Novel catalyst used in production of methyl ethyl ketone and preparation method thereof

A technology of catalyst and methyl ethyl ketone, which is applied in the field of new catalyst and its preparation, to achieve the effects of enhanced penetration, conversion rate and methyl ethyl ketone selectivity, and wide application range

Active Publication Date: 2018-01-30
台州路豹鞋业有限公司
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned preparation processes all have the advantages of simple process, mild reaction conditions, environmental friendliness, and low production cost. However, the concentration of the raw material solution (10-90wt%) applicable to the catalyst needs to be further expanded, and the catalyst itself needs to be modified so that the raw material solution can be Further improve the selectivity of the product methyl ethyl ketone while obtaining a higher conversion rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of preparation method of the used novel catalyst of producing methyl ethyl ketone, is to realize by following steps:

[0026] 1) Preparation of carrier

[0027] Add sodium aluminate and water into the beaker and stir evenly, then add [choline][aspartic acid] ionic liquid and continue to stir for 1h; then add tetraethyl silicate dropwise to it and continue to stir for 2h. The pH value was adjusted to 10 to obtain a mixture; the mixture was transferred to a polytetrafluoroethylene crystallization kettle and treated at 130°C for 72h, filtered and washed at 105 o C for 12 hours, then at 550 o Calcined at C for 5h to obtain KIT molecular sieve; wherein, SiO in the mixture 2 、Al 2 o 3 , [choline] [aspartic acid] ionic liquid, the molar ratio of deionized water is 1.0:0.05:0.02:120;

[0028] 2) Carrier pretreatment

[0029] Put the KIT molecular sieve in 1mol / L ammonium nitrate solution for ion exchange, the operating condition is stirring at 60°C for 15h, then fi...

Embodiment 2

[0034] A kind of preparation method of novel catalyst used for producing methyl ethyl ketone is realized by following steps:

[0035] 1) Preparation of carrier

[0036] Add sodium aluminate and water into the beaker and stir evenly, then add [choline][aspartic acid] ionic liquid and continue to stir for 1h; then add tetraethyl silicate dropwise to it and continue to stir for 2h. The pH value was adjusted to 12 to obtain a mixture; the mixture was transferred to a polytetrafluoroethylene crystallization kettle for 48 hours at 160°C, filtered and washed at 105 o C for 12 hours, then at 550 o Calcined at C for 5h to obtain KIT molecular sieve; wherein, SiO in the mixture 2、 Al 2 o 3、 The molar ratio of [choline][aspartic acid] ionic liquid to deionized water is 1.0:0.05:0.05:120;

[0037] 2) Carrier pretreatment

[0038] Put the KIT molecular sieve in 1mol / L ammonium nitrate solution for ion exchange, the operating condition is stirring at 80°C for 12h, then filtering, washin...

Embodiment 3

[0043] A kind of preparation method of the used novel catalyst of producing methyl ethyl ketone, is to realize by following steps:

[0044] 1) Preparation of carrier

[0045] Add sodium aluminate and water into the beaker and stir evenly, then add [choline][aspartic acid] ionic liquid and continue to stir for 1h; then add tetraethyl silicate dropwise to it and continue to stir for 2h. The pH value was adjusted to 11 to obtain a mixture; the mixture was transferred to a polytetrafluoroethylene crystallization kettle and treated at 145°C for 60h, filtered and washed at 105 o C for 12 hours, then at 550 o Calcined at C for 5h to obtain KIT molecular sieve; wherein, SiO in the mixture 2、 Al 2 o 3、 The molar ratio of [choline][aspartic acid] ionic liquid to deionized water is 1.0:0.05:0.035:120;

[0046] 2) Carrier pretreatment

[0047] Put the KIT molecular sieve in 1mol / L ammonium nitrate solution for ion exchange, the operating condition is stirring at 70°C for 13h, then f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel catalyst used in production of methyl ethyl ketone and a preparation method thereof. The method comprises the following steps: preparing a KIT-1 molecular sieve with amesoporous structure by taking ionic liquid, namely, [choline][aspartic acid] as a template agent, wherein the KIT-1 molecular sieve is taken as a catalyst carrier; meanwhile, loading elements V and Zn onto the catalyst carrier by a supercritical impregnation technology to obtain a methyl ethyl ketone catalyst which has the advantages of insusceptibility to inactivation, high hydrothermal stability, wide application range of reaction raw material concentration (5 to 100 percent), and remarkable increase in 2,3-butanediol transformation rate and methyl ethyl ketone selectivity.

Description

technical field [0001] The invention belongs to the technical field of methyl ethyl ketone production, and relates to a novel catalyst used in the production of methyl ethyl ketone and a preparation method thereof. Background technique [0002] Methyl ethyl ketone is an organic solvent with outstanding properties. It has moderate boiling point, outstanding solvency, good drying characteristics, good stability, fast volatilization speed, low viscosity and low toxicity. It is a second only Ketone solvents based on acetone. Methyl ethyl ketone can be used as a solvent for polymer compounds such as polyurethane, nitrocellulose, acrylic resin, vinyl acid resin, phenolic resin, alkyd resin, ink, tape, paint, adhesive and lubricating oil dewaxing. It is the most suitable solvent for "triphenyl" Good substitute. In addition, methyl ethyl ketone is widely used in industrial fields such as coatings, inks, adhesives, magnetic tapes, oil refining, electronic components, and medicine. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/78B01J35/10C07C45/52C07C49/10
CPCY02P20/54
Inventor 李俊霞
Owner 台州路豹鞋业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap