Water-based paint and preparing method thereof

A water-based paint, water-soluble technology, applied in the direction of anti-corrosion paint, coating, etc., can solve the problems of difficult to meet the requirements of shipyard painting, low painting cost, long time, etc., to achieve excellent physical and chemical rust prevention, simple preparation method, The effect of enhancing the binding force

Inactive Publication Date: 2018-07-17
WUHU WEINAN SHIPBUILDING CO LTD
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Large-scale steel installations and facilities, such as oil storage tanks, iron frames, iron bridges, sluice gates, ships, etc., can only be derusted by hand, which is not only labor-intensive and inefficient, but also difficult to remove rust
Small and medium-sized steel parts can be derusted by shot blasting. Although the derusting effect is good, it is subject to various restrictions due to large dust, loud noise, serious environmental pollution and high labor costs.
With the development of industry, there are more and more projects such as steel bridges and large pipelines. The above rust removal methods are far from meeting the needs of the project. Therefore, it is necessary to develop a coating that can directly paint the surface of corroded steel.
[0003] The application number is 201410165201.7, which discloses a water-based antirust coating with rust and its preparation method, which consists of styrene-acrylic emulsion, water-soluble epoxy resin, water-soluble acrylic resin, iron oxide red, graphene, zinc oxide, barium sulfate, and conversion , conversion accelerator, leveling agent, defoamer, dispersant, thickener and water, the coating does not contain organic solvents, is environmentally friendly, non-polluting, has the characteristics of the bottom surface and excellent physical and chemical resistance The functions of rust and rust conversion are not only suitable for rust prevention on steel surfaces with rust, hard oxide skin or old paint film, but also suitable for rust prevention on rust-free steel surfaces. The preparation method is simple and the construction is convenient. The compounding of the agent enhances the binding force between the paint and the rust, and it can be directly painted on the rusty steel surface. It is suitable for various construction methods such as spraying, brushing and showering. The coating cost is low and can fully meet the needs of urban road facilities. , bridges, oil and gas pipelines, construction machinery equipment and ships, etc., but the surface dry time of this invention is 1.5 hours, and the actual dry time is within 24 hours, which is too long to meet the shipyard's painting use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Below in conjunction with embodiment the present invention is described in further detail:

[0014] The water-based anti-rust paint with rust is characterized in that its formula consists of the following components in terms of mass percentage: 15%-25% of styrene-acrylic emulsion, 5%-10% of water-soluble epoxy resin, and 1%-10% of water-soluble acrylic resin. 5%, iron oxide red 1%~5%, graphene 0%~5%, zinc oxide 1%~2%, barium sulfate 20%~30%, conversion agent 1%~1.5%, conversion accelerator 0.5%~ 1%, leveling agent 0.05% ~ 0.20%, defoamer 0.05% ~ 0.20%, dispersant 0.1% ~ 0.3%, thickener 1% ~ 2%, ethanol 3% ~ 5%, the balance is water;

[0015] The conversion agent is a mixture of any two of salicylic acid, gallic acid, tea polyphenols, tannic acid, ascorbic acid and oxalic acid; the conversion accelerator is phloroglucinol or pyrocatechol; The agent is polyacrylate; the defoamer is tributyl phosphate or water-based silicone oil; the dispersant is unsaturated polyaminoami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of paint, and relates to water-based paint and a preparing method thereof. The water-based paint is prepared from a styrene-acrylic emulsion, water-soluble epoxy resin, water-soluble acrylic resin, iron oxide red, graphene, zinc oxide, barium sulfate, a transforming agent, a transformation accelerant, a flatting agent, a defoaming agent, a dispersing agent, a thickening agent and water. The paint does not contain an organic solvent, is friendly to the environment and free of pollution and has a bottom face integration characteristic and excellent physiochemical rust prevention and rust transformation functions, and finally the surface drying and hard drying time can be effectively shortened by adding ethyl alcohol.

Description

technical field [0001] The invention belongs to the field of coatings, and relates to a water-based coating and a preparation method thereof. Background technique [0002] Steel structure engineering is a structure mainly made of steel, which is one of the main types of modern industrial and architectural structures, but its easy to corrode characteristics have brought huge losses to the national economy. In order to protect steel from rust, a layer of paint is often applied to its surface. In the past, before using paint, the base material must be thoroughly derusted, and even the original color of the metal base must be exposed. Large-scale steel installations and facilities, such as oil storage tanks, iron frames, iron bridges, sluice gates, ships, etc., often can only be derusted by hand, which is not only labor-intensive and inefficient, but also difficult to remove rust. Small and medium-sized steel parts can be derusted by shot peening. Although the derusting effect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/08C09D7/20C09D7/61C09D7/63
CPCC09D125/14C08K2003/2272C08K2003/2296C08K2003/3045C08K2201/014C08L2205/035C09D5/08C08L63/00C08L33/04C08K13/02C08K3/22C08K3/04C08K3/30C08K5/13C08K5/1545C08K5/1535C08K5/092
Inventor 查俊强林汉陆青松
Owner WUHU WEINAN SHIPBUILDING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products