Efficient composite powder grinding aid and preparation method thereof
A compound type, grinding aid technology, applied in the cement field, can solve the problems of grinding aid failure and inconvenient use of cement, and achieve the effect of low cost, good grinding aid effect and stable quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0019] Example 1
[0020] A high-efficiency composite powder grinding aid, comprising the following parts by weight of raw materials: 0.8 parts of triethanolamine, 1 part of polyol, 0.3 parts of sodium thiocyanate, 0.8 parts of PC water reducer stock solution, 0.3 parts of sodium hydroxide and steel slag 94 copies. The polyol uses a mixture of pentaerythritol and trimethylolethane.
[0021] The specific steps of the preparation method of the high-efficiency composite powder grinding aid are as follows:
[0022] Step 1: Add triethanolamine, polyol and PC water reducer stock solution to the stirring tank in sequence and fully mix and react for 2 hours to obtain a mixed solution;
[0023] Step 2: The steel slag, sodium hydroxide and sodium thiocyanate are thoroughly mixed and then added to the mixed solution, mixed evenly to obtain the finished product.
Example Embodiment
[0024] Example 2
[0025] A high-efficiency composite powder grinding aid, comprising the following parts by weight of raw materials: 1 part of triethanolamine, 1.2 parts of polyol, 0.4 parts of sodium thiocyanate, 1 part of PC water reducer stock solution, 0.4 parts of sodium hydroxide and steel slag 96 copies. The polyol uses a mixture of pentaerythritol, glycerin, trimethylolethane and xylitol. The grain size of steel slag is 0.25 mm. The mass fraction of PC water reducing agent stock solution is 35%.
[0026] The specific steps of the preparation method of the high-efficiency composite powder grinding aid are as follows:
[0027] Step 1: Add triethanolamine, polyol and PC water reducer stock solution to the stirring tank in sequence and fully mix and react for 2 hours to obtain a mixed solution;
[0028] Step 2: The steel slag, sodium hydroxide and sodium thiocyanate are fully mixed and then added to the mixed solution, mixed uniformly, and the mixing speed is 75 rpm, and the f...
Example Embodiment
[0029] Example 3
[0030] A high-efficiency composite powder grinding aid, comprising the following parts by weight of raw materials: 1.5 parts of triethanolamine, 1.8 parts of polyol, 0.6 parts of sodium thiocyanate, 1.5 parts of PC water reducer stock solution, 0.4 parts of sodium hydroxide and steel slag 97.5 copies. The polyol uses pentaerythritol. The mass fraction of PC water reducing agent stock solution is 35%.
[0031] The specific steps of the preparation method of the high-efficiency composite powder grinding aid are as follows:
[0032] Step 1: Add triethanolamine, polyol and PC water reducer stock solution to the stirring tank in sequence and fully mix and react for 2 hours to obtain a mixed solution;
[0033] Step 2: The steel slag, sodium hydroxide and sodium thiocyanate are thoroughly mixed and then added to the mixed solution, mixed evenly to obtain the finished product.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap