Method of reducing combustion clinkering rate of corn straw biomass particle fuel

A technology of biomass pellets and corn stalks, applied in the direction of biofuels, waste fuels, fuels, etc., can solve the problems of high slagging rate and reduction, improve ash melting point, solve high slagging rate, and realize resource maximization The effect of using

Inactive Publication Date: 2018-12-07
合肥市晶谷农业科技开发有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to address the existing problems and provide a method for reducing the slagging rate of corn stalk biomass pellet fuel combustion, which effectively solves the problem of high slagging rate in the existing corn stalk biomass pellet fuel combustion, and improves The utilization value of straw waste and the intensity of environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for reducing the slagging rate of corn stalk biomass pellet fuel combustion. The prepared porous ceramic particles are mixed into corn stalks, the raw material for preparing biomass pellet fuel, in an amount of 0.25% of the mass of corn stalks. The porous ceramic particles The preparation method of ceramic particle comprises the following steps:

[0019] (1) Weigh 5.5 grams of graphene and add it to 150 milliliters of dimethylformamide solvent, stir at 1800 rpm for 20 minutes, then ultrasonically disperse for 8 minutes, add 0.5 grams of dodecyl to the dispersion Sodium sulfate, put into the ball ink tank for ball ink, the ball milling time is 7 hours, after the ball milling is completed, the feed liquid is taken out, and after standing and layering, it is centrifuged at high speed for 50 seconds to obtain the suspension under reduced pressure to remove the solvent, and the product is washed with ethanol for 2 After one pass, place in an oven at 80°C and dry to ...

Embodiment 2

[0027] A method for reducing the slagging rate of corn stalk biomass pellet fuel combustion. The prepared porous ceramic particles are mixed into corn stalks, a raw material for preparing biomass pellet fuel, in an amount of 0.27% of the mass of corn stalks. The porous ceramic particles The preparation method of ceramic particle comprises the following steps:

[0028] (1) Weigh 5.8 grams of graphene and add it to 155 milliliters of dimethylformamide solvent, stir at 1900 rpm for 25 minutes, then ultrasonically disperse for 9 minutes, add 0.65 grams of dodecyl to the dispersion Sodium sulfate, put into the ball ink tank for ball ink, the ball milling time is 7.5 hours, after the ball milling is completed, the feed liquid is taken out, and after standing and layering, it is centrifuged at high speed for 55 seconds to obtain the suspension under reduced pressure to remove the solvent, and the product is washed with ethanol for 2 After one pass, place in an oven at 85°C and dry to...

Embodiment 3

[0036] A method for reducing the slagging rate of corn stalk biomass pellet fuel combustion. The prepared porous ceramic particles are mixed into corn stalks, a raw material for preparing biomass pellet fuel, in an amount of 0.30% of the mass of corn stalks. The porous ceramic particles The preparation method of ceramic particle comprises the following steps:

[0037] (1) Weigh 6.0 grams of graphene and add it to 160 ml of dimethylformamide solvent, stir at 2000 rpm for 30 minutes, then ultrasonically disperse for 10 minutes, add 0.8 grams of dodecyl to the dispersion Sodium sulfate, put into the ball ink tank for ball ink, the ball milling time is 8 hours, after the ball milling is completed, the feed liquid is taken out, and after standing and layering, it is centrifuged at high speed for 60 seconds to obtain the suspension under reduced pressure to remove the solvent, and the product is washed with ethanol for 3 After one pass, place in a 90°C oven and dry to constant weigh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of modern agricultural industry and discloses a method of reducing the combustion clinkering rate of a corn straw biomass particle fuel. By means of combustion characteristic and combustion principle of dynamics, prepared porous ceramic particles with an adsorption function are doped into the corn straws, so that the condition that low-melting-point compounds are generated by alkaline metal elements such as potassium and sodium in biomass ash can be prevented, so that the clinkering rate is reduced and the melting point of ash of the corn straw particle fuel is improved, and the problem that the corn straws in the combustion process are easy to agglomerate and clinker is solved. By simulating a combustion test, the prepared corn straw biomass particle fuel is not coked fully at 1300 DEG C. The method solves the problem that the clinkering rate of the existing corn straw biomass particle combustion fuel is high is solved effectively, can achieve extreme utilization of resources and practical significance of environmental protection, has application value in development of biomass energy sources, and is a technical scheme which is worth being popularized and used extremely.

Description

technical field [0001] The invention belongs to the technical field of modern agricultural industry, and in particular relates to a method for reducing the slagging rate of corn stalk biomass particle fuel combustion. Background technique [0002] Biomass fuel: refers to the burning of biomass materials as fuel, generally mainly agricultural and forestry waste (such as straw, sawdust, bagasse, rice bran, etc.), which is mainly different from fossil fuels. In the current national policy and environmental protection standards, direct combustion of biomass is a highly polluting fuel, which is only used in large stoves in rural areas and is not allowed to be used in cities. The application of biomass fuel is actually mainly biomass briquette fuel, which uses agricultural and forestry waste as raw materials, and is made into various shapes (such as lumps, granules, etc.) through crushing, mixing, extrusion, drying and other processes. A new type of clean fuel that can be directl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10L9/10C10L5/44C04B38/02C04B35/16C04B35/622
CPCC04B35/16C04B35/622C04B38/009C04B2235/3217C04B2235/349C04B2235/6562C04B2235/6567C10L5/445C10L9/10C10L2290/02C10L2290/08C10L2290/28Y02E50/10Y02E50/30
Inventor 严晓武
Owner 合肥市晶谷农业科技开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap