Application of ultra-microporous metal-organic framework materials in isotope separation of hydrogen

A technology of isotope separation and organic framework, applied in the field of nuclear energy utilization, can solve the problems of inability to large-scale application, low separation efficiency, low separation efficiency, etc., and achieve the effects of cheap synthetic raw materials, low price, and simple preparation method.

Active Publication Date: 2018-09-28
TIANJIN POLYTECHNIC UNIV
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although cryogenic distillation is relatively easy for large-scale continuous production, its separation efficiency is very low; although chromatography has high efficie

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of ultra-microporous metal-organic framework materials in isotope separation of hydrogen
  • Application of ultra-microporous metal-organic framework materials in isotope separation of hydrogen
  • Application of ultra-microporous metal-organic framework materials in isotope separation of hydrogen

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] see Figure 1a , Figure 1b , Test of adsorption isotherms of H2, D2 and T2 pure components in SIFSIX-3-Zn.

[0040] Take 30-2000mg SIFSIX-3-Zn, put it into a sample tube that has been accurately weighed, and carry out vacuum degassing on the adsorption instrument. The degassing temperature is between 30-300 ° C, and the degassing time is between 1-12 hours. After the degassing is completed, the sample tube with the sample is accurately weighed again to obtain the sample mass, and at the same time, the sample tube is transferred to the workstation for testing. The test temperature is between 18K and 77K, and the purity of the gas obtained by the test is greater than 99.99%.

Embodiment 2

[0042] see Figure 2a , 2b , 2c, 2d, 2e, 2f, Intermittent adsorption separation performance test of H2, D2 and T2 mixture in SIFSIX-3-Zn,.

[0043]Take 3-5mg SIFSIX-3-Zn sample, put it in the sample cell, and perform vacuum degassing and activation between 30-300°C. After fully activated, cool the sample cell to the test temperature. After the system is balanced, inject the mixture of H2 / D2 / T2 with a specific ratio into the sample cell one or more times to make it reach a certain temperature between 1kPa and 100kPa. pressure point. After the adsorption equilibrium of the system, open the valve to quickly extract the unadsorbed gas mixture, and then close the valve. Cool down the system to a certain temperature between 18K-30K. After equilibrium, connect the sample cell to the mass spectrometer, and gradually raise the temperature. At the same time, use mass spectrometry to analyze the change of hydrogen isotope content over time. The adsorption selectivity can be calculate...

Embodiment 3

[0045] see image 3 , Performance test of fixed bed adsorption separation of H2, D2 and T2 mixture in SIFSIX-3-Zn.

[0046] Take 100-2000mg SIFSIX-3-Zn powder and put it into a packed bed column of a certain specification to ensure that the sample is packed compactly. At the same time, the samples in the packed bed were activated by vacuum degassing at 30–300 °C and purged with He for a certain period of time. After fully activated, cool the sample cell to the test temperature. After the system is balanced, pass a specific ratio of H2 / D2 / T2 mixture from one end of the fixed bed to the bed at a certain flow rate, and monitor the flow of gas from the other end with a mass spectrometer. Concentration changes until the effluent gas concentration remains stable and consistent with the inlet gas concentration. Due to the high selectivity of the material to hydrogen isotopes at 20K, the material can effectively separate D2 / H2 / T2 mixtures.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses the application of ultra-microporous metal-organic framework materials in isotope separation of hydrogen. The ultra-micro porous metal-organic framework material is SIFSIX-3-Zn, used for the effective separation of hydrogen isotopes at low temperature, and the chemical formula of the SIFSIX-3-Zn is Zn (pyr) 2(SiF6). Application of the ultra-microporous metal-organic framework material in the isotope separation of hydrogen enables the separation and purification of D2, H2 in the hydrogen isotope, and the preparation method of the ultra-microporous metal-organic frameworkmaterial is simple. The material can be synthesized in large volumes, and has the advantages of cheap raw materials and low price, and can be widely applied to the industrial hydrogen isotope separation.

Description

technical field [0001] The invention belongs to the technical field of nuclear energy utilization, and in particular relates to the application of an ultra-microporous metal-organic framework material in hydrogen isotope separation, which is a new application of ultra-microporous metal aggregates. The ultramicroporous structure of organic framework materials and the quantum sieve effect of D2 and H2 under low temperature conditions are used to separate and purify D2 / H2. Background technique [0002] Since the discovery of X-rays and radium elements at the end of the 19th century, nuclear science and technology have been continuously developed and matured, and have been gradually applied in military, energy, industry, agriculture, medicine and other fields. At present, the use of nuclear energy is mainly carried out by utilizing the nuclear decay of high atomic number radioactive atoms, such as the current nuclear power plants, nuclear powered submarines and aircraft carriers...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/22B01J20/30B01D59/00C08G83/00
CPCB01D59/00B01J20/226C08G83/008
Inventor 仲崇立韩国鹏黄宏亮刘大欢
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap