Furfuryl alcohol resin wood and modification treatment process

A technology of furfuryl alcohol resin and wood, applied in wood treatment, wood treatment details, wood processing appliances, etc., can solve the problem of acid resistance, alkali resistance, flame retardancy, abrasion resistance, color stability, mechanical strength and dimensional stability In order to improve the anti-corrosion effect, prevent moisture erosion, and improve the aesthetics

Active Publication Date: 2018-11-16
A ZENITH HOME FURNISHINGS CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing wood does not have good acid resistance, alkali resistance, flame retardancy, abrasion resistance, color stability, mechanical strength and dimensional stability, and it is not convenient for the staff to connect the wood during use. Therefore it is necessary to design a kind of furfuryl alcohol resin wood and modification process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Furfuryl alcohol resin wood and modification treatment process
  • Furfuryl alcohol resin wood and modification treatment process
  • Furfuryl alcohol resin wood and modification treatment process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] It includes the following steps: step one, preparation of furfuryl alcohol resin; step two, degreasing; step three, washing and drying; step four, cross-linking treatment; step five, acetylation and cyanoacetation treatment; step six, resin impregnation treatment; step seven , Wood bleaching and dyeing;

[0035] Among them, in the above step 1, according to the weight percentage of each raw material, they are: furfuryl alcohol 55%, formaldehyde 15%, urea 10%, sodium hydroxide 5%, acetic acid 5%, p-toluenesulfonic acid 5%, xylene sulfonic acid 5% is selected and weighed according to the above weight; first add formaldehyde to the reactor, add urea under stirring, and add 1 / 4 of the total furfuryl alcohol, turn on steam to heat, and add sodium hydroxide solution to adjust the pH value , Continue to heat up to about 98°C. At this time, you can see that there is reflux, that is, the reaction product is produced, from the sight of the reflux. The time is 15 minutes after seeing...

Embodiment 2

[0043] It includes the following steps: step one, preparation of furfuryl alcohol resin; step two, degreasing; step three, washing and drying; step four, cross-linking treatment; step five, acetylation and cyanoacetation treatment; step six, resin impregnation treatment; step seven , Wood bleaching and dyeing;

[0044] Among them, in the above step 1, according to the weight percentage of each raw material, they are: furfuryl alcohol 60%, formaldehyde 10%, urea 10%, sodium hydroxide 5%, acetic acid 5%, p-toluenesulfonic acid 5%, xylene sulfonic acid 5% is selected and weighed according to the above weight; first add formaldehyde to the reactor, add urea under stirring, and add 1 / 4 of the total furfuryl alcohol, turn on steam to heat, and add sodium hydroxide solution to adjust the pH value , Continue to heat up to about 98°C. At this time, you can see that there is reflux, that is, the reaction product is produced, from the sight of the reflux. The time is 15 minutes after seeing...

Embodiment 3

[0052] It includes the following steps: step one, preparation of furfuryl alcohol resin; step two, degreasing; step three, washing and drying; step four, cross-linking treatment; step five, acetylation and cyanoacetation treatment; step six, resin impregnation treatment; step seven , Wood bleaching and dyeing;

[0053] Among them, in the above step 1, according to the weight percentage of each raw material: furfuryl alcohol 50%, formaldehyde 20%, urea 10%, sodium hydroxide 5%, acetic acid 5%, p-toluenesulfonic acid 5%, xylene sulfonic acid 5% is selected and weighed according to the above weight; first add formaldehyde to the reactor, add urea under stirring, and add 1 / 4 of the total furfuryl alcohol, turn on steam to heat, and add sodium hydroxide solution to adjust the pH value , Continue to heat up to about 98°C. At this time, you can see that there is reflux, that is, the reaction product is produced, from the sight of the reflux. The time is 15 minutes after seeing the reflu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses furfuryl alcohol resin wood and a modification treatment process. The furfuryl alcohol resin wood comprises a wood body, a sliding block, a sliding groove, positioning holes, threaded holes, concave grooves, fixing bolts, a polyvinyl chloride coating, a wear-resistant layer, a wood grain layer, an anti-corrosion layer, a balance layer, through holes, a mounting groove, a spring and a ball, wherein the sliding block is installed on one side of the wood body, the positioning holes are formed in the two ends of the outer side of the sliding block correspondingly, the threaded holes are formed in the two sides of the top end of the sliding block correspondingly, the sliding groove is formed in one side of the wood body, and the concave grooves are formed in the two endsof the top end of the sliding groove correspondingly; and the through holes are formed in the centers of the interiors of the concave grooves, the fixing bolts are arranged inside the through holes,and the fixing bolts are connected with the threaded holes in a matched mode; according to the wood and the process, the treatment process comprises the following steps of preparing the furfuryl alcohol resin; degreasing; cleaning and drying; cross-linking treatment; acetylation and cyanation treatment; resin impregnation treatment; wood bleaching and dyeing, so that the wear resistance and the corrosion resistance of the furfuryl alcohol resin wood are effectively ensured.

Description

Technical field [0001] The invention relates to the technical field of wood modification, in particular to a furfuryl alcohol resin wood and a modification treatment process. Background technique [0002] Physical or (and) chemical processing methods to improve or change the physical, mechanical, chemical properties and structural characteristics of wood, the purpose of which is to improve the wood’s natural corrosion resistance, acid resistance, alkali resistance, flame retardancy, Abrasion resistance, color stability, mechanical strength and dimensional stability. Wood that has been modified is called modified wood or modified wood. As for wood that has been treated with protection, plywood, particleboard, etc., although they have some properties of modified wood, However, it is customarily not included in the category of modified wood. [0003] However, the existing wood does not have good acid resistance, alkali resistance, flame resistance, abrasion resistance, color stabilit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/20B27K5/00B27K3/08B27K5/04B27K3/36B27K5/02B27K3/50F16B5/00B27D1/00B32B21/06
CPCB27D1/00B27K3/08B27K3/20B27K3/36B27K3/50B27K5/001B27K5/02B27K5/04B27K2240/20B27K2240/70B27K2240/90B32B21/06F16B5/00
Inventor 卢建军钱蒋锋高伟张玲云沈霞张爱林
Owner A ZENITH HOME FURNISHINGS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com