Method for preparation of high polymer material/graphene nanocomposite material by continuous mixing in-situ reduction and application thereof

A technology of nanocomposite materials and polymer materials, which is applied in the field of polymer materials/graphene nanocomposite materials and their preparation, can solve the problem that the continuous preparation of nanocomposite materials cannot be realized, it is difficult to achieve good exfoliation and dispersion of RGO, and the degree of reduction of RGO can be solved. limited and other problems, to achieve the effect of easy promotion, avoiding unfriendly environment, and simple and easy operation.

Active Publication Date: 2018-08-21
SOUTH CHINA UNIV OF TECH
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(1) It is difficult to achieve good exfoliation and dispersion of RGO in the polymer matrix; (2) The degree of reduction of RGO in the obtained polymer material / RGO nanocomposite is limited; (3) It is impossible to realize the continuous preparation of nanocomposites; (4) Most of the reducing agents used have certain toxicity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparation of high polymer material/graphene nanocomposite material by continuous mixing in-situ reduction and application thereof
  • Method for preparation of high polymer material/graphene nanocomposite material by continuous mixing in-situ reduction and application thereof
  • Method for preparation of high polymer material/graphene nanocomposite material by continuous mixing in-situ reduction and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The water-assisted melting mixing extrusion equipment adopted in the present invention comprises an extruder, a set of water injection device, and a water ring vacuum pump. Along the flow direction of the material, the barrel of the extruder is provided with a feeding port, a water injection port and an exhaust port. The feeding port is used for the feeding of polymer materials, the water injection port is used for the injection of graphene oxide suspension, and the exhaust port is used for the discharge of water vapor. The water injection port is equipped with a nozzle, and the nozzle is connected with a water injection device, and the water injection device includes a liquid storage cylinder and a metering pump. The exhaust port is connected to a water ring vacuum pump.

[0034] Take a certain amount of GO powder and add it into deionized water for 2 h to prepare a GO suspension with a concentration of 15.2 g / L, which is placed in a liquid storage tank; start the ext...

Embodiment 2

[0036] In this example, the water-assisted melt kneading and extrusion equipment of Example 1 was used, and the method of Example 1 was used to prepare the GO suspension.

[0037] Add polystyrene (PS) pellets into the extruder from the feeding port, and when the melt pressure in the water injection section of the extruder reaches above 2MPa, inject a certain concentration of GO suspension into the PS melt at a certain flow rate , GO was exfoliated, dispersed and in-situ thermally reduced during the mixing and extrusion process, and PS / RGO nanocomposites with GO being better exfoliated and dispersed and in-situ thermally reduced were obtained by extruding at the outlet of the machine head. The screw speed of the extruder is 120r / min, the barrel temperature is 150-190°C, and the pressure of the water injection section is 5-6MPa.

[0038] The parts not mentioned are the same as in Example 1.

Embodiment 3

[0040] In this example, the water-assisted melt kneading and extrusion equipment of Example 1 was used, and the method of Example 1 was used to prepare the GO suspension.

[0041] Mix PS and PVDF pellets evenly according to a certain ratio and then add them into the extruder from the feeding port. When the melt pressure in the water injection section of the extruder reaches above 3MPa, inject a certain concentration of GO suspension into the extruder at a certain flow rate. In the PS / PVDF blend melt, GO was exfoliated, dispersed and in-situ thermally reduced during the mixing and extrusion process, and extruded at the outlet of the die, the GO was better exfoliated and dispersed and in-situ thermally reduced PS / PVDF / RGO blend nanocomposites. The screw speed of the extruder is 100r / min, the barrel temperature is 160-200°C, and the pressure of the water injection section is 4-5MPa.

[0042] The parts not mentioned are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Relating to the field of polymer material / graphene nanocomposite materials and preparation technology thereof, the invention discloses a method for preparation of a high polymer material / graphene nanocomposite material by continuous mixing in-situ reduction and application thereof. The used equipment is water assisted melt mixing extrusion equipment. According to the preparation method of the nanocomposite material, graphite oxide powder is placed in deionized water for ultrasonic dispersion to obtain a graphene oxide (GO) suspension, the GO suspension is injected into a high polymer materialmelt in an extruder through a water filling port by a metering pump for mixing, water plays the role of promoting GO stripping, dispersion and in-situ thermal reduction, and finally, the high polymermaterial / reduced graphene oxide (RGO) nanocomposite material can be obtained. The RGO in the nanocomposite material prepared by the method provided by the invention has good stripping and dispersion performance and high reduction degree, and the preparation method has the characteristics of simple operation, no toxicity, and no surface modification to GO.

Description

technical field [0001] The invention relates to the technical field of polymer material / graphene nanocomposite material and its preparation, in particular to a method of realizing in-situ thermal reduction of graphene oxide and better stripping and dispersion in the process of continuous mixing and extrusion to prepare high-performance high-performance composite materials. Methods and applications of molecular materials / graphene nanocomposites. Background technique [0002] Graphene presents a two-dimensional layered nanostructure, has excellent properties such as high hardness, strength, thermal conductivity and electrical conductivity, and has broad application prospects in the fields of materials, information, biomedicine, electronics and energy. However, graphene has poor compatibility with polymer materials and is prone to agglomeration, which is not conducive to its exfoliation and dispersion in polymer materials. Graphene oxide (GO) is a single-layer or multi-layer g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C47/92B29C47/38B29C47/76C08K3/04C08L27/16C08L25/06C08L33/12C09K5/14H05K9/00B29C48/92B29C48/395B29C48/76
CPCB29C48/395B29C48/762B29C48/766B29C48/92C08K3/042C08K2201/001C08K2201/011C08L25/06C08L27/16C08L33/12C08L2201/04C09K5/14H05K9/0081B29C48/022B29C48/40B29C48/767B29C2948/92514B29C2948/9259B29C2948/926
Inventor 黄汉雄童俊
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap