Non-toxic environmental-friendly water-resistant coating and preparation method thereof

A waterproof coating, non-toxic and environmentally friendly technology, applied in the direction of anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of toxicity, etc., to achieve the effects of reducing bubbles, increasing gloss, and fast film forming speed

Inactive Publication Date: 2018-10-09
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when using this kind of paint, it is generally diluted with organic solvents such as toluene and xylene, so it also contains toxicity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A non-toxic and environment-friendly waterproof coating, the waterproof coating is made of the following raw materials in parts by weight: 48 parts of polyurethane resin, 12 parts of epoxy resin, 4 parts of alkyd resin, 2 parts of organic silicon, 2 parts of mica powder, oxidized 1.4 parts of zinc, 0.4 parts of graphene, 3 parts of linoleic acid, 0.8 parts of leveling agent, and 0.4 parts of defoaming agent.

[0023] The leveling agent is any one of polyacrylic acid and carboxymethyl cellulose; the defoamer is polydimethylsiloxane.

[0024] A kind of preparation method of non-toxic environment-friendly waterproof paint, comprises the following steps:

[0025] (1) Mix and stir the polyurethane resin and the alkyd resin, then add silicone and keep warm and stir evenly at a temperature of 40-50°C to obtain a mixed resin for later use;

[0026] (2) Epoxy resin is added to deionized water and mixed and stirred evenly, then linoleic acid is added to continue stirring to obta...

Embodiment 2

[0030] A non-toxic and environment-friendly waterproof coating, the waterproof coating is made of the following raw materials in parts by weight: 60 parts of polyurethane resin, 16 parts of epoxy resin, 10 parts of alkyd resin, 4 parts of organic silicon, 3 parts of mica powder, oxidized 2 parts of zinc, 1.2 parts of graphene, 5 parts of linoleic acid, 1.8 parts of leveling agent, and 0.8 parts of defoamer.

[0031] The leveling agent is any one of polyacrylic acid and carboxymethyl cellulose; the defoamer is polydimethylsiloxane.

[0032] A kind of preparation method of non-toxic environment-friendly waterproof paint, comprises the following steps:

[0033] (1) Mix and stir the polyurethane resin and the alkyd resin, then add silicone and keep warm and stir evenly at a temperature of 40-50°C to obtain a mixed resin for later use;

[0034] (2) Epoxy resin is added to deionized water and mixed and stirred evenly, then linoleic acid is added to continue stirring to obtain water...

Embodiment 3

[0038] A non-toxic and environment-friendly waterproof coating, the waterproof coating is made of the following raw materials in parts by weight: 50 parts of polyurethane resin, 13 parts of epoxy resin, 6 parts of alkyd resin, 2.5 parts of organic silicon, 2.2 parts of mica powder, oxidized 1.6 parts of zinc, 0.6 parts of graphene, 3.5 parts of linoleic acid, 1 part of leveling agent, and 0.5 parts of defoaming agent.

[0039] The leveling agent is any one of polyacrylic acid and carboxymethyl cellulose; the defoamer is polydimethylsiloxane.

[0040] A kind of preparation method of non-toxic environment-friendly waterproof paint, comprises the following steps:

[0041] (1) Mix and stir the polyurethane resin and the alkyd resin, then add silicone and keep warm and stir evenly at a temperature of 40-50°C to obtain a mixed resin for later use;

[0042] (2) Epoxy resin is added to deionized water and mixed and stirred evenly, then linoleic acid is added to continue stirring to o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a non-toxic environmental-friendly water-resistant coating and a preparation method thereof and relates to the technical field of coating processing. The non-toxic environmental-friendly water-resistant coating is prepared from the follow raw materials in parts by weight: 48-60 parts of a polyurethane resin, 12-16 parts of an epoxy resin, 4-10 parts of an alkyd resin, 2-4 parts of organosilicone, 2-3 parts of mica powder, 1.4-2 parts of zinc oxide, 0.4-1.2 parts of graphene, 3-5 parts of linoleic acid, 0.8-1.8 parts of a leveling agent and 0.4-0.8 part of a defoaming agent. The coating provided by the invention is prepared by using methods such as mixing, modification, heating and stirring; the filming property of a common water-resistant coating is improved, the water-resistant effect of the coating is improved, and in addition, the coating is safe and environmental-friendly in raw material and free of toxic component volatilization and has the advantages of long-lasting water resistance, wearing resistance and corrosion resistance.

Description

technical field [0001] The invention relates to the technical field of paint processing, in particular to a non-toxic and environment-friendly waterproof paint and a preparation method thereof. Background technique [0002] Waterproof coating is a kind of coating that is painted on the surface of a building and forms a thin film through the volatilization of solvent or water or the chemical reaction of the two components to isolate the surface of the building from water, thereby playing the role of waterproof and sealing. . The waterproof film formed after the waterproof coating is cured has certain extensibility, elastic-plasticity, crack resistance, impermeability and weather resistance, and can play a waterproof, anti-seepage and protective role for related buildings and materials. [0003] The main category of waterproof materials on the market is polyurethane waterproof coatings. Such materials are generally made of polyurethane and coal tar as raw materials. The tar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/61C09D7/65C09D5/08
CPCC08L2205/03C09D5/08C09D7/61C09D7/65C09D175/04C08L67/08C08L63/00C08K13/02C08K3/34C08K3/22C08K3/042
Inventor 王和山王厚国王和东殷东楼殷芳荣曹文强张万霞张萍
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com