Water-based inorganic environment-friendly coating and preparation method thereof

An environmentally friendly coating and inorganic technology, applied in the direction of anti-corrosion coatings, fire-resistant coatings, coatings, etc., can solve the problems of water-based coatings such as poor acid and alkali resistance, low corrosion resistance, etc., to achieve favorable environmental ecology, improve optical performance, and protect the ecological environment Effect

Inactive Publication Date: 2018-05-18
环秀(青岛)建材科技有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention proposes a water-based inorganic environmental protection coating and a preparation method thereof, which

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based inorganic environment-friendly coating and preparation method thereof
  • Water-based inorganic environment-friendly coating and preparation method thereof
  • Water-based inorganic environment-friendly coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of water-based inorganic environmental protection coating, comprises the raw material of following weight portion:

[0030] 10 parts of silica sol, 20 parts of vinyl acetate-vinyl tertiary carbonate emulsion, 4 parts of nano-silica powder, 3 parts of hydroxyethyl cellulose, 0.1 part of antifungal agent, 0.1 part of defoamer, 1 part of film-forming aid , The film-forming aid is a mixture of alcohol ester and propylene glycol in a weight ratio of 2:1, 1 part of sodium hexametaphosphate, 10 parts of calcined kaolin, 10 parts of heavy calcium carbonate, 10 parts of titanium dioxide, and 20 parts of deionized water.

[0031] A preparation method of water-based inorganic environmental protection paint, comprising the following steps:

[0032] Add 20 parts of deionized water, 1 part of sodium hexametaphosphate, and 10 parts of titanium dioxide into the dispersing kettle at a speed of 1000r / min, stir for 5 minutes, and then grind to a fineness of 40 microns. Add alcohol ...

Embodiment 2

[0034] A kind of water-based inorganic environmental protection coating, comprises the raw material of following weight portion:

[0035] 25 parts of silica sol, 30 parts of vinyl acetate-vinyl tertiary carbonate emulsion, 7 parts of nano-silica powder, 4 parts of hydroxyethyl cellulose, 0.3 parts of antifungal agent, 0.2 parts of defoamer, 2 parts of film-forming aid , The film-forming aid is a mixture of alcohol ester and propylene glycol in a weight ratio of 2:1, 6 parts of sodium hexametaphosphate, 20 parts of calcined kaolin, 30 parts of heavy calcium carbonate, 20 parts of titanium dioxide, and 35 parts of deionized water.

[0036] A preparation method of water-based inorganic environmental protection paint, comprising the following steps:

[0037] Add 35 parts of deionized water, 6 parts of sodium hexametaphosphate, and 20 parts of titanium dioxide into the dispersing kettle at a speed of 1000r / min, stir for 5min, and then grind to a fineness of 40 microns, add alcohol ...

Embodiment 3

[0039] A kind of water-based inorganic environmental protection coating, comprises the raw material of following weight portion:

[0040] 40 parts of silica sol, 40 parts of vinyl acetate-vinyl tertiary carbonate emulsion, 10 parts of nano-silica powder, 6 parts of hydroxyethyl cellulose, 0.5 parts of antifungal agent, 0.3 parts of defoaming agent, 3 parts of film-forming aid , The film-forming aid is a mixture of alcohol ester and propylene glycol in a weight ratio of 2:1, 10 parts of sodium hexametaphosphate, 30 parts of calcined kaolin, 50 parts of heavy calcium carbonate, 30 parts of titanium dioxide, and 40 parts of deionized water.

[0041] A preparation method of water-based inorganic environmental protection paint, comprising the following steps:

[0042] Add 40 parts of deionized water, 10 parts of sodium hexametaphosphate, and 30 parts of titanium dioxide into the dispersing kettle at a speed of 1000 r / min, stir for 5 minutes, and then grind to a fineness of 40 micro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention proposes a water-based inorganic environment-friendly coating and a preparation method thereof, which solve the problem that water-based coating in the prior art cannot resist acid and alkali and is low in corrosion resistance. The technical solution of the invention is implemented in the following way: the water-based inorganic environment-friendly coating is prepared from the following materials in parts by weight: 10 to 40 parts of silicasol, 20 to 40 parts of polymer emulsion, 4 to 10 parts of nano silicon dioxide powder, 3 to 6 parts of thickener, 0.1 to 0.5 part of mould inhibitor, 0.1 to 0.3 part of defoaming agent, 1 to 3 parts of film coalescing aid, 1 to 10 parts of dispersant, 10 to 30 parts of calcined kaolin, 10 to 50 parts of heavy calcium carbonate, 10 to 30 parts of pigment and 20 to 40 parts of deionized water. The compatibility between the additives chosen by the invention is better, the coating is odorless and smellless, the protection of ecological environments is benefited, the coating has the nature of inorganic matter, and does not contain any organic chemical material or solvent, and during production and application, the coating has the characteristics of no odor and no allergy, which are good for environment and ecology.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based inorganic environmental protection coating and a preparation method thereof. Background technique [0002] At present, water-based coatings have gradually been recognized and accepted by users due to their advantages of environmental protection, non-combustibility, and health, and are being widely used in fields such as flooring, construction, wood, concrete surface protection, and metal surface protection. [0003] According to the classification of film-forming substances, water-based coatings can be divided into inorganic, polyurethane, acrylic, epoxy, polyester and other types. Each water-based coating has its advantages and disadvantages. For conventional water-based coatings, there are defects such as poor solvent and chemical resistance, poor acid and alkali resistance and weather resistance, brittle and easy to crack, poor hardness and wear resistance, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D131/04C09D5/08C09D7/61C09D7/63C09D7/65
CPCC09D131/04C08K2003/2241C08K2003/265C08K2201/011C08K2201/014C09D5/08C09D5/18C08L1/284C08K13/02C08K3/36C08K5/053C08K3/32C08K3/346C08K3/26C08K3/22
Inventor 刘金德刘强
Owner 环秀(青岛)建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap