Nano silica-modified core-shell acetic acrylic emulsion flame-retardation high-speed cigarette nozzle connecting adhesive and preparation method thereof

A nano-silica, vinegar-acrylic emulsion technology, applied in the direction of adhesive types, non-polymer adhesive additives, monocarboxylate copolymer adhesives, etc., can solve the unsatisfactory flame retardant effect of flame retardants and other issues, to achieve the effect of being conducive to movement and diffusion, good water resistance, and low glass transition temperature

Inactive Publication Date: 2018-01-26
CHUZHOU GUANGWEI CHEM
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flame retardant effect of this method is not ideal due to agglomeration or uneven coating. Therefor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A core-shell vinegar-acrylic emulsion modified by nano-silica flame-retardant high-speed cigarette tip glue, characterized in that the high-speed cigarette tip glue uses vinyl acetate as a hard monomer, butyl acrylate and isoacrylate Octyl ester is a soft monomer, acrylic acid is a cross-linking monomer, and flame retardant, nano-silica and other additives are added, and it is prepared by core-shell emulsion polymerization; the other additives are polyvinyl alcohol 1788 , emulsifier, potassium persulfate and hydroxymethylcellulose, wherein the amount of polyvinyl alcohol 1788 is 4% of the total amount of monomers, the amount of emulsifier is 2.6% of the total amount of monomers, and the amount of potassium persulfate is 4% of the total amount of monomers. 1.3% of the total amount, and the amount of hydroxymethylcellulose is 0.8% of the total amount of monomers.

[0018] The mass ratio of vinyl acetate: butyl acrylate: isooctyl acrylate: acrylic acid is 15:3:2:2.

[001...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nano silica-modified core-shell acetic acrylic emulsion flame-retardation high-speed cigarette nozzle connecting adhesive and a preparation method thereof. The method employsa core-shell emulsion polymerisation method, the butyl acrylate monomer and iso-octyl acrylate-modified acetic acrylic emulsion adhesive are synthesized, the emulsion particles have a core-shell structure having a hard core and a soft shell, persistent adhesivity of the adhesive is guaranteed, film forming temperature is obviously reduced, and primary viscosity is increased; iso-octyl acrylate induced in a shell layer substitutes partial butyl acrylate, the primary viscosity is further increased, and the emulsion viscosity is reduced; a fire retardant and nano silica are introduced into the polymerization process, compatibility with a polymer is increased, dispersion is uniform, so that the acetic acrylic emulsion has better water proofness, stain resistance, and solvent resistance, the prepared core-shell acetic acrylic emulsion is used as the nozzle connecting adhesive, through testing by a M5 cigarette maker, sealing degree of cigarette loading is high, bonding effect is good, andthe flame-retardation self-extinguishing character is obvious.

Description

technical field [0001] The invention relates to the technical field of cigarette adhesives, in particular to a core-shell type vinegar-acrylic emulsion modified by nano-silica and a flame-retardant high-speed cigarette joint glue and a preparation method. Background technique [0002] With the development of tobacco technology, "smoking and safety" and "smoking and health" advocated by the tobacco industry have become a trend and main content. From the perspective of safety, it is required to minimize the damage of smoking (smoke) to the human body, including reducing the pollution of the sidestream smoke of cigarettes to the environment; on the other hand, it is proposed to "reduce the tendency of ignition" of cigarettes to prevent smoking from causing fires . The combustion process of cigarettes belongs to smoldering, flameless, slow and low-temperature combustion process. With the consumption of oxygen in cigarettes, to maintain the combustion of cigarettes, oxygen must ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J131/04C09J11/04C08F2/26C08F2/30C08F2/44C08F218/08C08F220/18C08F220/06
Inventor 李勇
Owner CHUZHOU GUANGWEI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap