Catalyst for production of vinyl acetate

A vinyl acetate and catalyst technology, applied in the field of vinyl acetate synthesis, can solve the problems of environmental pollution, corrosion, unspecified catalyst activity data, etc., and achieve the effect of improving selectivity and reducing benzene content

Active Publication Date: 2018-03-09
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent (CN 86107833A, a catalyst for the synthesis of vinyl acetate and its preparation method) reported ZnO-ZnCl 2 / C catalyst has a higher space-time yield than Zn(OAc) 2 / C catalyst is about 30%, but because of the use of nitrate in the preparation process of the catalyst, a large amount of NO will be generated during decomposition x And pollute the environment, and ZnCl is added in the catalyst 2 , Cl - It is corrosive to equipment, which limits the promotion of this catalyst
Chinese patent (CN 102284304A, a preparation method of a high-efficiency catalyst for the synthesis of vinyl acetate by acetylene method) in addition to hydrogen peroxide, also selects a series of oxidants such as sulfuric acid, potassium permanganate and ammonium persulfate to pretreat activated carbon and use it to synthesize acetic acid Preparation of ethylene catalyst, the patent only reports the percentage of vinyl acetate in the product, and does not indicate the activity data of the catalyst
And academia and industry mainly focus on the problems such as improving catalyst activity and catalyst life-span for the research work of acetylene method vinyl acetate catalyst, for improving the selectivity of catalyst, especially the problem of reducing by-product benzene content has not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for production of vinyl acetate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The preparation of catalyst: with 102g zinc acetate (C 4 h 6 o 4 Zn), cadmium acetate containing 3.1g Cd (C 4 h 6 o 4 Cd) fully mixed and dissolved in acetic acid aqueous solution to obtain 350ml of impregnation solution with a pH of 4.8, and 1L of 3mm in diameter, 2cm in length, and 0.80cm in pore volume 3 / g, the specific surface area is 1200m 2 / g columnar coal-based activated carbon carrier was impregnated in the above impregnating solution, left to stand for 3 hours and dried at 110°C to obtain the catalyst. The zinc acetate content of this catalyst measured by ICP is 102g / L, and the Cd content is 3.1g / L.

[0039] The synthesis of vinyl acetate: 30ml catalyst is packed in the miniature fixed-bed reactor, with N 2 After leak test, use N 2 Fully purge the system, after the system heats up, turn off the N 2 , cut into acetylene in turn, turn on the acetic acid pump, control the reaction temperature to 180°C, and the reaction pressure to 0.20atm; raw material ...

Embodiment 2

[0054] The preparation of catalyst: with 102g zinc acetate (C 4 h 6 o 4 Zn), scandium trichloride (ScCl) containing 3.1g Sc 3 ) were fully mixed and dissolved in acetic acid aqueous solution to obtain 350ml of impregnation solution with a pH of 4.8, and 1L of 3mm in diameter, 2cm in length, and 0.80cm in pore volume 3 / g, the specific surface area is 1200m 2 / g columnar coal-based activated carbon carrier was impregnated in the above impregnating solution, left to stand for 3 hours and dried at 110°C to obtain the catalyst. The zinc acetate content of this catalyst measured by ICP is 102g / L, and the Sc content is 3.1g / L.

[0055] The synthesis of vinyl acetate: 30ml catalyst is packed in the miniature fixed-bed reactor, with N 2 After leak test, use N 2 Fully purge the system, after the system heats up, turn off the N 2 , cut into acetylene in turn, turn on the acetic acid pump, control the reaction temperature to 180°C, and the reaction pressure to 0.20atm; raw materia...

Embodiment 3

[0059] The preparation of catalyst: with 102g zinc acetate (C 4 h 6 o 4 Zn), mercury acetate containing 3.1g Hg (C 4 h 6 o 4 Hg) is fully mixed and dissolved in acetic acid aqueous solution to obtain 350ml of impregnation solution with a pH of 4.8, and 1L of 3mm in diameter, 2cm in length, and 0.80cm in pore volume 3 / g, the specific surface area is 1200m 2 / g columnar coal-based activated carbon carrier was impregnated in the above impregnating solution, left to stand for 3 hours and dried at 110°C to obtain the catalyst. The zinc acetate content of this catalyst measured by ICP is 102g / L, and the Hg content is 3.1g / L.

[0060] The synthesis of vinyl acetate: 30ml catalyst is packed in the miniature fixed-bed reactor, with N 2 After leak test, use N 2 Fully purge the system, after the system heats up, turn off the N 2 , cut into acetylene in turn, turn on the acetic acid pump, control the reaction temperature to 180°C, and the reaction pressure to 0.20atm; raw material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a catalyst for production of vinyl acetate. The problem that the byproduct benzene content is high in the prior art is mainly solved. By adoption of the technical scheme, thecatalyst for production of vinyl acetate takes activated carbon as a carrier, active components comprise zinc acetate and a cocatalyst, and the cocatalyst comprises at least one metal element selectedfrom IIB group elements, so that the problem is solved well and the catalyst can be applied to industrial production of synthesizing vinyl acetate by an acetylene method.

Description

technical field [0001] The invention relates to a catalyst for producing vinyl acetate, a preparation method of the catalyst, and a synthesis method of vinyl acetate. Background technique [0002] Vinyl acetate, referred to as vinyl acetate (VAM), is an important organic chemical raw material, mainly used in the production of polyvinyl acetate (PVAc), polyvinyl alcohol (PVOH), vinyl acetate-ethylene copolymer emulsion (VAE) or copolymer resin (EVA), vinyl acetate-vinyl chloride copolymer (EVC), polyacrylonitrile comonomer and acetal resin derivatives, in coatings, pastes, adhesives, vinylon, films, leather processing, synthetic fibers, soil Improvement and other aspects have extensive development and utilization value. With the continuous progress of production technology, its application field is still expanding. [0003] In 2011, the global production capacity of vinyl acetate reached 7.434 million tons per year, mainly concentrated in Asia, North America and Western Eur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J31/04B01J31/26C07C67/04C07C69/15
CPCB01J31/04B01J31/26C07C67/04C07C69/15
Inventor 邱鹏远杨运信张丽斌
Owner CHINA PETROLEUM & CHEM CORP