Thermal insulation board special for building and preparation method thereof

A technology for thermal insulation and board, applied in thermal insulation, building components and other directions, can solve the problems of high water absorption, reduced thermal insulation performance of thermal insulation materials, flammability, etc., to achieve good thermal insulation effect, improve thermal insulation performance, and improve fire performance. Effect

Inactive Publication Date: 2018-07-31
合肥天沃能源科技有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Thermal insulation is the most important energy-saving measure in building energy conservation. At present, there are many types of thermal insulation materials in my country, but there are generally problems of high water absorption, poor durability or flammability, and poor fire resistance. The former greatly reduces the thermal insulation performance of thermal insulation materials. It affects the effect of thermal insulation and increases the energy consumption of the air conditioning system, which will pose a threat to human life and safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment relates to a thermal insulation board for buildings, including the following raw materials in parts by weight: 20 parts of polyurethane, 10 parts of expandable polystyrene, 15 parts of fly ash, 8 parts of modified bentonite, expanded vitrified micro 12 parts of beads, 6 parts of dispersible latex powder, 2 parts of polypropylene fiber, 1 part of cloth fiber, 2 parts of sodium carboxymethyl cellulose, 1 part of waterproofing agent, and 1 part of flame retardant.

[0028] Wherein, the preparation method of described modified bentonite is as follows:

[0029] (1) In parts by weight, weigh 100 parts of bentonite powder, 40 parts of nano-calcium oxide, 25 parts of nano-calcium carbonate, 7 parts of epoxy resin, and 15 parts of phenolic resin;

[0030] (2) Mix bentonite powder, nano-calcium oxide and nano-calcium carbonate to obtain a mixture;

[0031] (3) Add epoxy resin and phenolic resin to the mixture obtained in step (2) to obtain the modified bentonite....

Embodiment 2

[0042] This embodiment relates to a special thermal insulation board for buildings, including the following raw materials in parts by weight: 30 parts of polyurethane, 20 parts of expandable polystyrene, 30 parts of fly ash, 19 parts of modified bentonite, expanded vitrified micro 27 parts of beads, 11 parts of dispersible latex powder, 4 parts of polypropylene fiber, 3 parts of cloth fiber, 3 parts of sodium carboxymethyl cellulose, 2 parts of waterproofing agent, and 3 parts of flame retardant.

[0043] Wherein, the preparation method of described modified bentonite is as follows:

[0044] (1) In parts by weight, weigh 100 parts of bentonite powder, 40 parts of nano-calcium oxide, 25 parts of nano-calcium carbonate, 7 parts of epoxy resin, and 15 parts of phenolic resin;

[0045] (2) Mix bentonite powder, nano-calcium oxide and nano-calcium carbonate to obtain a mixture;

[0046] (3) Add epoxy resin and phenolic resin to the mixture obtained in step (2) to obtain the modifi...

Embodiment 3

[0057] This embodiment relates to a thermal insulation board for buildings, including the following raw materials in parts by weight: 24 parts of polyurethane, 11 parts of expandable polystyrene, 20 parts of fly ash, 10 parts of modified bentonite, expanded vitrified micro 15 parts of beads, 8 parts of dispersible latex powder, 2.5 parts of polypropylene fiber, 1.7 parts of cloth fiber, 2.3 parts of sodium carboxymethyl cellulose, 1.1 parts of waterproofing agent, and 1.5 parts of flame retardant.

[0058] Wherein, the preparation method of described modified bentonite is as follows:

[0059] (1) In parts by weight, weigh 100 parts of bentonite powder, 40 parts of nano-calcium oxide, 25 parts of nano-calcium carbonate, 7 parts of epoxy resin, and 15 parts of phenolic resin;

[0060] (2) Mix bentonite powder, nano-calcium oxide and nano-calcium carbonate to obtain a mixture;

[0061] (3) Add epoxy resin and phenolic resin to the mixture obtained in step (2) to obtain the modif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a thermal insulation board special for a building. The thermal insulation board comprises the following raw materials in parts by weight: 20-30 parts of polyurethane, 10-20 parts of foamable polystyrene, 15-30 parts of fly ash, 8-19 parts of modified bentonite, 12-27 parts of expanded vitrified microbeads, 6-11 parts of dispersible latex powder, 2-4 parts of polypropylene fiber, 1-3 parts of cloth fiber, 2-3 parts of sodium carboxymethyl cellulose, 1-2 parts of a waterproof agent and 1-3 parts of a flame retardant. According to the thermal insulation board special for the building, by controlling the types of raw materials and the proportions of the raw materials, the prepared product has the advantages of low water absorption, good durability, good thermal insulation effect, good fire resistance and no threat to human life and safety.

Description

technical field [0001] The invention belongs to the technical field of energy-saving products, and in particular relates to a special thermal insulation board for buildings and a preparation method thereof. Background technique [0002] Thermal insulation is the most important energy-saving measure in building energy conservation. At present, there are many types of thermal insulation materials in my country, but there are generally problems of high water absorption, poor durability or flammability, and poor fire resistance. The former greatly reduces the thermal insulation performance of thermal insulation materials. It affects the effect of thermal insulation and increases the energy consumption of the air conditioning system, which will pose a threat to human life and safety. Contents of the invention [0003] The invention provides a thermal insulation board for building and its preparation method, which solves the problems in the background technology. The thermal insu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L75/04C08L25/06C08L23/12C08L1/28C08L61/06C08L63/00C08K13/04C08K3/34C08K3/22C08K3/26C08K7/26C08K7/18C08K5/17C08K3/30C08J9/22E04B1/80
CPCC08J9/0028C08J9/0042C08J9/0061C08J9/0066C08J9/008C08J9/0085C08J9/228C08J2375/04C08J2425/06C08K3/22C08K3/26C08K3/30C08K3/34C08K5/17C08K7/18C08K7/26C08K13/02E04B1/80
Inventor 魏芳芳
Owner 合肥天沃能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com