Processing method of water-proof carbonization wood board

A processing method and water-repellent technology, which is applied to wood processing equipment, wood treatment, impregnated wood, etc., can solve the problems of insufficient carbonization and high cost, and achieve the effects of improving waterproof performance, short time consumption, and strong cohesion

Active Publication Date: 2018-06-22
台州中知英健机械自动化有限公司
6 Cites 6 Cited by

AI-Extracted Technical Summary

Problems solved by technology

At present, the method of surface carbonization of wood boards is mainly to grill with an oxygen torch, so that the wood surface has a very thin layer of carbonization. The whole process requires people to carefully control the degree of carbonization to prevent excessive carbonization or insufficient carbonization.
In addition, the waterproof performance of the surface carbonized wood board also needs t...
View more

Abstract

The invention belongs to the field of wood, and discloses a processing method of a water-proof carbonization wood board. The processing method comprises the five steps of cutting and cleaning, drying,surface treating, carbonization and shaping. The invention provides a processing method of a water-proof carbonization wood board, less time is consumed, and the carbonization is even.

Application Domain

Wood treatment detailsCoating impregnation +3

Technology Topic

Surface finishingCarbonization +3

Image

  • Processing method of water-proof carbonization wood board
  • Processing method of water-proof carbonization wood board

Examples

  • Experimental program(4)
  • Comparison scheme(2)

Example Embodiment

[0023] Example 1
[0024] A processing method of waterproof carbonized wood board includes the following steps:
[0025] (1) Preparation of treatment solution: 1) Raw materials of treatment solution: 20 parts of EVA resin, 15 parts of rosin resin, 1 part of copper sulfate, 1.5 parts of ferrous sulfate, 2.5 parts of molybdenum oxide, 5 parts of nano titanium dioxide, 10 parts of polyethylene wax , 4 parts of diacetyl tartaric acid monoglyceride, 1 part of polyoxypropylene oxide ethylene glycerol ether and 100 parts of water;
[0026] 2) Preparation method of treatment solution: Dissolve 1 part of copper sulfate, 1.5 parts of ferrous sulfate and 2.5 parts of molybdenum oxide in 100 parts of water, mix well under stirring, and then add 4 parts of diacetyl tartrate monoglyceride and polyoxypropylene 1 part of oxyethylene glyceryl ether, make an emulsion, add the other components in sequence, and mix evenly to obtain;
[0027] (2) Cutting and cleaning: Cut the wood into 0.2m long and 2cm thick wooden boards, spray saturated lime water on the surface of the wooden boards, rinse them with water, and dry them naturally;
[0028] (3) Drying: transfer the dried wood board in step (2) to an oven or a drying room, and bake at 55°C until the water content of the wood board is less than 20%;
[0029] (4) Surface treatment: spray the treatment liquid evenly on the surface of the wood board prepared in step (3) to wet the wood board, and then dry it naturally;
[0030] (5) Carbonization: Place the wood board treated in step (4) in a closed high-temperature carbonization furnace, under the protection of nitrogen, slowly heat up to 300°C at a rate of 10°C/min per minute, and the continuous carbonization time is 60min. After cooling, burn the cooled wood board under the spray of oxygen torch for 30s;
[0031] (6) Shaping: Surface grinding and polishing of the wood board prepared in step (5).

Example Embodiment

[0032] Example 2
[0033] A processing method of waterproof carbonized wood board includes the following steps:
[0034] (1) Preparation of treatment solution: 1) Raw materials of treatment solution: 25 parts of EVA resin, 20 parts of rosin resin, 1.6 parts of copper sulfate, 2.4 parts of ferrous sulfate, 4 parts of molybdenum oxide, 8 parts of nano titanium dioxide, 12 parts of polyethylene wax , 5 parts of diacetyl tartaric acid monoglyceride, 2 parts of polyoxypropylene oxide ethylene glycerol ether and 105 parts of water;
[0035] 2) The preparation method of the treatment solution: dissolve 1.6 parts of copper sulfate, 2.4 parts of ferrous sulfate and 4 parts of molybdenum oxide in 105 parts of water, mix well under stirring, and then add 5 parts of diacetyl tartrate monoglyceride and polyoxypropylene 2 parts of oxyethylene glycerol ether, make emulsion, add other components in sequence, mix evenly, and get;
[0036] (2) Cutting and cleaning: Cut the wood into 0.5m long and 4cm thick wooden boards, spray saturated lime water on the surface of the wooden boards, rinse them with water, and dry them naturally;
[0037] (3) Drying: transfer the dried wood board in step (2) into an oven or a drying room, and bake at 60°C until the water content of the wood board is less than 20%;
[0038] (4) Surface treatment: spray the treatment liquid evenly on the surface of the wood board prepared in step (3) to wet the wood board, and then dry it naturally;
[0039] (5) Carbonization: Place the wood board treated in step (4) in a closed high-temperature carbonization furnace, under the protection of nitrogen, slowly heat up to 350°C at a rate of 10°C/min per minute. The continuous carbonization time is 50 minutes. After cooling, burn the cooled wood board under the spray of an oxygen torch for 35s;
[0040] (6) Shaping: Surface grinding and polishing of the wood board prepared in step (5).

