Environment-friendly anti-fouling material based on silicone hydrogel resin and natural anti-fouling agent

A technology of silicone hydrogel and natural antifouling agent, which is applied in antifouling/underwater coatings, biocide-containing paints, coatings, etc., and can solve the problem of limiting the development of hydrogel antifouling coatings and coating surfaces Poor adhesion, poor mechanical properties and other problems, to achieve the effect of improving adhesion and weather resistance, strong adhesion, and lasting stability

Active Publication Date: 2018-02-02
ZHEJIANG MARINE DEV RES INST
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the research on hydrogel is still in the stage of theoretical research. Although a large number of experiments have proved that hydrogel has excellent anti-adhesive and anti-fouling effects, there are still certain defec

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly anti-fouling material based on silicone hydrogel resin and natural anti-fouling agent
  • Environment-friendly anti-fouling material based on silicone hydrogel resin and natural anti-fouling agent
  • Environment-friendly anti-fouling material based on silicone hydrogel resin and natural anti-fouling agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The preparation route of embodiment 1 and embodiment 3~5 is as follows:

[0035]

[0036] Wherein, x, y, z and n are all integers ≥ 1.

[0037] Example 1:

[0038] The preparation method of the environment-friendly antifouling material based on silicone hydrogel resin and natural antifouling agent, comprises the following steps:

[0039] (1) Using allyl polyglycol ether and hydrogen-containing silicone oil as starting materials, heat to 70°C for hydrosilation reaction, then add fully swollen and dissolved butyl rubber in xylene, and continue the reaction for 50 minutes to prepare into silicone hydrogel resin;

[0040] (2) Keeping the reaction temperature constant, add thixotropic agent, hydroxyl silicone oil, 3-hydroxybutenoic acid-β-lactone, 4,5-dichloro-2 to the silicone hydrogel resin obtained in step (1) -n-octyl-4-isothiazolin-3-one, synthetic camphor and cage polysilsesquioxane, stirred and reacted for 1 hour to obtain component A, set aside;

[0041] (3) M...

Embodiment 2

[0054] The preparation method of the environment-friendly antifouling material based on silicone hydrogel resin and natural antifouling agent, comprises the following steps:

[0055] (1) Using ethylene glycol monoallyl ether and hydrogen-containing silicone oil as starting materials, heating to 90°C for hydrosilation reaction, then adding fully swollen and dissolved butyl rubber in xylene, and continuing the reaction for 70 minutes to prepare into silicone hydrogel resin;

[0056] (2) Keeping the reaction temperature constant, add thixotropic agent, hydroxyl silicone oil, 3-hydroxybutenoic acid-β-lactone, 4,5-dichloro-2 to the silicone hydrogel resin obtained in step (1) - n-octyl-4-isothiazolin-3-one, synthetic camphor and cage polysilsesquioxane, stirred and reacted for 2 hours to obtain component A, set aside;

[0057] (3) Mix ethyl orthosilicate with di-n-butyltin dilaurate, methyltriethoxysilane, cyclohexanone, acetylacetone and xylene to obtain component B;

[0058] (4...

Embodiment 3

[0071] The preparation method of the environment-friendly antifouling material based on silicone hydrogel resin and natural antifouling agent, comprises the following steps:

[0072] (1) Using allyl polyglycol ether and hydrogen-containing silicone oil as starting materials, heat to 80°C for hydrosilation reaction, then add fully swollen and dissolved butyl rubber in xylene, and continue the reaction for 60 minutes to prepare into silicone hydrogel resin;

[0073] (2) Keeping the reaction temperature constant, add thixotropic agent, hydroxyl silicone oil, 3-hydroxybutenoic acid-β-lactone, 4,5-dichloro-2 to the silicone hydrogel resin obtained in step (1) -n-octyl-4-isothiazolin-3-one, synthetic camphor and cage polysilsesquioxane, stirred and reacted for 1 hour to obtain component A, set aside;

[0074] (3) Mix ethyl orthosilicate with di-n-butyltin dilaurate, methyltriethoxysilane, cyclohexanone, acetylacetone and xylene to obtain component B;

[0075] (4) Mix component A a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of an environment-friendly anti-fouling material based on silicone hydrogel resin and a natural anti-fouling agent. The preparation method includes: usingallyl polyglycol ether or 2-allyloxyethanol and hydrogen-containing silicone oil as the initial raw materials, heating to perform hydrogen silicification reaction, adding butyl rubber sufficiently swollen and dissolved in xylene, and continuing reaction to prepare silicone hydrogel resin; keeping reaction temperature unchanged, adding a thixotropic agent, hydroxyl silicone oil, diketen, 4, 5-dichloro-2-n-octyl-4-isothiazolin-3-one, synthetic camphor and polyhedral oligomeric silsesquioxane, and performing stirring reaction to obtain a component A for standby; evenly mixing tetraethyl orthosilicate with di-n-butyltin dilaurate, methyl triethoxysilane, cyclohexanone, acetylacetone and xylene to obtain a component B; evenly mixing the component A and the component B according to the mass ratio of (7-9):1, and solidifying for 5-8 hours to obtain the anti-fouling material.

Description

technical field [0001] The invention relates to an antifouling material, in particular to an environment-friendly antifouling material based on silicone hydrogel resin and natural antifouling agent. Belongs to the technical field. Background technique [0002] Marine biofouling refers to the biofouling formed by the adsorption, growth and reproduction of marine microorganisms, plants and animals on the surface of ships and marine facilities, which brings many disadvantages to human beings engaged in marine activities. Brushing antifouling paint is widely used in the world as the main antifouling means, among which, tributyltin (TBT) and copper-containing antifouling paint are the most significant. However, antifouling agents in coatings can enrich human health and ecological security through food chain enrichment. In recent years, urgent attention to marine environmental issues has prompted people to continuously study new environmentally friendly antifouling coatings. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/10C09D5/16C09D7/61C09D7/63C09D7/65C08G77/46C08G77/442
CPCC08G77/442C08G77/46C08L2205/02C08L2205/035C09D5/1618C09D5/1625C09D5/1675C09D5/1687C09D183/10C08L83/06C08L83/04C08K5/00C08K5/1525C08K5/07C08K5/47C08K5/5419
Inventor 胡建坤陆阿定沈思哲张海春孙宝库
Owner ZHEJIANG MARINE DEV RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap