Antirust agent for autoclaved sand aerated concrete slab reinforcement and preparation method

A technology for air-entrained concrete and concrete, applied in the field of rust inhibitor, can solve the problems of complex preparation process of rust inhibitor, poor bonding performance and high cost of raw materials, and achieve the effects of promoting sustainable development, low cost and protecting the environment

Active Publication Date: 2020-05-12
SHAANXI NITYA NEW MATERIALS TECH CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of antirust agent and preparation method for autoclaved sand aerated concrete slab reinforcement, which effectively solves the problem of complicated preparation process of antirust agent in the prior art, high cost of raw materials, and anticorrosion caused by antirust agent. The problem of poor bonding performance between layers and lightweight autoclaved sand aerated concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] A method for preparing an antirust agent for autoclaved sand aerated concrete slab reinforcement as described above, comprising the following steps:

[0027] (1) Each component is mixed according to the carboxylated styrene-butadiene latex 53%~57%, iron oxide red 1.2%~1.7%, slaked lime 8%~11%, high-efficiency thickener 3.2%~3.7%, quartz sand 18%~22 %, sand aerated concrete slab waste 5%~10%, tap water 3%~7% for batching;

[0028] (2) Component processing:

[0029] Slaked lime: put the quicklime in water for 2-3 days to make slaked lime;

[0030] Dilution of high-efficiency thickener: mix water: high-efficiency thickener: sodium hydroxide according to the ratio of 40:1.5:1 and stir evenly;

[0031] (3) Pour carboxylated styrene-butadiene latex and iron oxide red into the mixer, turn on the mixer and stir for 30s, then pour in slaked lime and stir for 30s; then pour in the diluted high-efficiency thickener and stir for 30s; then pour in quartz sand and stir for 300s ; ...

Embodiment 1

[0033] The components are mixed according to the ratio of 55% carboxylated styrene-butadiene latex, 1.4% iron oxide red, 10% slaked lime, 3.6% high-efficiency thickener, 20% quartz sand, 5% sand aerated concrete slab waste, and 5% tap water ; Among them, the model of carboxylated styrene-butadiene latex is PC-02, the model of iron oxide red is S130-3, the model of high-efficiency thickener is KP-E, the particle size of quartz sand is 0~1mm, and the waste of sand aerated concrete slabs The particle size is 0~2mm.

[0034] Component processing:

[0035] Slaked lime: put the quicklime in water for 2-3 days to make slaked lime;

[0036] Dilution of high-efficiency thickener: mix water: high-efficiency thickener: sodium hydroxide according to the ratio of 40:1.5:1 and stir evenly;

[0037] Pour carboxylated styrene-butadiene latex and iron oxide red into the mixer, turn on the mixer and stir for 30s, then pour in hydrated lime and stir for 30s; then pour in the diluted high-effic...

Embodiment 2

[0040] The components are mixed according to the ratio of 57% carboxylated styrene-butadiene latex, 1.5% iron oxide red, 10% slaked lime, 3.5% high-efficiency thickener, 20% quartz sand, 4% sand aerated concrete slab waste, and 4% tap water. ; Among them, the model of carboxylated styrene-butadiene latex is PC-02, the model of iron oxide red is S130-3, the model of high-efficiency thickener is KP-E, the particle size of quartz sand is 0~1mm, and the waste of sand aerated concrete slabs The particle size is 0~2mm.

[0041] Component processing:

[0042] Slaked lime: put the quicklime in water for 2-3 days to make slaked lime;

[0043] Dilution of high-efficiency thickener: mix water: high-efficiency thickener: sodium hydroxide according to the ratio of 40:1.5:1 and stir evenly;

[0044] Pour carboxylated styrene-butadiene latex and iron oxide red into the mixer, turn on the mixer and stir for 30s, then pour in hydrated lime and stir for 30s; then pour in the diluted high-effi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a rust inhibitor for a steel bar for an autoclaved sand aerated concrete board and a preparation method. The rust inhibitor is prepared from the following components in percentage by weight: 53 to 57 percent of carboxylic butadiene-styrene latex, 1.2 to 1.7 percent of iron oxide red, 8 to 11 percent of slaked lime, 3.2 to 3.7 percent of high-efficiency thickener, 18 to 22 percent of quartz sand, 5 to 10 percent of sand aerated concrete board waste material and 3 to 7 percent of tap water. Raw materials of the rust inhibitor provided by the invention are easily purchased, and the rust inhibitor has a low cost and a simple confecting process, can be abundantly confected once to be stored and used, has high adhesive force with the steel bar and is environmentally friendly and pollution-free.

Description

technical field [0001] The invention relates to an antirust agent, in particular to an antirust agent used for steel bars of autoclaved sand aerated concrete plates and a preparation method thereof. Background technique [0002] Lightweight autoclaved sand aerated concrete slab is a green and environmentally friendly new building material made of steel mesh cage as the skeleton and lime, cement, sand, aluminum powder and other materials through batching, pouring, static stopping, cutting, and autoclaving. A green building material vigorously developed by the country. The lightweight autoclaved sand aerated concrete product is a porous material. Oxygen, carbon dioxide, and moisture in the air can easily enter the plate and contact the steel mesh cage, which will cause corrosion of the steel bar and affect the stress of the plate and the entire structure. [0003] Antirust agent for steel bars is a necessary material for the coating of steel mesh cages in the production of li...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D113/02C09D5/08C09D7/61
CPCC08K3/36C08K2003/2206C08K2003/2272C09D5/08C09D113/02
Inventor 刘洋李军奇
Owner SHAANXI NITYA NEW MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com