Example Embodiment

[0041] Example 3
[0042] A processing method of waterproof carbonized wood board includes the following steps:
[0043] (1) Preparation of treatment solution: 1) Raw materials of treatment solution: 30 parts of EVA resin, 25 parts of rosin resin, 1.6 parts of copper sulfate, 2.4 parts of ferrous sulfate, 4 parts of molybdenum oxide, 12 parts of nano titanium dioxide, 16 parts of polyethylene wax , 5 parts of diacetyl tartaric acid monoglyceride, 2.5 parts of polyoxypropylene oxide ethylene glyceryl ether and 112 parts of water;
[0044] 2) The preparation method of the treatment solution: Dissolve 1.6 parts of copper sulfate, 2.4 parts of ferrous sulfate and 4 parts of molybdenum oxide in 112 parts of water, mix well under stirring, and then add 5 parts of diacetyl tartrate monoglyceride and polyoxypropylene 2.5 parts of oxyethylene glyceryl ether, make an emulsion, add the other components in sequence, mix evenly, and get it;
[0045] (2) Cutting and cleaning: Cut the wood into 0.8m long and 8cm thick wooden boards, spray saturated lime water on the surface of the wooden boards, rinse them with water, and dry them naturally;
[0046] (3) Drying: transfer the wooden boards dried in step (2) into an oven or drying room, and bake them at 65°C until the moisture content of the wooden boards is less than 20%;
[0047] (4) Surface treatment: spray the treatment liquid evenly on the surface of the wood board prepared in step (3) to wet the wood board, and then dry it naturally;
[0048] (5) Carbonization: Place the wood board treated in step (4) in a closed high-temperature carbonization furnace, under the protection of nitrogen, slowly heat up to 400°C at a rate of 10°C/min per minute. The continuous carbonization time is 45 minutes. After cooling, burn the cooled wood board under the spray of oxygen torch for 40s;
[0049] (6) Shaping: The wood board prepared in step (5) is subjected to surface grinding and polishing.

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.

Similar technology patents

Building block lap joint structure

InactiveCN107638706ASimple structurestrong connection
Owner:黄芳

Three-dimensional enclosure bulkhead member coupling type paper box

InactiveCN114194561AIncreased stability and efficiency of installation and removalStrong connection
Owner:湖南圣芯超能环保科技有限公司

Automobile seat cover convenient to disassemble and assemble

InactiveCN111409524AStrong connectioneasy to operate
Owner:广州勒高汽车科技有限公司

Connecting structure for display and display bracket

PendingCN108458223Acompact structureStrong connection
Owner:LOCTEK ERGONOMIC TECH CORP

Classification and recommendation of technical efficacy words

  • short time
  • strong connection

Heavy oil upgrading process (LAW813)

InactiveUS6171471B1short time
Owner:EXXON RES & ENG CO

Step scan photo-etching machine double-platform exchanging and positioning system

ActiveCN1828427Ashort timeThe exchange process is simple
Owner:SHANGHAI MICRO ELECTRONICS EQUIP (GRP) CO LTD

No-tools breakdown furniture

InactiveUS20090284111A1quickly and easily assemble and disassembleshort time
Owner:HAZZARD THOMAS B +1

Sealed small low-impact release screw bolt

InactiveCN101875404Areduce shockstrong connection
Owner:BEIJING INSTITUTE OF TECHNOLOGYGY

Ovalized concrete block-out tube with tear away nailing flange

ActiveUS20050044809A1high pullout strengthstrong connection
Owner:THOMPSON HARRY A

Connector for coaxial cable and method

InactiveUS20080020637A1strong connection
Owner:JOHN MEZZALINGUA ASSOC INC

Automobile safety chair for child

ActiveCN105857131AThe connection structure is firm and reliablestrong connection
Owner:NINGBO BOLENN MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products