Method for improving waterproof performance of rattan chair

A technology for rattan chairs and performance, which is applied in the field of improving the waterproof performance of rattan chairs, which can solve the problems of poor water resistance and reduced service life, and achieve excellent water resistance, prevent water infiltration, and excellent corrosion and oxidation resistance.

Inactive Publication Date: 2018-11-06
阜南县富昌恒业工艺品有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The rattan chairs made in the prior art have poor water resistance, and if they are placed outdoors, their service life will be greatly reduced after being exposed to rain.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A method for improving the waterproof performance of rattan chairs, comprising the following steps:

[0015] (1) Wash the rattan, put it into the modification solution, soak it for 4 hours, then take it out and dry it until the water content is 8%, wherein the modification solution is made of the following components by weight: aminoguanidine sulfuric acid 3 parts of salt, 8 parts of sodium dimethylformamide sulfonate, 13 parts of dibutyl sulfosuccinate sodium salt, 140 parts of water;

[0016] (2) Apply waterproof paint on the surface of the dried rattan, then put the rattan into an oven, and after drying, weave it into a rattan chair, wherein the waterproof paint is made by the following method: by weight In total, 36 parts of isobutyl methacrylate, 20 parts of methyl methacrylate, 1 part of sodium cyclamate, 2 parts of poloxamer, 6 parts of low-substituted hydroxypropyl cellulose, and 1 part of initiator After mixing evenly, heat to 74° C., and heat preservation tre...

Embodiment 2

[0020] A method for improving the waterproof performance of rattan chairs, comprising the following steps:

[0021] (1) Wash the rattan, put it into the modification solution, soak it for 4.5 hours, then take it out and dry it until the water content is 10%, wherein the modification solution is made of the following components by weight: aminoguanidine sulfuric acid 5 parts of salt, 9 parts of sodium dimethylformamide sulfonate, 15 parts of dibutyl sulfosuccinate sodium salt, 150 parts of water;

[0022] (2) Apply waterproof paint on the surface of the dried rattan, then put the rattan into an oven, and after drying, weave it into a rattan chair, wherein the waterproof paint is made by the following method: by weight In total, 40 parts of isobutyl methacrylate, 22 parts of methyl methacrylate, 3 parts of sodium cyclamate, 5 parts of poloxamer, 8 parts of low-substituted hydroxypropyl cellulose, 2 parts of initiator After mixing evenly, heat to 76° C. and heat preservation tre...

Embodiment 3

[0026] A method for improving the waterproof performance of rattan chairs, comprising the following steps:

[0027] (1) After washing the rattan, put it into the modification solution, soak it for 5 hours, then take it out and dry it until the water content is 12%, wherein the modification solution is made of the following components by weight: aminoguanidine sulfuric acid 6 parts of salt, 10 parts of sodium dimethylformamide sulfonate, 17 parts of dibutyl sulfosuccinate sodium salt, 160 parts of water;

[0028] (2) Apply waterproof paint on the surface of the dried rattan, then put the rattan into an oven, and after drying, weave it into a rattan chair, wherein the waterproof paint is made by the following method: by weight In total, 44 parts of isobutyl methacrylate, 24 parts of methyl methacrylate, 4 parts of sodium cyclamate, 7 parts of poloxamer, 10 parts of low-substituted hydroxypropyl cellulose, 2 parts of initiator After mixing evenly, heat to 80° C. and heat preserv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing method for improving the waterproof performance of a rattan chair. The method comprises the following operation steps that 1, after being washed cleanly, rattanis placed in modified liquid and subjected to soaking treatment for 4-5 hours, and then the rattan is taken out and dried until the water content is 8-12%; and 2, the surface of the rattan obtained after drying treatment is brushed with waterproof paint, then the rattan is placed in an oven, and after the drying treatment, the rattan is woven into the rattan chair. The rattan chair manufactured by the adoption of the method is excellent in various mechanical properties, high in strength, and excellent in corrosion resistant and oxidization resistant performance, and especially has excellent waterproof performance.

Description

technical field [0001] The invention belongs to the technical field of wicker chair weaving, and in particular relates to a method for improving the waterproof performance of a wicker chair. Background technique [0002] Rattan is a climbing plant of the palm family in the treasure house of tropical and subtropical forests. It has thorns, rapid growth and strong regeneration ability. The general growth cycle is 5-7 years. There are many kinds of vines. There are more than 600 species in 13 genera in the world, 10 of which are distributed in Southeast Asia and its adjacent areas, and 4 are distributed in tropical West Africa (3 of which are endemic). Among the many vine-producing areas, Indonesia is located in the equatorial tropical rainforest area, with abundant sunshine and rain all year round, and fertile volcanic ash soil, which makes the vines produced are thick, plump, well-proportioned, and of good quality. Indonesian vines are famous all over the world for this reaso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/04B27K3/50B27K3/12B27K5/04B27K9/00B27J1/02C09D4/06C09D4/02C09D7/63
CPCB27K3/04B27J1/02B27K3/12B27K3/50B27K5/04B27K9/002C09D4/06
Inventor 张恒
Owner 阜南县富昌恒业工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com