A method for treating mercury tailings by oxidation leaching

A technology for leaching and tailings, applied in the fields of metallurgy and environmental protection, can solve the problems of difficulty in large-scale application, high cost, and high processing cost, and achieve the effects of reducing disposal costs, fast leaching, and low operating costs.

Active Publication Date: 2020-09-22
NORTHEASTERN UNIV LIAONING
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, mercury-containing solid waste is mostly treated by fire distillation, and mercury is cooled and recovered from the flue gas; however, fire distillation requires high temperature operation, and for safety and environmental protection considerations, the flue gas needs to be strictly purified and dust collected. The overall cost is high; for a large amount of mercury-containing tailings that have been stockpiled in the past, the treatment cost of fire distillation is high, and it is difficult to apply on a large scale

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Oxidant TCCA and pH adjuster hydrochloric acid are dissolved in water, make leaching solution, the concentration of TCCA in the leaching solution is 0.5g / L, and the concentration of HCl is 3g / L;

[0026] The mercury tailings used are the flotation tailings obtained by the flotation process of mercury mines. The mercury content is 118g / t, and 87.4% of the particles are smaller than 150μm. The main gangue components are quartz and dolomite. Mercury exists in the form of cinnabar. Grinding is required;

[0027] Put the mercury tailings in the leaching solution, leaching under stirring conditions, the leaching time is 10min, and the leaching material is obtained after the leaching is completed; the amount of mercury tailings added in each liter of leaching solution is 0.4kg, that is, 1kg of mercury tailings is placed in In 2.5L leaching solution;

[0028] Filter the leached material to separate the leached residue and the leached liquid; the leached residue is a mercury-re...

Embodiment 2

[0032] Method is with embodiment 1, and difference is:

[0033] (1) The concentration of TCCA in the leaching solution is 1g / L, and the concentration of HCl is 3.5g / L; the mercury tailings used are the flotation tailings obtained by the mercury mine flotation process, and the mercury content is 187g / t, 83.5 % of the particles are less than 150μm, the main gangue components are quartz and dolomite, mercury exists in the form of cinnabar, and does not need to be ground;

[0034] (2) The leaching time is 15 minutes; the leaching residue contains 0.03mg / L of mercury, and the leaching solution contains 71.6mg / L of mercury as measured by the toxicity leaching test, and the leaching rate of mercury reaches 95.7%;

[0035] (3) Ferrous sulfide is 40% of the total mass of TCCA, and the precipitation reaction time is 35 minutes; the solid content in the precipitation contains 18.7% mercury by mass percentage, and the precipitation rate of mercury is greater than 99%.

Embodiment 3

[0037] Method is with embodiment 1, and difference is:

[0038] (1) The concentration of TCCA in the leaching solution is 1.5g / L, and the concentration of HCl is 4.5g / L; the mercury tailings used are the flotation tailings obtained by the mercury mine flotation process, and the mercury content is 306g / t. 71.0% of the particles are smaller than 150μm, the main gangue components are quartz and dolomite, mercury exists in the form of cinnabar, and does not need to be ground;

[0039] (2) The leaching time is 15 minutes; the addition amount of mercury tailings in each liter of leaching solution is 0.2kg, that is, 1kg of mercury tailings is placed in 5L of leaching solution; Mercury content is 57.2mg / L, and the mercury leaching rate reaches 93.4%;

[0040] (3) Ferrous sulfide is 25% of the total mass of TCCA, and the precipitation reaction time is 40 minutes; the solid content in the precipitation contains 17.1% mercury by mass percentage, and the precipitation rate of mercury is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for treating mercury tailings by oxidative leaching, which is carried out according to the following steps: (1) Dissolve TCCA and hydrochloric acid in water to prepare a leaching solution; (2) Place the mercury tailings in the leaching solution and proceed under stirring conditions Leaching; (3) Filter the leaching material to separate the leaching residue and leaching liquid; add the precipitating agent ferrous sulfide to the leaching liquid, and then perform a precipitation reaction under stirring conditions. The material after the precipitation reaction is left to stand and filtered to separate out the precipitate. and filtrate. The method of the present invention does not require grinding or heating of materials, effectively reduces the disposal cost of mercury tailings, a hazardous waste, and reduces potential harm to the environment; at the same time, the operating conditions are mild, and the mercury leaching speed is fast and efficient. It has the advantages of low energy consumption, small reagent consumption and low operating cost.

Description

technical field [0001] The invention belongs to the technical field of metallurgy and environmental protection, and in particular relates to a method for treating mercury tailings by oxidation leaching. Background technique [0002] Mercury is the only liquid metal at normal temperature, and it mainly exists in the form of metallic mercury, inorganic mercury and organic mercury compounds in nature; mercury is persistent, easy to migrate and highly bioaccumulative, and highly toxic; While mercury and mercury-containing resources are widely used, a large amount of mercury enters the environment with human activities, and the environmental pollution caused by mercury pollution has gradually attracted people's attention. [0003] Since August 2017, the Mercury Convention has officially entered into force in China. China has clearly banned the mining of new primary mercury mines, but the mercury tailings left over from historical mining still have potential environmental pollutio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More