Anti-cracking green environment-friendly spray coating paint and preparation method thereof

A kind of green environmental protection, anti-cracking technology, applied in the field of paint, can solve the problems of affecting paint quality, cracks, layering, etc., to achieve the effect of wide application range, good uniformity and low concentration

Inactive Publication Date: 2018-09-28
CARPOLY CHEM GRP
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Furthermore, many existing paints will have cracks and layers after being used for a period of time, which will seriously affect the quality of the paint.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] In the present embodiment, the anti-crack type green environmental protection spray paint is made up of following components by weight parts: 10 parts of water-soluble acrylic resins, 5 parts of titanium dioxide, 3 parts of linseed oils, 2 parts of natural resins, 2 parts of cobalt isooctanoate, 8 parts of tung oils 5 parts of calcium oxide, 3 parts of turpentine, 4 parts of stabilizer, 6 parts of glycerin, 2 parts of curing agent, 5 parts of epoxy resin coagulant, 5 parts of limonene, 3 parts of dimethylaniline, and 0.3 parts of defoamer 0.3 parts of leveling agent, 0.3 parts of wetting agent, 5 parts of mica powder, 3 parts of filler and 1 part of pigment;

[0028] The preparation method of the anti-cracking type green environmental protection spray paint of the present embodiment is as follows:

[0029] (1) Add water-soluble acrylic resin, titanium dioxide, linseed oil, natural resin, cobalt isooctanoate, tung oil, and calcium oxide into the reaction kettle for stirr...

Embodiment 2

[0038] The preparation method of the anti-cracking type green environmental protection spray paint in the present embodiment is basically the same as the method of embodiment 1, the difference is that the anti-crack type green environmental protection spray paint in the present embodiment consists of the following components in parts by weight : 11 parts of water-soluble acrylic resin, 6 parts of titanium dioxide, 5 parts of linseed oil, 4 parts of natural resin, 3 parts of cobalt isooctanoate, 10 parts of tung oil, 8 parts of calcium oxide, 5 parts of turpentine, 6 parts of stabilizer, 7 parts of glycerin 3 parts, 3 parts of curing agent, 7 parts of epoxy resin coagulant;

[0039] Optionally, 6 parts of limonene, 4 parts of dimethylaniline, 0.5 parts of defoamer, 0.5 parts of leveling agent, 0.5 parts of wetting agent, 8 parts of mica powder, 6 parts of filler and 3 parts of pigment can be added to the above components .

[0040] The anti-cracking type green environmental pr...

Embodiment 3

[0042] The preparation method of the anti-cracking type green environmental protection spray paint in the present embodiment is basically the same as the method of embodiment 1, the difference is that the anti-crack type green environmental protection spray paint in the present embodiment consists of the following components in parts by weight : 12 parts of water-soluble acrylic resin, 8 parts of titanium dioxide, 6 parts of linseed oil, 5 parts of natural resin, 4 parts of cobalt isooctanoate, 12 parts of tung oil, 10 parts of calcium oxide, 6 parts of turpentine, 4-8 parts of stabilizer, glycerin 8 parts of alcohol, 4 parts of curing agent, and 8 parts of epoxy resin coagulant.

[0043] Optionally, 8 parts of limonene, 5 parts of dimethylaniline, 0.6 parts of defoamer, 0.6 parts of leveling agent, 0.6 parts of wetting agent, 10 parts of mica powder, 8 parts of filler and 4 parts of pigment can be added to the above components .

[0044] The anti-cracking type green environmen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides anti-cracking green environment-friendly spray coating paint and a preparation method thereof. The anti-cracking green environment-friendly spray coating paint is prepared fromthe following ingredients in parts by weight: 10 to 12 parts of water soluble acrylic resin, 5 to 8 parts of titanium dioxide, 3 to 6 parts of linseed oil, 2 to 5 parts of natural resin, 2 to 4 partsof cobalt iso-octoate, 8 to 12 parts of tung oil, 5 to 10 parts of calcium oxide, 3 to 6 parts of turpentine, 4 to 8 parts of stabilizing agents, 6 to 8 parts of glycerol, 2 to 4 parts of curing agents, 5 to 8 parts of epoxy resin curing glue and optional auxiliary materials. The linseed oil, the natural resin, the tung oil and the turpentine are added in the paint, so that the problems of cracking, layering and the like cannot occur with the use time increases; in addition, the paint obtained by using the formula is safe, environmental friendly, non-toxic and harmless; in addition, the concentration is low; a spray coating manner can be used; the uniformity is high; the furniture spray coating is facilitated; the application range is wide.

Description

technical field [0001] The invention belongs to the technical field of paints, and in particular relates to an anti-cracking type green environmental protection spray paint and a preparation method thereof. Background technique [0002] Paint, traditionally called paint in China, is coated on the surface of an object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated. It is usually based on resin, oil or emulsion, with or without adding Pigments, fillers and corresponding additives are viscous liquids prepared with organic solvents or water. The relatively authoritative book "Painting Technology" in the Chinese coatings industry defines it as follows: "Painting is a material that can be coated on the surface of an object by different construction techniques to form a firm adhesion, a certain strength, and a continuous coating. Solid film. The film formed in this way is commonly called a coating film, also known as a paint...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/06C09D7/61C09D7/63C09D7/65
CPCC09D4/06C09D7/61C09D7/63C09D7/65
Inventor 苏东泓段琪
Owner CARPOLY CHEM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com