A kind of ultra-high performance fiber concrete and preparation method thereof

A fiber reinforced concrete, ultra-high performance technology, applied in climate sustainability, sustainable waste treatment, solid waste management, etc., can solve the problems of poor compactness and homogeneity, poor brittleness, etc., achieve good fluidity, increase toughness and ductility, the effect of improving workability

Active Publication Date: 2021-05-11
陕西建研结构工程股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, ultra-high performance fiber concrete is mostly composed of cement, gravel, sand, water and water reducing agent, which has poor compactness and homogeneity, and the interior of the concrete contains large pores and poor brittleness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-high performance fiber concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of ultra-high-performance fiber concrete of this embodiment is composed of P.O.52.5R Portland cement, silica fume, sand, steel fiber, polypropylene fiber, early-strength polycarboxylate high-efficiency water reducer, silicone defoamer and Composition of water; the loss on ignition of the silica fume is 6%, and the specific surface area of ​​the silica fume is 16000m 2 / kg, the mass content of silicon dioxide in the silica fume is 92%, the particle diameter of the sand is 0.85mm~2mm, and the mass ratio of the P.O.52.5R Portland cement, silica fume, sand and water is 1: 0.24:1.25:0.2, the water reducing rate of the early-strength polycarboxylate superplasticizer is 35%, and the dosage of the early-strength polycarboxylate superplasticizer is P.O.52.5R Portland cement and silica fume 2.38% of the total mass, the dosage of the organosilicon defoamer is 0.137% of the total mass of P.O.52.5R Portland cement and silica fume, the steel fiber is Shanghai Zhenqiang brand s...

Embodiment 2

[0023] A kind of ultra-high-performance fiber concrete of this embodiment is composed of P.O.52.5R Portland cement, silica fume, sand, steel fiber, polypropylene fiber, early-strength polycarboxylate high-efficiency water reducer, silicone defoamer and Composition of water; the loss on ignition of the silica fume is 5%, and the specific surface area of ​​the silica fume is 19000m 2 / kg, the mass content of silicon dioxide in the silica fume is 95%, the particle diameter of the sand is 0.85mm~2mm, and the mass ratio of the P.O.52.5R Portland cement, silica fume, sand and water is 1: 0.21:1.26:0.22, the water reducing rate of the early-strength polycarboxylate superplasticizer is 40%, and the dosage of the early-strength polycarboxylate superplasticizer is P.O.52.5R Portland cement and silica fume 2.35% of the total mass, the dosage of the organosilicon defoamer is 0.12% of the total mass of P.O.52.5R portland cement and silica fume, the steel fiber is Sichuan Sanhe brand steel ...

Embodiment 3

[0026] A kind of ultra-high-performance fiber concrete of this embodiment is composed of P.O.52.5R Portland cement, silica fume, sand, steel fiber, polypropylene fiber, early-strength polycarboxylate high-efficiency water reducer, silicone defoamer and Composition of water; the loss on ignition of the silica fume is 7%, and the specific surface area of ​​the silica fume is 19000m 2 / kg, the mass content of silica in silica fume is 94%, the particle diameter of described sand is 0.85mm~2mm, and the mass ratio of described P.O.52.5R Portland cement, silica fume, sand and water is 1: 0.22:1.27:0.24, the water reducing rate of the early-strength polycarboxylate superplasticizer is 33%, and the dosage of the early-strength polycarboxylate superplasticizer is P.O.52.5R portland cement and silica fume 2.35% of the total mass, the dosage of the organosilicon defoamer is 0.12% of the total mass of P.O.52.5R Portland cement and silica fume, and the steel fiber is the steel fiber produce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultra-high-performance fiber concrete, which is composed of cement, silica fume, sand, steel fiber, polypropylene fiber, polycarboxylate high-efficiency water reducer, organic silicon defoamer and water. The silica fume in the concrete component of the present invention improves the compactness and homogeneity of the concrete, and the sand plays the role of filling and skeleton, can effectively transmit stress and support the load, and at the same time inhibit the shrinkage and cracking of the concrete, and the steel fiber inhibits and constrains It prevents the formation and development of concrete micro-cracks and increases the toughness and ductility of concrete. The invention also discloses a preparation method of concrete. After mixing cement, silica fume, polypropylene fiber and sand evenly, adding polycarboxylate high-efficiency water reducer, organic silicon defoamer and water with a total mass of 90% Stir evenly, then add steel fibers and stir evenly, and finally add the remaining 10% of water and stir evenly. This method is reasonable in process, simple and efficient.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, and in particular relates to an ultra-high performance fiber concrete and a preparation method thereof. Background technique [0002] Ultra-high-performance fiber-reinforced concrete plays a role in improving the compressive strength and improving durability in the reinforcement of concrete structures. Ultra-high performance fiber reinforced concrete has strong deformation ability and strong bonding performance with other concrete structural components, which plays a vital role in improving the seismic performance of concrete structural components. At present, ultra-high-performance fiber-reinforced concrete is mostly composed of cement, gravel, sand, water and water-reducing agent, which has poor compactness and homogeneity, and the interior of the concrete contains large pores and poor brittleness. Contents of the invention [0003] The technical problem to be solved by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B18/14C04B14/48C04B16/06
CPCC04B14/48C04B16/0633C04B18/146C04B28/04C04B2201/50C04B14/06C04B24/24C04B24/42C04B22/002Y02W30/91
Inventor 梁兴文于婧李林高宗祺胡翱翔景晓辉张涛常亚峰皇垚华尹文哲
Owner 陕西建研结构工程股份有限公司