Wood board for steaming room and preparation method of wood board
A room-use, wood-based technology, applied in the field of sweat steam room, can solve the problems of air pollution, paint adhesion and light curing ability weakening, inconvenient use, etc., to meet the needs of use, the preparation process is simple, and the effect of promoting metabolism
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] A wooden board for a sweat steaming room, comprising the following raw materials in parts by weight: 5.2 parts of fructooligosaccharide, 16.3 parts of tourmaline powder, 30.6 parts of wood powder, 15.4 parts of straw powder, 9.4 parts of epoxy resin powder, 6.8 parts of low density polyethylene 3.4 parts of negative ion powder, 4.4 parts of zinc stearate, 38 parts of cyclohexanol, 3.3 parts of coupling agent, 14.2 parts of diatomaceous earth, 5.6 parts of crystal salt and 8.2 parts of slag. Straw powder includes a mixture of rice straw powder, soybean straw powder and sorghum straw powder.
[0021] The preparation method of the wooden board for the sweat steaming room, the specific steps are as follows:
[0022] Step 1, calcining tourmaline powder, negative ion powder, crystal salt and slag at 580 degrees Celsius for 90 minutes, and then mixing them uniformly to obtain the first mixture;
[0023] Step 2, heating epoxy resin powder and low-density polyethylene to a molt...
Embodiment 2
[0027] A wooden board for a sweat steam room, comprising the following raw materials in parts by weight: 6.3 parts of fructooligosaccharide, 17.4 parts of tourmaline powder, 32.5 parts of wood powder, 17.6 parts of straw powder, 9.9 parts of epoxy resin powder, 8.4 parts of low density polyethylene 3.9 parts of negative ion powder, 5.1 parts of zinc stearate, 38.8 parts of cyclohexanol, 3.9 parts of coupling agent, 15.2 parts of diatomaceous earth, 6.3 parts of crystal salt and 9.1 parts of slag. The particle size of the slag is 0.24mm, and the particle size of the anion powder and tourmaline powder are both 880nm.
[0028] The preparation method of the wooden board for the sweat steaming room, the specific steps are as follows:
[0029] Step 1, calcining tourmaline powder, negative ion powder, crystal salt and slag at 720 degrees Celsius for 90 minutes, and then mixing them uniformly to obtain the first mixture;
[0030] Step 2, heating epoxy resin powder and low-density pol...
Embodiment 3
[0034] A wooden board for a sweat steaming room, comprising the following raw materials in parts by weight: 7.3 parts of fructooligosaccharide, 18.9 parts of tourmaline powder, 34.7 parts of wood powder, 20.6 parts of straw powder, 10.6 parts of epoxy resin powder, and 10.8 parts of low-density polyethylene 5.2 parts of negative ion powder, 6 parts of zinc stearate, 40.8 parts of cyclohexanol, 4.3 parts of coupling agent, 16.1 parts of diatomaceous earth, 7.7 parts of crystal salt and 9.9 parts of slag. The relative molecular weight of FOS is 480-660. Straw powder includes a mixture of rice straw powder and sorghum straw powder.
[0035] The preparation method of the wooden board for the sweat steaming room, the specific steps are as follows:
[0036] Step 1, calcining tourmaline powder, negative ion powder, crystal salt and slag at 720 degrees Celsius for 96 minutes, and then mixing them uniformly to obtain the first mixture;
[0037] Step 2, heating epoxy resin powder and ...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com