A graphene-based hollow cobalt sulfide nanocrystal capable of efficiently activating persulfate and its preparation method

A technology for activating persulfate and graphene-based, applied in the directions of cobalt sulfide, graphene, chemical instruments and methods, etc., can solve the problem of low electrical conductivity, low utilization rate of internal sites, and density of catalytic sites on the surface of solid cobalt sulfide. Low problems, to overcome large dosage, rapid treatment of pollutants, significant environmental and economic significance

Active Publication Date: 2020-01-31
NANJING UNIV
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the catalyst activity is still limited by the low conductivity of CoS4
Kong et al. synthesized graphene-supported solid cobalt sulfide in one step by solvothermal method for use as lithium-ion batteries and photocatalysts (Kong et al. Morphological Effect of Graphene Nanosheets on Ultrathin CoSNanosheets and Their Applications for High-Performance Li-Ion Batteries and Photocatalysis, J .Phys.Chem.C 2014,118,25355-25364), but the density of catalytic sites on the surface of solid cobalt sulfide is low, and the utilization rate of internal sites is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A graphene-based hollow cobalt sulfide nanocrystal capable of efficiently activating persulfate and its preparation method
  • A graphene-based hollow cobalt sulfide nanocrystal capable of efficiently activating persulfate and its preparation method
  • A graphene-based hollow cobalt sulfide nanocrystal capable of efficiently activating persulfate and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A graphene-based hollow cobalt sulfide nanocrystal capable of efficiently activating persulfate and a preparation method thereof, the steps of which are:

[0032] a. Preparation of graphene oxide-based zeolite-type imidazolate framework 67: Graphene oxide is uniformly dispersed in water by ultrasound to obtain a graphene oxide dispersion with a concentration of 3 mg / mL, and then cobalt nitrate hexahydrate is added to it at a concentration of 12 mg / mL mL, stirred at room temperature for 0.5-2 hours to adsorb cobalt ions on the surface of graphene oxide, then added 2-methylimidazole aqueous solution with a concentration of 54 mg / mL, stirred at room temperature for 5-30 minutes, then centrifuged, washed with water, and dried to obtain Graphene oxide-based zeolitic imidazolate frameworks67.

[0033] b. Preparation of graphene oxide-based hollow cobalt tetrasulfide: the graphene oxide-based zeolite-type imidazolate framework 67 obtained in step a is uniformly dispersed in et...

Embodiment 2

[0039] With embodiment 1, difference is:

[0040] The concentration of graphene oxide dispersion in step a is 0.5mg / mL;

[0041] In step b, the concentration of the graphene oxide-based zeolite-type imidazolate framework 67 ethanol dispersion is 3mg / mL, the concentration of thioacetamide is 4.5mg / mL, the solvothermal reaction temperature is 140°C, and the reaction time is 6h;

[0042] In step c, the inert protective gas is argon, and the heating rate is 10° C. / min.

[0043] The degradation rate of the obtained catalyst to bisphenol A within 8 minutes under the same experimental conditions as in Example 1 was 88%.

Embodiment 3

[0045] With embodiment 1, difference is:

[0046] The concentration of cobalt nitrate hexahydrate in step a is 20mg / mL, and the concentration of 2-methylimidazole is 90mg / mL;

[0047] In step b, the concentration of the graphene oxide-based zeolite-type imidazolate framework 67 ethanol dispersion is 1 mg / mL, the concentration of thioacetamide is 1.5 mg / mL, the solvothermal reaction temperature is 120 ° C, and the reaction time is 3 h;

[0048] The obtained catalyst had a degradation rate of 99% to bisphenol A within 8 minutes under the same experimental conditions as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of environmental catalyst synthesis, and relates to a graphene-based hollow cobalt sulfide nanocrystal capable of efficiently activating persulfate and a preparation method thereof. First, a zeolite-type imidazole ester framework 67 is grown on the surface of graphene oxide by a precipitation method; The ester framework 67 is a self-template, thioacetamide is used as a sulfur source, and a hollow structure cobalt tetrasulfide is prepared by solvothermal reaction; finally, it is calcined in an inert atmosphere, and three cobalt tetraoxide is converted into a hollow cobalt sulfide through a desulfurization reaction, and the graphene oxide Reduced to graphene, thereby making graphene-based hollow cobalt sulfide nanocrystals; the hollow cobalt sulfide nanocrystals prepared by the present invention have the advantages of high catalytic activity, large free radical production, and simple recycling, which can strengthen conventional oxidation methods and significantly reduce The reaction time is shortened, and the amount of catalyst and oxidant is greatly reduced, which has significant technical and economic advantages.

Description

technical field [0001] The invention belongs to the field of environmental catalyst synthesis, and relates to a graphene-based hollow cobalt sulfide nanocrystal capable of efficiently activating persulfate and a preparation method thereof. Background technique [0002] The uncontrolled discharge of organic waste water from industry, life and medicine has caused more and more serious water pollution. For highly toxic and persistent organic substances, physical and chemical methods such as traditional adsorption and membrane treatment can only transfer but are difficult to reduce their toxicity. Microorganisms in biochemical methods are not very tolerant to highly toxic organic substances, and the treatment effect is not good. Advanced oxidation technology can degrade or even mineralize organic matter, can significantly reduce its toxicity and improve biodegradability, and can be placed at the front or end of the water treatment process to achieve efficient removal of organic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/184C01G51/00B82Y40/00B82Y30/00B01J27/043B01J35/02C02F1/72C02F101/30B01J35/00
CPCB82Y30/00B82Y40/00C01B32/184C01G51/30C02F1/725B01J27/043C01P2004/03C01P2004/04C01P2004/64C02F2101/30B01J35/50B01J35/40
Inventor 刘福强朱长青凌晨江昊吴海德李爱民
Owner NANJING UNIV