Wear-resistant and temperature-resistant organic coating material and preparation method thereof

An organic coating and high-temperature-resistant technology, applied in the mechanical field, can solve problems such as insufficient performance and unfavorable processing of ceramic materials, and achieve excellent high-temperature resistance and wear resistance, toughness and superplasticity.

Inactive Publication Date: 2019-01-11
徐州台力福数控科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional ceramic materials are relatively brittle, and without further processing of ceramic materials, the performance of ceramic materials in many fields is slightly insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A wear-resistant and high-temperature resistant organic coating material is composed of the following components in parts by mass:

[0025] (1) Ta 2 o 5 2 parts; (2) 3 parts of nano-thorium dioxide; (3) 4 parts of magnesium hydroxide; (4) 10 parts of aluminate cement; (5) 12 parts of aluminum silicate fiber; (6) 20 parts of glass fiber powder .

[0026] According to the preparation method of the wear-resistant and high-temperature resistant organic coating material provided by the present invention, the above-mentioned wear-resistant and high-temperature resistant organic coating material is prepared, and the preparation steps are as follows:

[0027] (1) Weighing: Accurately weigh each component;

[0028] (2) Grinding: Mix the components together, stir well, and put them into a grinder for grinding;

[0029] (3) Calcination: Put the mixture obtained in step (2) into a mold and perform high-temperature calcination at a temperature of 1000°C and a pressure of 3GPa fo...

Embodiment 2

[0032] A wear-resistant and high-temperature resistant organic coating material is composed of the following components in parts by mass:

[0033] (1) Ta 2 o 5 3 parts; (2) 6 parts of nano-thorium dioxide; (3) 5 parts of magnesium hydroxide; (4) 15 parts of aluminate cement; (5) 15 parts of aluminum silicate fiber; (6) 22 parts of glass fiber powder .

[0034] According to the preparation method of the wear-resistant and high-temperature resistant organic coating material provided by the present invention, the above-mentioned wear-resistant and high-temperature resistant organic coating material is prepared, and the preparation steps are as follows:

[0035] (1) Weighing: Accurately weigh each component;

[0036] (2) Grinding: Mix the components together, stir well, and put them into a grinder for grinding;

[0037] (3) Calcination: Put the mixture obtained in step (2) into a mold and perform high-temperature calcination at a temperature of 1350°C and a pressure of 5GPa fo...

Embodiment 3

[0040] A wear-resistant and high-temperature resistant organic coating material is composed of the following components in parts by mass:

[0041] (1) Ta 2 o 5 5 parts; (2) 10 parts of nano-thorium dioxide; (3) 6 parts of magnesium hydroxide; (4) 20 parts of aluminate cement; (5) 18 parts of aluminum silicate fiber; (6) 25 parts of glass fiber powder .

[0042] According to the preparation method of the wear-resistant and high-temperature resistant organic coating material provided by the present invention, the above-mentioned wear-resistant and high-temperature resistant organic coating material is prepared, and the preparation steps are as follows:

[0043] (1) Weighing: Accurately weigh each component;

[0044] (2) Grinding: Mix the components together, stir well, and put them into a grinder for grinding;

[0045] (3) Calcination: Put the mixture obtained in step (2) into a mold and perform high-temperature calcination at a temperature of 1550°C and a pressure of 9GPa f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a wear-resistant and temperature-resistant resistant organic coating material and a preparation method thereof, which relate to the technical field of machinery. The coating material consists of the following components in parts by mass: (1) 15 to 30 parts of silicon carbide; (2) 3 to 9 parts of nano-nickel oxide and 6 to 12 parts of nano-magnesium oxide; (3) 15 to 23 parts of nano-Al2O3; (4) 2.5 to 4 parts of Ta2O5; (5) 25 to 45 parts of silica; (6) 4.5 to 7.5 parts of titanium oxide; and (7) 5 to 15 parts of nano thorium dioxide. The wear-resistant and high temperature-resistant organic coating material provided by the invention utilizes a nano material technology to modify the existing coating materials, so that the strength, toughness and superplasticity of thematerial are greatly improved. The wear-resistant and temperature-resistant organic coating material and a coating provided by the preparation method have excellent high temperature resistance and wear resistance, and the coating can be used as the coating material.

Description

technical field [0001] The invention belongs to the technical field of machinery, and in particular relates to a wear-resistant and high-temperature-resistant organic coating material with excellent high-temperature resistance and wear-resistant performance and a preparation method thereof. Background technique [0002] In the field of mechanical processing, when processing tools such as machine tools, they are affected by the debris of the workpiece itself or high-temperature environmental factors, especially when industrial liquids such as cutting fluids are used, they often erode the processing tools and affect the processing of the processing tools. Accuracy and service life have adverse effects on machining. Therefore, surface coating treatment for processing tools can effectively overcome this problem. [0003] In recent years, coating materials have developed rapidly, especially ceramic coating materials, which have received widespread attention. Unlike traditional co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More