Complete-extinction network stretch yarn and preparation method thereof

A technology of full matting and elastic yarn, which is applied in rayon manufacturing, melt spinning, filament/thread forming, etc. It can solve problems such as difficulty in achieving matting effect, high fiber unevenness, and affecting fiber performance, so as to improve strength , low gloss, and the effect of improving compatibility

Active Publication Date: 2018-04-13
JIANGSU HENGLI CHEM FIBER
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In recent years, the application range of the full-dull network elastic yarn made of PET has gradually increased. However, the glossiness of the fully-dull network elastic yarn prepared by the prior art is still high, and it is difficult to achieve the daily required matting effect. The oil agent used in the process volatilizes quickly and is easy to bond on the surface of the fiber, resulting in a high unevenness of the fiber and affecting the performance of the fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Complete-extinction network stretch yarn and preparation method thereof
  • Complete-extinction network stretch yarn and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A preparation method of full-dull network elastic yarn, the steps are as follows:

[0053] (1) Preparation of oiling agent for oiling: 2-hydroxymethyl-12-crown-4 and dodecyl phosphate potassium salt, trimethylolpropane laurate and sodium dodecyl sulfonate After mixing evenly at room temperature, add it to 9# mineral oil and stir evenly at 40°C for 1 hour to obtain an oil agent. The amount of each component added is as follows: 9# mineral oil is 2 parts; trimethylolpropane Lauric acid ester is 10 parts; 2-hydroxymethyl-12-crown-4 is 90 parts; dodecyl phosphate potassium salt is 8 parts; sodium dodecylsulfonate is 3 parts; the prepared oil The content of the crown ether is 79.6wt%, and the high temperature resistance of the oil is excellent, and the thermal weight loss is 14.5wt% after heat treatment at 200°C for 2 hours; the viscosity of the oil is low, and the kinematic viscosity 29.6mm 2 / s, the kinematic viscosity after the concentration of 10wt% emulsion is configu...

Embodiment 2

[0058] A preparation method of full-dull network elastic yarn, the steps are as follows:

[0059] (1) Preparation of oiling agent for oiling: 15-crown ether-5 and isomeric tridecanol polyoxyethylene ether phosphate potassium salt, trimethylolpropane laurate and sodium pentadecylsulfonate in After mixing evenly at room temperature, add it to 10# mineral oil and stir evenly at 43°C for 1.5 hours to obtain the oil agent. In parts by weight, the addition amount of each component is as follows: 10# mineral oil is 2 parts; 15 parts of propane laurate; 70 parts of 15-crown-5; 10 parts of potassium isotridecyl polyoxyethylene ether phosphate; 7 parts of sodium pentadecyl sulfonate; prepared oil The content of crown ether in the agent is 67.30wt%. The high temperature resistance of the oil agent is excellent. After heat treatment at 200°C for 2 hours, the thermal weight loss is 13wt%. The viscosity of the oil agent is low. 28.1mm 2 / s, the kinematic viscosity after the concentration ...

Embodiment 3

[0064] A preparation method of full-dull network elastic yarn, the steps are as follows:

[0065] (1) Preparation of oiling agent for oiling: mix 2-hydroxymethyl-15-crown-5 with potassium salt of tetradecyl phosphate, trimethylolpropane laurate and sodium pentadecylsulfonate After mixing evenly at room temperature, add it to 11# mineral oil and stir evenly at 48°C for 3 hours to obtain an oil agent. The addition amount of each component is as follows in parts by weight: 11# mineral oil is 8 parts; 10 parts of propane laurate; 85 parts of 2-hydroxymethyl-15-crown-5; 11 parts of potassium tetradecyl phosphate; 5 parts of sodium pentadecylsulfonate; The content of crown ether in the oil is 70.83wt%. The high temperature resistance of the oil is excellent. After heat treatment at 200°C for 2 hours, the thermal weight loss is 11wt%. The viscosity of the oil is low. Viscosity is 30.1mm 2 / s, the kinematic viscosity after the concentration is 10wt% emulsion configured with water is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
surface tensionaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a complete-extinction network stretch yarn and a preparation method thereof. The preparation method comprises the following steps: metering, extruding, cooling, oiling and winding polyester melt to obtain POY yarns, enabling the POY yarns to pass through a yarn guide pipe and a network, heating and stretching the POY yarns, false twisting the POY yarns, thermosetting, winding molding the POY yarns to obtain DTY yarns, thus obtaining the complete-extinction network stretch yarns, wherein oil for oiling comprises crown ether, the content of the crown ether is 67.30 to 85.58 percent by weight, a matt agent is dispersed in the polyester melt, the matt agent is a mixture of amorphous titanium dioxide and amorphous silicon dioxide or a mixture of calcium carbonate and amorphous silicon dioxide. The gloss of the prepared complete-extinction network stretch yarn is less than 20 percent, a curling shrinkage rate is greater than or equal to 35 percent, and the curling stability is 75 to 85 percent. The method is simple and reasonable, and the prepared complete-extinction network stretch yarn has the advantages of complete extinction and good performance and is high in popularization value.

Description

technical field [0001] The invention belongs to the field of fiber preparation, and relates to a full-dull network elastic yarn and a preparation method thereof. Background technique [0002] Since the appearance of polyethylene terephthalate (PET) fiber, it has developed rapidly because of its excellent performance, and its output has become the crown of synthetic fiber in the world. Polyester fiber has a series of excellent properties such as high breaking strength, high elastic modulus, moderate resilience, excellent heat setting performance, good heat resistance and light resistance, acid resistance, alkali resistance and corrosion resistance, and the fabric prepared from it has wrinkle resistance. And crispness and other advantages, so polyester fiber is widely used in clothing and home textiles and other fields. [0003] Due to the small dielectric constant, low moisture regain and high friction coefficient of most PET fibers, spinning oil must be used in the spinning...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10D01D5/08D01D5/088D01D5/096D01D7/00D06M13/02D06M13/11D06M13/224D06M13/256D06M13/292D06M101/32
CPCD01D5/08D01D5/088D01D5/096D01D7/00D01F1/10D01F6/92D06M13/02D06M13/11D06M13/224D06M13/256D06M13/292D06M2101/32
Inventor 张学东沈建根马文平王锋宾袁正平
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com