Polyaspartic ester urea adhesive and construction technology thereof

A technology of aspartate urea glue and aspartate ester, which is applied in the direction of polyurea/polyurethane coatings and coatings, can solve the problems of poor safety and environmental protection performance, toxic and harmful components, etc., so as to prevent discoloration and avoid volatilization Good effect on toxicity and resilience

Active Publication Date: 2017-12-29
SHENZHEN FEIYANG JUNYAN TECH DEV
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For this reason, the technical problem to be solved by the present invention is that the existing glue for plastic track has toxic and harmful components, and has poor safety and environmental protection performance. Aspartate Urea Adhesive and Its Construction Technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] This embodiment provides a two-component polyaspartate urea adhesive, the adhesive is composed of a main agent and a curing agent, and the equivalent ratio of the two is 1:1.1, wherein in parts by weight, the The main ingredients are as follows:

[0021] 47.5 parts of N,N'-(methylenedi-4,1-cyclohexanediyl) diaspartic acid tetraethyl ester;

[0022] 40 parts of N,N'-(polyoxy(methyl-1,2-ethylene)diyl)diaspartic acid tetraethyl ester;

[0023] 3 parts of oxazolidine absorbent;

[0024] 10 parts of A3 molecular sieve;

[0025] Defoamer BYK085 (Byk Chemicals) 0.3 parts;

[0026] 0.2 parts of wetting agent BorchiGol1375 (Ouanji);

[0027] In parts by weight, the curing agent components are as follows:

[0028] Bayer trimer N3900 30 parts;

[0029] Bayerone diurea N3400 20 parts;

[0030] Hydroxyl modified curing agent 1# 50 parts;

[0031] The mass ratio of the three is 3:2:5.

[0032] Wherein, the preparation method of hydroxyl modified curing agent 1# is as follows...

Embodiment 2

[0036] This embodiment provides a two-component polyaspartate urea adhesive, the adhesive is composed of a main agent and a curing agent, and the equivalent ratio of the two is 1:1, wherein in parts by weight, the The main ingredients are as follows

[0037] 55 parts of N,N'-(methylene di-4,1-cyclohexanediyl) diaspartic acid tetrabutyl ester;

[0038] N,N'-(polyoxy(methyl-1,2-ethylene)diyl)diaspartic acid tetraethyl ester 30 parts;

[0039] 3 parts of oxazolidine absorbent;

[0040] Defoamer BYK085 (Byk Chemicals) 0.4 parts;

[0041] Substrate wetting agent Borchi Gol 1375 (Ouanji) 0.3 parts;

[0042] A3 molecular sieve 11.6 parts.

[0043] In parts by weight, the curing agent components are as follows:

[0044] Bayer trimer N3900 20 parts;

[0045] Bayerone diurea N3400 17 parts;

[0046] Hydroxyl modified curing agent 2# 53 parts;

[0047] The mass ratio of the three is 2:1.7:5.3.

[0048] Wherein, the preparation method of hydroxyl modified curing agent is as follo...

Embodiment 3

[0052] This embodiment provides a two-component polyaspartate urea adhesive, the adhesive is composed of a main agent and a curing agent, and the equivalent ratio of the two is 1:0.9, wherein in parts by weight, the The main ingredients are as follows:

[0053] 30 parts of tetraethyl N,N'-(methylene bis-(1-methyl-4,1-cyclohexanediyl)) diaspartate;

[0054] N,N'-(polyoxy(methyl-1,2-ethylene)diyl)diaspartic acid tetraethyl ester 30 parts;

[0055] 30 parts of N,N'-(methylene di-4,1-cyclohexanediyl) diaspartic acid tetrabutyl ester;

[0056] 5 parts of oxazolidine absorbent;

[0057] Silicone defoamer BYK085 (Byk Chemicals) 0.5 parts;

[0058] 0.5 parts of substrate wetting agent Borchi Gol 1375 (Ouanji);

[0059] 12 parts of A3 molecular sieve.

[0060] In parts by weight, the curing agent component consists of 30 parts of HDI trimer N3900 (Bayer), 20 parts of HDI ketone diurea N3400 (Bayer), 60 parts of hydroxyl resin modified curing agent, the quality of the three compone...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyaspartic ester urea adhesive and a construction technology thereof. The adhesive comprises a main agent and a curing agent in an equivalence ratio being 1:(0.9-1.1), and the main agent is prepared from 80-90 parts by weight of polyaspartic ester resin, 2-5 parts by weight of an oxazolidine absorbent, 8-12 parts by weight of a molecular sieve, 0.1-0.5 parts by weight of a defoaming agent and 0.1-0.5 parts by weight of a base material wetting agent. The adhesive contains no toxic substances such as free TDI (toluene diisocyanate) and the like, contains no organic solvents, phthalate plasticizers and heavy metal, belongs to a solvent-free system, is environmentally friendly, non-toxic and harmless, further has good physical performance and is good in weather fastness, high in tensile strength and elongation at break, good in rebound resilience and not prone to discoloration, construction is easy, operability and physical performance of the adhesive are equivalent to those of a conventional polyurethane adhesive, and excellent environment-friendly safety and physical characteristics are integrated. The technological process of preparation is simple, conditions are mild, construction performance is good, coating is easy, and therefore, the adhesive is suitable for industrial batch production.

Description

technical field [0001] The invention belongs to the technical field of adhesive production, and in particular relates to a polyaspartate urea adhesive used for a water-permeable plastic runway and a construction process thereof. Background technique [0002] With the improvement of people's living standards, leisure sports are becoming more and more popular. The plastic runway is widely used because of its good flatness, moderate hardness and elasticity, which is conducive to the speed and technology of athletes, and can also reduce the rate of falls. It is used in various schools and stadiums, national fitness paths, playground road pavement, indoor and outdoor running tracks, stadiums, parks, residential areas and other activity venues. [0003] The plastic runway is generally paved with synthetic materials. The main production method is to use one-component moisture-cured polyurethane glue mixed with EPDM particles to form an elastic layer with a thickness of about 10mm, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/79C08G18/75C08G18/66C08G18/48C08G18/32C08G18/10C09D123/16C09D175/02C09D7/12
CPCC08G18/10C08G18/325C08G18/48C08G18/6685C08G18/725C08G18/755C08G18/79C08G18/798C09D123/16C09D175/02C08L75/02C08K7/26
Inventor 薛隽鲁晓东邬茳
Owner SHENZHEN FEIYANG JUNYAN TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products