Knitted fabric capable of improving flame-retardant performance and preparation method thereof

A technology for knitted fabrics and flame retardant properties, applied in the field of knitted fabrics with improved flame retardant properties and their preparation, can solve problems such as poor flame retardant properties, and achieve the effects of improved flame retardant properties, good toughness, and improved overall performance

Inactive Publication Date: 2018-11-23
HEFEI YUANKE GARMENT DESIGN CO LTD
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing Chinese patent document (publication number: CN105595488A) discloses an anti-pilling knitted fabric and its preparation method. The fabric is composed of three layers of inner, middle and outer layers respectively composed of different components, and the inner layer is made of cellulose fiber and acrylic fiber. The middle layer is made of polyester fiber, polyester fiber and lignin fiber; the outer layer is made of cotton fiber, hemp fiber and wool blended fiber. Although the knitted fabric can resist pilling, it has poor flame retardancy and requires further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The knitted fabric with improved flame retardancy of this embodiment includes the following raw materials in parts by weight:

[0031] Pretreated bamboo fiber 24 parts, polypropylene fiber 16 parts, pure cotton 12 parts, needle-like wollastonite powder 8 parts, flame retardant reinforcing agent 6 parts, sepiolite fiber 4 parts, sodium silicate 2 parts, hindered phenol 1 part , 4 parts of microporous bamboo charcoal, 1 part of mullite powder.

[0032] The preparation method of the pretreated bamboo fiber in this embodiment is to send the bamboo fiber into boiling water and boil it for 35 minutes, then add isopropyl triisostearate titanate for reflux, reflux for 12 minutes, the reflux temperature is 65 ℃, and then send it to the barrier Soak in the combustion aid for 25 minutes, take it out and dry, and get the pretreated bamboo fiber.

[0033] The flame retardant auxiliary agent of this embodiment is a mixture of ammonium chloride and ammonium bromide in a weight ratio of 3:1....

Embodiment 2

[0042] The knitted fabric with improved flame retardancy of this embodiment includes the following raw materials in parts by weight:

[0043] Pretreated bamboo fiber 30 parts, polypropylene fiber 22 parts, pure cotton 14 parts, needle-like wollastonite powder 12 parts, flame retardant reinforcing agent 10 parts, sepiolite fiber 8 parts, sodium silicate 5 parts, hindered phenol 3 parts , 8 parts of microporous bamboo charcoal, 3 parts of mullite powder.

[0044] The preparation method of the pretreated bamboo fiber in this embodiment is to send the bamboo fiber into boiling water for 45 minutes, then add isopropyl triisostearate titanate for reflux, reflux for 16 minutes, the reflux temperature is 75 ℃, and then send it to the barrier Soak in the combustion aid for 35 minutes, take it out and dry, and get the pretreated bamboo fiber.

[0045] The flame retardant auxiliary agent of this embodiment is a mixture of ammonium chloride and ammonium bromide in a weight ratio of 6:1.

[0046]...

Embodiment 3

[0054] The knitted fabric with improved flame retardancy of this embodiment includes the following raw materials in parts by weight:

[0055] Pretreated 27 parts of bamboo fiber, 18 parts of polypropylene fiber, 13 parts of pure cotton, 10 parts of acicular wollastonite powder, 8 parts of flame retardant reinforcing agent, 6 parts of sepiolite fiber, 3.5 parts of sodium silicate, 2 parts of hindered phenol , 6 parts of microporous bamboo charcoal, 2 parts of mullite powder.

[0056] The preparation method of the pretreated bamboo fiber in this embodiment is to send the bamboo fiber into boiling water for 40 minutes, then add isopropyl triisostearate titanate for reflux, reflux for 14 minutes, the reflux temperature is 70 ℃, and then send it into the barrier Soak in the combustion aid for 30 minutes and take it out to dry to obtain pretreated bamboo fiber.

[0057] The flame retardant auxiliary in this embodiment is a mixture of ammonium chloride and ammonium bromide in a weight rati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a knitted fabric capable of improving flame-retardant performance. The knitted fabric is prepared from the following raw materials in parts by weight: 24 to 30 parts of preprocessed bamboo fibers, 16 to 22 parts of polypropylene fibers, 12 to 14 parts of pure cotton, 8 to 12 parts of needle-shaped wollastonite, 6 to 10 parts of a flame-retardant reinforcing agent, 4 to 8 parts of sepiolite fibers, 2 to 5 parts of sodium silicate, 1 to 3 parts of hindered phenol, 4 to 8 parts of micro-porous bamboo charcoal, and 1 to 3 parts of mullite powder. The invention aims at providing the knitted fabric capable of improving the flame-retardant performance. Compared with the knitted fabric in the prior art, the flame-retardant performance of the fabric is greatly improved. Theknitted fabric provided by the invention has high application value and good application prospect.

Description

Technical field [0001] The invention relates to the technical field of fabrics, in particular to a knitted fabric with improved flame retardancy and a preparation method thereof. Background technique [0002] Fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly influence the performance of clothing colors and shapes. In the clothing world, clothing fabrics are diverse and change with each passing day. But generally speaking, high-quality and high-end fabrics have the characteristics of comfortable wearing, sweat-absorbing and breathable, drape and stiff, noble vision, and soft touch. Knitted fabrics use knitting needles to bend the yarn into loops and Fabrics formed by intertwining, knitted fabrics and woven fabrics are different in the form of yarns in the fabric. Knitting is divided into weft knitting and warp knitting. At present, knitted fabrics are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/79D06M11/74D06M13/152D06M13/50D06M11/13D06M11/45D06M15/55D06M101/20D06M101/04D06M101/06
CPCD06M11/79D06M11/13D06M11/45D06M11/74D06M13/152D06M13/50D06M15/55D06M2101/04D06M2101/06D06M2101/20D06M2200/30
Inventor 张力
Owner HEFEI YUANKE GARMENT DESIGN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com