A kind of electrolyte and battery

An electrolyte and battery technology, applied in the field of energy storage materials, can solve the problems of the cycle performance and storage performance to be improved, and achieve the effects of good high temperature and high pressure cycle performance and storage performance, inhibiting oxidation, and reducing battery gas production.

Active Publication Date: 2020-10-02
CONTEMPORARY AMPEREX TECH CO
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still many deficiencies in the above-mentioned electrolyte system. For example, under high voltage and high temperature conditions, the cycle performance and storage performance of the above-mentioned electrolyte system need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of electrolyte and battery
  • A kind of electrolyte and battery
  • A kind of electrolyte and battery

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0180] (1) Preparation of the compound of general formula I-1:

[0181] Its reaction equation is:

[0182]

[0183] The specific preparation process is:

[0184] 1. Add the P-2 aqueous solution with a concentration of 30-40% to the raw material P-1 dropwise within 20-60 minutes and stir rapidly. After the dropwise addition, stir rapidly for 15-30 hours, and stir in an oil bath at 70-90°C for 3-5 hours under reflux. A colorless fuming viscous liquid intermediate product I-1-1 was obtained;

[0185] 2. Continue to join K 2 CO 3 , KI, anhydrous acetonitrile; stir quickly to form a solid-liquid mixed phase, quickly add raw material P-3 at 40-60°C, continue stirring for 10-20h, then cool to room temperature, separate and purify to obtain the compound shown in formula I-1.

[0186] (two) preparation of general formula I-2 compound:

[0187] Its reaction equation is:

[0188]

[0189] The specific preparation process is:

[0190] Anhydrous sodium carbonate, raw material ...

Synthetic example 1

[0197]

[0198] 1. Add 37% formaldehyde aqueous solution dropwise to 1,3-propylenediamine within 0.5h and stir rapidly. After the dropwise addition, stir rapidly for 20h, then reflux and stir in an oil bath at 80°C for 4h to obtain a colorless fuming viscous liquid intermediate product Hexahydropyrimidine;

[0199] 2. Continue to join K 2 CO 3 , KI, anhydrous acetonitrile; stir quickly to form a solid-liquid mixed phase, add β-chloropropionitrile within 0.5h at 60°C, continue stirring for 17h, cool to room temperature, separate and purify to obtain the compound of formula A2.

[0200] Carbon NMR spectrum such as figure 1 shown.

Synthetic example 2

[0202]

[0203] Anhydrous sodium carbonate, piperazine and β-chloropropionitrile were mixed in absolute ethanol, and the reaction was stirred for 4h. The crude product was obtained by washing with hot ethanol several times, and recrystallized to obtain the compound of formula A8.

[0204] Carbon NMR spectrum such as figure 2 shown.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application relates to the field of energy storage materials, specifically, to an electrolyte and a battery using the electrolyte. The electrolyte contains additives, and the additives are selected from formula I-1, formula I-2 or formula I-3. At least one of polynitrile-based six-membered nitrogen heterocyclic compounds. The electrolyte of the present application can effectively passivate the surface activity of the positive electrode material by adding a polynitrile-based six-membered nitrogen heterocyclic compound as an additive, and inhibit its oxidation to the electrolyte. The battery using the electrolyte of the present application has better high temperature High-voltage cycle performance and storage performance, while reducing battery gas production.

Description

technical field [0001] The present application relates to the field of energy storage materials, in particular, to an electrolyte and a battery using the electrolyte. Background technique [0002] Lithium-ion batteries are widely used in electric vehicles and consumer electronics due to their advantages such as high energy density, high output power, long cycle life and low environmental pollution. The current demand for lithium-ion batteries is: high voltage, high power, long cycle life, long storage life and excellent safety performance. [0003] Lithium-ion batteries are currently widely used in an electrolyte system using lithium hexafluorophosphate as a conductive lithium salt and cyclic carbonate and / or chain carbonate as a solvent. However, there are still many deficiencies in the above-mentioned electrolyte system, for example, under the condition of high voltage and high temperature, the cycle performance and storage performance of the above-mentioned electrolyte s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/0567H01M10/42H01M10/0525
CPCH01M10/0525H01M10/0567H01M10/4235H01M2300/0025Y02E60/10
Inventor 伊天成胡春华郝莉湛英杰梁成都
Owner CONTEMPORARY AMPEREX TECH CO
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com