Mint fiber spunlace non-woven mask substrate and preparation method thereof

A peppermint fiber and non-woven technology is applied in the field of peppermint fiber spunlace non-woven mask base fabric and its preparation field, which can solve the problems of large shrinkage and deformation of the fabric, low wet breaking strength, resistance to washing and the like, and achieves the promotion of cell proliferation and growth. , The effect of promoting metabolism and preventing water evaporation

Inactive Publication Date: 2018-01-16
ZHONGYUAN ENGINEERING COLLEGE
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wet breaking strength is small, and the shrinkage deformation of the fabric made of pure viscose fiber is large
The strength of viscose fiber is lower than that of cotton fiber, it is not washable, its elongation at break is higher than that of cotton fiber, it has poor wear resistance, it is easy to deform under small load, it has poor dimensional stability, low stiffness and poor elasticity
[0010] Polyester fiber has the advantages of high strength, good recovery, and good heat setting, but the mass specific resistance of polyester fiber is large, and the electrostatic phenomenon is prominent, which makes it difficult to form a net in the process of carding pure polyester fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Using the above process flow, equipment and technical measures, etc., the mint fiber spunlace nonwoven mask base fabric has been developed, which is made of the following raw materials in the weight ratio: the weight content of mint fiber accounts for 80%, viscose fiber The weight content accounts for 10%, and the weight content of polyester fiber accounts for 10%. The performance index of the spunlace nonwoven mask base fabric is: the actual weight is 65g / m 2 , average thickness 0.45mm; longitudinal strength 91.4N, transverse strength 87.67N, longitudinal and transverse strength ratio 1.04:1; longitudinal elongation at break 21.73%, transverse elongation at break 35.6%, longitudinal and transverse elongation at break ratio 0.61:1 ; Longitudinal tear strength 11.7N, transverse tear strength 13.0N, longitudinal and transverse tear strength ratio 0.96:1. The antibacterial rate of Staphylococcus aureus (ATCC6538) was 89.1%, the antibacterial rate of Escherichia coli (8089...

Embodiment 2

[0050] Utilizing the above technological process, equipment and technical measures, etc., the mint fiber spunlace nonwoven mask base fabric has been developed, which is made of the following raw materials in the weight ratio: the weight content of mint fiber accounts for 60%, and the weight content of viscose fiber The weight content accounts for 10%, and the weight content of polyester fiber accounts for 30%. The performance index of the spunlace nonwoven mask base fabric is: the actual weight is 59.72g / m 2, average thickness 0.37mm; longitudinal strength 105.57N, transverse strength 97.79N, longitudinal and transverse strength ratio 1.08:1; longitudinal elongation at break 24.43%, transverse elongation at break 37.54%, longitudinal and transverse elongation at break ratio 0.65:1 ; The longitudinal tear strength is 14.69N, the transverse tear strength is 15.62N, and the longitudinal and transverse tear strength ratio is 0.94:1. The antibacterial rate of Staphylococcus aureus...

Embodiment 3

[0052] Using the above technological process, equipment and technical measures, etc., the mint fiber spunlace nonwoven mask base fabric has been developed, which is made of the following raw materials in the weight ratio: the weight content of mint fiber accounts for 100%, and the weight content of viscose fiber The weight content accounts for 0%, and the weight content of polyester fiber accounts for 0%. The performance index of the spunlace nonwoven mask base fabric is: the actual weight is 51.47g / m 2 , average thickness 0.38mm; longitudinal strength 60.25N, transverse strength 54.88N, longitudinal and transverse strength ratio 1.10:1; longitudinal elongation at break 22.88%, transverse elongation at break 35.75%, longitudinal and transverse elongation at break ratio 0.64:1 ; Longitudinal tear strength 8.75N, transverse tear strength 8.88N, longitudinal and transverse tear strength ratio 0.99:1. The antibacterial rate of Staphylococcus aureus (ATCC6538) was 92.9%, that of E...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tear loadaaaaaaaaaa
tear loadaaaaaaaaaa
Login to View More

Abstract

The invention relates to an antibacterial healthcare spunlace fabric, in particular to a preparation method and application of a mint fiber spunlace non-woven mask substrate. The mint fiber spunlace non-woven mask substrate is prepared from, by weight, 10-100% of mint fiber, 0-90% of copper ammonia fiber, 0-90% of pearl fiber, 0-90% of viscose and 0-90% of polyester fiber. The mint fiber spunlacenon-woven mask substrate has the advantages that the developed mint fiber spunlace non-woven mask substrate is soft in touch and good in adsorption, has the water wetting and lightsome skin feeling and has the efficient anti-aging, anti-radiation, anti-bacterial and anti-oxidative effects, and the mask substrate has the functions of preserving moisture, activating cells, supplying oxygen and the like, and achieves the nourishing, nutritional and healthcare effects on the skin.

Description

technical field [0001] The invention relates to a health-care spunlace cloth for medical textiles, in particular to a mint fiber spunlace nonwoven fabric processed by mixing mint fiber, cupro fiber, pearl fiber, viscose fiber and polyester fiber. Mask base fabric and its preparation method and application. Background technique [0002] After the pre-wetted fiber web enters the spunlace area, multiple streams of extremely fine high-pressure clustered water jets are ejected from the small holes of the water jet plate of the spunlace head, and shoot vertically to the fiber web, causing a part of the surface fibers in the fiber web to displace and vertically Net bottom movement, when the water needle penetrates the fiber net, it is rebounded by the conveying net curtain against the high-pressure water flow, and scatters to the opposite side of the fiber net in different directions. Movement, interspersion, entanglement, and cohesion occur between them, forming countless soft en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D04H1/42D04H1/4258D04H1/435D04H1/492
Inventor 赵博
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products