is minus 20 to minus 15 DEG C. The waterproof coating has the advantages of fast drying, high environmental friendliness and excellent mechanical property.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a hydrophobic polymer cement waterproof coating and a preparation method thereof. Background technique [0002] Most of the polymer cement waterproof coatings are two-component waterproof coatings prepared by adding polymer emulsions such as acetic acid-vinyl acetate emulsion (VAE) or acrylate emulsions and their derivatives and cement as the main raw materials, and adding fillers and other additives. . The physical properties of traditional polymer cement waterproof coatings mostly meet the GB / T 23445-2009 standard, but with the development of the industry, the requirements for practical application performance are getting higher and higher. [0003] Among them, the liquid material is made of acetic acid-vinyl acetate emulsion (VAE) or acrylate copolymerized emulsion. Due to the high glass transition temperature and poor flexibility, it is necessary to add plasticizers to incr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D125/14C09D7/61C09D7/63C09D7/65
Inventor 张鑫宇王会元黄凯赵建成张文龙李法鑫
Owner 青岛东方雨虹建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com