Cement-based crystal master batch material and preparation method

A cement-based, crystalline technology, applied in the field of building materials, can solve the problem of low performance, and achieve the effects of simple preparation method, good waterproof performance, good stability and practicability

Inactive Publication Date: 2018-09-28
上海美澎材料科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the performance is still low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A cement-based crystalline masterbatch material, the weight percentage of each component in the material is: 0.5% citric acid, 0.04% sodium tartrate, 15% tartaric acid, 0.3% pimelic acid, 0.3% copper formate tetrahydrate, silicic acid Dicalcium composite powder material is 35%, silicon oxide composite material is 0.02%, and the rest is dicalcium silicate.

[0019] In the silicon oxide composite material, calcium molybdate accounts for 4%.

[0020] For the dicalcium silicate composite powder material, the weight percentage of each component of the material is: 0.5% aluminum sulfate, 0.15% magnesium silicate, 0.5% aluminum potassium sulfate, 0.3% ferric chloride, 3% ferric sulfate, Calcium molybdate 0.06%, aluminum hypophosphite 0.3%, aluminum phosphate 0.3%, and the rest dicalcium silicate.

[0021] Compared with Chinese patent CN201611186413.9, the secondary impermeability is 0.5-1.0MPa, the flexural strength is 3.1-4.5MPa, the compressive strength is 36-48MPa, and the...

Embodiment 2

[0027] A cement-based crystalline masterbatch material, the weight percentage of each component in the material is: 0.6% citric acid, 0.06% sodium tartrate, 18% tartaric acid, 0.4% pimelic acid, 0.4% copper formate tetrahydrate, silicic acid Dicalcium composite powder material is 38%, silicon oxide composite material is 0.03%, and the rest is dicalcium silicate.

[0028] In the silicon oxide composite material, calcium molybdate accounts for 6%.

[0029] The dicalcium silicate composite powder material, the weight percentage of each component of the material is: aluminum sulfate 0.6%, magnesium silicate 0.18%, aluminum potassium sulfate 0.7%, ferric chloride 0.5%, iron sulfate 6%, Calcium molybdate 0.07%, aluminum hypophosphite 0.5%, aluminum phosphate 0.5%, and the rest dicalcium silicate.

[0030]Compared with Chinese patent CN201611186413.9, the secondary impermeability is 0.5-1.0MPa, the flexural strength is 3.1-4.5MPa, the compressive strength is 36-48MPa, and the imperm...

Embodiment 3

[0036] A cement-based crystalline masterbatch material, the weight percentage of each component in the material is: 0.7% citric acid, 0.09% sodium tartrate, 20% tartaric acid, 0.6% pimelic acid, 0.5% copper formate tetrahydrate, silicic acid Dicalcium composite powder material is 40%, silicon oxide composite material is 0.05%, and the rest is dicalcium silicate.

[0037] In the silicon oxide composite material, calcium molybdate accounts for 9%.

[0038] The dicalcium silicate composite powder material, the weight percentage of each component of the material is: 0.8% of aluminum sulfate, 0.20% of magnesium silicate, 0.9% of aluminum potassium sulfate, 0.7% of ferric chloride, 10% of ferric sulfate, Calcium molybdate 0.09%, aluminum hypophosphite 0.8%, aluminum phosphate 0.8%, and the rest dicalcium silicate.

[0039] Compared with Chinese patent CN201611186413.9, the secondary impermeability is 0.5-1.0MPa, the flexural strength is 3.1-4.5MPa, the compressive strength is 36-48...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cement-based crystal master batch material and a preparation method. The material is prepared from, by weight, 0.5-0.7% of citric acid, 0.04-0.09% of sodium tartrate, 15-20%of tartaric acid, 0.3-0.6% of pimelic acid, 0.3-0.5% of copper formate tetrahydrate, 35-40% of dicalcium silicate compound powder materials, 0.02-0.05% of monox compound materials and the balance dicalcium silicate. The cement-based crystal master batch material is applied to cement, has better water-proof performance and is harmless to human bodies, and the preparation method is simple in processand low in production cost and is applicable to industrial production.

Description

technical field [0001] The invention belongs to the field of building materials, and relates to a cement-based crystalline masterbatch material and a preparation method. Background technique [0002] Cement-based crystalline masterbatch materials are used as building materials, and can be widely used in fields such as airports, sports venues, subways, and building construction. CN201611186413.9 discloses a cement-based high-permeability crystalline masterbatch concrete, including high-permeability crystalline masterbatch 8- 12 parts by mass, 60-150 mesh graded quartz sand 35-50 parts by mass, redispersible rubber powder 0.5-2 parts by mass, water reducing agent 0.3-0.5 parts by mass, defoamer 0.3-0.5 parts by mass number, 0.2-0.4 mass fractions of cellulose ether, 40-60 mass fractions of cement and 80-120 mass fractions of water. But the performance is still low. Contents of the invention [0003] The object of the present invention is to provide a cement-based crystalli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/02
CPCC04B7/02
Inventor 丁保俊李合彦赵浩峰
Owner 上海美澎材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap