Gas-shielded flux-cored wire for welding of SUS316L austenitic stainless steel deep-cooling low-temperature storage and transportation container and device

A technology of austenitic stainless steel and flux-cored wire, applied in welding equipment, welding equipment, arc welding equipment, etc., can solve the mismatch between tensile strength and base metal, ultra-low temperature impact energy, intergranular corrosion resistance, etc. question

Active Publication Date: 2018-05-01
ATLANTIC CHINA WELDING CONSUMABLES
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the patent is applied to the welding of SUS316L austenitic stainless steel cryogenic storage and transportation containers and equipment, the chemical composition of the weld deposited metal, the tensile strength and the base metal will not match, and the ultra-low temperature impact energy and intergranular corrosion resistance will not meet the standards. Defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Choose the ultra-low carbon stainless steel strip of 76kg, by mass percent, described ultralow carbon stainless steel strip comprises following composition (wt%): C 0.0093, Mn 1.16, Si 0.32, Cr 18.65, Ni 10.84, Cu 0.006, S 0.003, P0.011, N 0.021, Mo 2.55, the balance is Fe and unavoidable impurities.

[0037] The weight of each component in the drug core is as follows: TiO 2 96.52wt%, S 0.022wt%, P 0.027wt% natural rutile 5.85kg; containing SiO 2 99.4wt%, Al 2 o 3 0.8kg of quartz sand with 0.33wt%, S 0.019wt%, P 0.023wt%; containing TiO 2 72.7wt%, NaO 2 1.3kg of sodium titanate with 16.8wt%, S 0.025wt%, P 0.034%; 0.25kg of sodium fluoride containing NaF99.6wt%; containing Al 2 o 3 0.125kg of calcined α-alumina with 98.2wt%, S≤0.017wt%, P≤0.24wt%, nitrogen containing Cr 62.4wt%, N7.4wt%, C 0.044wt%, S 0.023wt%, P 0.027wt% 0.025kg ferrochromium; 0.05kg spray ferrosilicon containing Si 45.0wt%, C 0.087wt%, S 0.011wt%, P 0.031wt%; containing Mn 99.7wt%, C 0.03...

Embodiment 2

[0044] In this example, except that the weights of the components in the flux core are different, other conditions and manufacturing process are the same as those in Example 1 to obtain 2# flux-cored welding wire.

[0045] Wherein, the present embodiment selects 76 kg of ultra-low carbon stainless steel strips, and takes the drug core, and the weight of each component in the drug core is as follows: 2 96.52wt%, S 0.022wt%, P 0.027wt% natural rutile 4.9kg; containing SiO 2 99.4wt%, Al 2 o 3 0.33wt%, S 0.019wt%, P 0.023wt% quartz sand 1.2kg; containing TiO 2 72.7wt%, NaO 2 0.7kg of sodium titanate with 16.8wt%, S 0.025wt%, P 0.034%; 0.25kg of sodium fluoride containing NaF 99.6wt%; containing Al 2 o 3 98.2wt%, S≤0.017wt%, P≤0.24wt% calcined α-alumina 0.21kg; nitrogen containing Cr62.4wt%, N7.4wt%, C 0.044wt%, S 0.023wt%, P 0.027wt% 0.15kg ferrochrome; 0.04kg spray ferrosilicon containing Si 45.0wt%, C0.087wt%, S 0.011wt%, P 0.031wt%; containing Mn 99.7wt%, C 0.035wt%,...

Embodiment 3

[0049] In this example, except that the weights of the components in the flux core are different, other conditions and manufacturing process are the same as those in Example 1, and 3# flux-cored welding wire is obtained.

[0050] Wherein, the present embodiment selects 76 kg of ultra-low carbon stainless steel strips, and takes the drug core, and the weight of each component in the drug core is as follows: 4.25 kg of natural rutile containing TiO2 96.52wt%, S 0.022wt%, P 0.027wt%; 1.9kg of quartz sand with SiO2 99.4wt%, Al2O3 0.33wt%, S 0.019wt%, P 0.023wt%; 1.8kg of sodium titanate containing TiO2 72.7wt%, NaO2 16.8wt%, S 0.025wt%, P 0.034% ; 0.3kg of sodium fluoride containing NaF 99.6wt%; 0.275kg of calcined α-alumina containing Al2O3 98.2wt%, S ≤ 0.017wt%, P ≤ 0.24wt%; containing Cr62.4wt%, N7.4wt%, C 0.12kg of ferrochrome nitride with 0.044wt%, S 0.023wt%, P 0.027wt%; 0.085kg of sprayed ferrosilicon containing Si 45.0wt%, C0.087wt%, S 0.011wt%, P 0.031wt%; containing Mn ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a gas-shielded flux-cored wire for welding of a SUS316L austenitic stainless steel deep-cooling low-temperature storage and transportation container and device and the preparation method thereof. The as-shielded flux-cored wire comprises a steel strip and a flux core wrapped in the steel strip, and the flux core comprises the following components of, by weight, 4.25-5.85 parts of natural rutile, 0.8-1.9 parts of quartz sand, 0.7-1.8 parts of sodium titanate, 0.25-0.3 part of sodium fluoride, 0.125-0.275 part of calcined alpha alumina, 0. 27wt% of calcined alpha aluminaand 0.025-0.15 part of nitrogen-containing ferrochromium, 0.085-0.05 part of spray silicon iron, 1.05-1.45 parts of electrolytic manganese, 3.6-4.85 parts of metal chromium, 6.42-6.85 parts of atomized iron powder, 1. 9-2.5 parts of nickel powder, and 1.0-1.35 parts of molybdenum. The gas-shielded flux-cored wire has the advantages that efficient semi-automatic and automatic welding technologies are achieved, the welding efficiency is high, splashing is low, the appearance is attractive, the welding current is wide, and the voltage adaptability strong.

Description

technical field [0001] The field of welding technology of the present invention, more specifically, relates to a kind of welding wire that meets the corresponding technical requirements of GB / T17853 standard and AWSA5.22 standard E316LT1-1 type flux cored wire, and has high strength and extremely Excellent low-temperature plasticity and toughness are mainly used for welding SUS316L austenitic stainless steel cryogenic storage and transportation containers, equipment (LNG storage tanks, LNG carriers, LNG satellite stations, LNG tankers, ultra-low temperature refrigerators, ultra-low temperature refrigeration equipment, etc.) Flux-cored welding wire and its production process. Background technique [0002] SUS316L steel is a commonly used austenitic stainless steel, which has been widely used in the LNG industry because of its good comprehensive properties, and the cryogenic welding consumables for SUS316L are mainly manual welding rods and solid welding wires. [0003] Wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/368B23K35/40B23K9/16
CPCB23K9/16B23K35/368B23K35/40
Inventor 赵佳张晓柏蒋勇袁均山刘奇望
Owner ATLANTIC CHINA WELDING CONSUMABLES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com