Antirust and anticorrosive fitness equipment primer and preparation method thereof

A fitness equipment and anti-corrosion technology, which is applied in the direction of anti-corrosion coatings, coatings, epoxy resin coatings, etc., can solve the problems of not being able to play a good role in anti-rust, greater harm to operators, and difficulty in removing greasy, etc., to achieve good Rust removal effect, good water removal effect, good anti-rust and anti-corrosion effect

Active Publication Date: 2018-07-20
SHAOXING HENG YUAN MACHINERY MFG CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current anti-rust paint includes two kinds of oily anti-rust primer and water-based anti-rust paint. The oily anti-rust primer makes it difficult to remove the greasy surface of the material. Although the price is low, it contains toxic substances such as nitrite and chromium nitrate. The danger to the operator is greater; while the water-based anti-rust primer is mainly composed of a metal chelating agent with good effect and a water-based additive. Since the two are only a simple physical mixture, the matching is poor, and the paint is easy to separate after being placed. layer, the paint film is easy to be uneven when spraying, and cannot play a good role in antirust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antirust and anticorrosive fitness equipment primer and preparation method thereof
  • Antirust and anticorrosive fitness equipment primer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of antirust and anticorrosion fitness equipment primer, this antirust and anticorrosion fitness equipment primer comprises A component and B component, and wherein A component comprises following material: modified epoxy resin 45kg, polyvinyl alcohol 0.1 kg, sorbitan monooleate 2kg, fatty acid glycerides 2kg, tricresyl phosphate 5kg, triethanolamine 10kg, xylene 30kg and bentonite 1kg;

[0035] The B component includes the following materials: polyurethane prepolymer 25kg, didecyl phthalate 10kg, dewatering agent 5kg, titanium dioxide 5kg, silane coupling agent A-187 0.5kg and stannous octoate 0.1kg;

[0036] Described modified epoxy resin obtains according to the following steps:

[0037] ①Put 50kg of bisphenol A and 100kg of epichlorohydrin in the reactor, mix them evenly, raise the temperature of the system to 50°C, then add 20kg of 30% sodium hydroxide aqueous solution to the reactor dropwise, and the reaction time is 2 hours. After the reaction was complete...

Embodiment 2

[0042] A kind of anti-rust and anti-corrosion fitness equipment primer, including A component and B component, wherein A component includes the following materials: modified epoxy resin 55kg, polyvinyl alcohol 0.5kg, sorbitan monooleate 6kg , fatty acid glyceride 5kg, tricresyl phosphate 10kg, triethanolamine 15kg, xylene 40kg and bentonite 2kg;

[0043] The B component includes the following materials: 40kg of polyurethane prepolymer, 25kg of didecyl phthalate, 10kg of dewatering agent, 10kg of titanium dioxide, 1kg of silane coupling agent A-187 and 1kg of stannous octoate;

[0044] Described modified epoxy resin obtains according to the following steps:

[0045] ①Put 55kg of bisphenol A and 125kg of epichlorohydrin in the reactor, mix well, raise the temperature of the system to 60°C, then add 30kg of 40% sodium hydroxide aqueous solution to the reactor dropwise, and the reaction time is 3h , after the completion of the reaction, add 60kg water and 30kg toluene therein, le...

Embodiment 3

[0050] A kind of anti-rust and anti-corrosion fitness equipment primer, including A component and B component, wherein A component includes the following materials: modified epoxy resin 48kg, polyvinyl alcohol 0.2kg, sorbitan monooleate 3kg , fatty acid glyceride 4kg, tricresyl phosphate 6kg, triethanolamine 12kg, xylene 32kg and bentonite 1.2kg;

[0051] The B component includes the following materials: polyurethane prepolymer 28kg, didecyl phthalate 16kg, dewatering agent 6kg, titanium dioxide 8kg, silane coupling agent A-187 0.6kg and stannous octoate 0.2kg;

[0052] Described modified epoxy resin obtains according to the following steps:

[0053] ①Put 51kg of bisphenol A and 110kg of epichlorohydrin in the reactor, mix well, raise the temperature of the system to 52°C, then add 23kg of 32% sodium hydroxide aqueous solution to the reactor dropwise, and the reaction time is 2.5 h, after the reaction was completed, add 54kg water and 27kg toluene therein, leave standstill an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antirust and anticorrosive fitness equipment primer and a preparation method thereof. The antirust and anticorrosive fitness equipment primer comprises a component A and a component B, wherein the component A includes the following materials: modified epoxy resin, polyvinyl alcohol, sorbitan monooleate, fatty glyceride, tricresyl phosphate, triethanolamine, xylene and bentonite; and the component B includes the following materials: a polyurethane prepolymer, didecyl phthalate, a water removal agent, titanium dioxide, a silane coupling agent A-187 and stannous octoate. The antirust paint provided by the invention is obtained by mixing the component A and the component B, the two components are used cooperatively to achieve a good antirust and anticorrosive effect,also the adhesion is strong, which is determined by the proportion of the components, specifically, cooperative use of all the assistants in the component A not only has good compatibility, but alsocan generate a synergistic superposition of antirust function, the film-forming time is short, the formed film is firmly adsorbed, and in a room temperature environment, water vapor does not seep intometal surfaces, therefore the primer has a good rust removal effect.

Description

technical field [0001] The invention relates to the technical field, in particular to an antirust and anticorrosion primer for fitness equipment and a preparation method thereof. Background technique [0002] The rust problem of fitness equipment has attracted more and more people's attention. Applying paint on fitness equipment can not only achieve the purpose of rust prevention, but also be more beautiful and give people visual enjoyment. However, the current antirust paint has poor adhesion and is very It is easy to crack or peel, has poor mechanical properties, short anti-rust time, and poor anti-corrosion performance, which cannot meet people's needs. Because fitness equipment must not only have an aesthetic effect but also be wear-resistant, especially outdoor fitness equipment that is exposed to the sun, wind and sun, and because the environmental pollution is becoming more and more serious, the fitness equipment with good performance in anti-rust and anti-corrosion ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D175/08C09D129/04C09D5/10C09D7/61C09D7/63
CPCC08K2003/2241C08L2205/025C08L2205/035C09D5/103C09D163/00C08L75/08C08L29/04C08K13/02C08K3/22C08K3/346C08K5/103C08K5/523C08K5/12
Inventor 李保才
Owner SHAOXING HENG YUAN MACHINERY MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap