Silk fibroin based antibacterial nano-fibers and preparation method thereof

A technology of silk fibroin and nanofibers, which is applied in the fields of fiber chemical characteristics, single-component protein rayon, textiles and papermaking, etc., can solve the problems of high processing cost and complicated preparation process, and achieve the improvement of color fixing performance and adsorption function, the effect of improving stability

Inactive Publication Date: 2018-08-10
HAIYAN SHUOCHUANG CLOTHING RES INST
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the research on antibacterial materials is mostly reported on antibacterial materials containing nano-silver or sil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silk fibroin based antibacterial nano-fibers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1:

[0020] The silk fibroin-based antibacterial nanofibers are composed of the following components and parts by weight: 120 parts of silk fibroin, 6 parts of titanium dioxide, 24 parts of chitosan, 13 parts of nano-copper oxide, 11 parts of polyethylene oxide, and the particle size of nano-copper oxide It is 600nm.

[0021] The preparation method of silk fibroin-based antibacterial nanofibers includes the following steps:

[0022] 1) Preparation of silk fibroin film: silk fibroin fiber is obtained by degumming and drying. The silk fibroin fiber is processed. The processing of silk fibroin fiber includes the process of dissolving, drying, washing, and then drying. The solvent used in the dissolution process is selected from An acid / salt mixture with a mass ratio of acid: salt of 15:85. The acid is formic acid solution; the salt is octacalcium phosphate, and the nano cuprous oxide solution is stirred and dissolved to prepare a silk fibroin film. The preparation steps...

Example Embodiment

[0025] Example 2:

[0026] Silk fibroin-based antibacterial nanofibers are composed of the following components and preferred parts by weight: 140 parts of silk fibroin, 6 parts of titanium dioxide, 24 parts of chitosan, 11 parts of nano-copper oxide, 12 parts of polyethylene oxide, and particles of nano-copper oxide The diameter is 450nm.

[0027] The preparation method of silk fibroin-based antibacterial nanofibers includes the following steps:

[0028] 1) Preparation of silk fibroin film: silk fibroin fiber is obtained by degumming and drying. The silk fibroin fiber is processed. The processing of silk fibroin fiber includes the process of dissolving, drying, washing and re-drying, and the solvent used in the dissolving process is selected from An acid / salt mixture with a mass ratio of acid: salt of 95:5, the acid is a mixture of formic acid and phosphoric acid; the salt is calcium chloride, and the nano cuprous oxide solution is stirred and dissolved to prepare a silk fibroin fi...

Example Embodiment

[0031] Example 3:

[0032] Silk fibroin-based antibacterial nanofibers are composed of the following components and parts by weight: 110 parts of silk fibroin, 6 parts of titanium dioxide, 27 parts of chitosan, 14 parts of nano copper oxide, 12 parts of polyethylene oxide, and the particle size of nano copper oxide It is 1000nm.

[0033] The preparation method of silk fibroin-based antibacterial nanofibers includes the following steps:

[0034] 1) Preparation of silk fibroin film: silk fibroin fiber is obtained by degumming and drying. The silk fibroin fiber is processed. The processing of silk fibroin fiber includes the process of dissolving, drying, washing, and then drying. The solvent used in the dissolution process is selected from The acid / salt mixture with a mass ratio of acid: salt of 20:80, the acid is phosphoric acid solution; the salt is calcium hydroxide, and the nano cuprous oxide solution is added to stir and dissolve to prepare silk fibroin film, nano cuprous oxide so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides silk fibroin based antibacterial nano-fibers. The silk fibroin based antibacterial nano-fibers are prepared from the following components in parts by weight: 100 to 150 parts ofsilk fibroin, 4 to 8 parts of titanium dioxide, 20 to 30 parts of chitosan, 10 to 15 parts of nano copper oxide and 10 to 15 parts of polyethylene oxide. The invention further provides a preparationmethod of the silk fibroin based antibacterial nano-fibers; the silk fibroin based antibacterial nano-fibers, prepared by the preparation method, have good biocompatibility, anti-sticking performance,good antibacterial effect and excellent color fixing effect.

Description

technical field [0001] The invention belongs to the technical field of antibacterial fiber preparation, and in particular relates to a silk fibroin-based antibacterial nanofiber and a preparation method thereof. Background technique [0002] Nano antibacterial material is a new type of material with antibacterial properties. Due to the special effect of high specific surface area and high reactivity of the antibacterial agent in the material, the overall antibacterial effect is greatly improved, and it can make microorganisms including bacteria, fungi, yeast, Growth and reproduction of algae, viruses etc. are kept at a low level. Various products made of antibacterial materials have hygienic and self-cleaning functions, which can effectively prevent the spread of bacteria and strengthen the mechanical properties of antibacterial materials. Nano antibacterial products can not only effectively prevent people from people, people from things, things Bacterial cross-infection wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F4/00D01F1/10
CPCD01F1/10D01F1/103D01F4/00
Inventor 王硕
Owner HAIYAN SHUOCHUANG CLOTHING RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap