Insulating material for cable joint and preparation method thereof

A technology for insulating materials and cable joints, which is applied to organic insulators, plastic/resin/wax insulators, etc., can solve the problem that insulating materials cannot have both insulation properties, etc., and achieves low production cost, enhanced weather resistance, adhesion and insulation. good effect

Inactive Publication Date: 2019-01-18
贵州安众成电线电缆有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the existing insulating materials used for cable joints mainly include EPDM rubber, silicone rubber, epoxy resin and polyethylene, etc., and through continuous development of materials, all three can meet the general performance of cable joints, but now Some insulating materials cannot have good insulation, high temperature resistance, corrosion resistance and low temperature cold resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An insulating material for cable joints, the insulating material comprises the following raw materials in parts by weight: 60 parts of epoxy resin, 25 parts of polyvinyl chloride, 15 parts of curing agent, 15 parts of zeolite powder, and 10 parts of silicone resin , 10 parts of plasticizer, 8 parts of phenolic resin, 6 parts of asbestos powder, 6 parts of preservative, 5 parts of cellulose, 4 parts of silicon carbide, 3 parts of stabilizer, 2 parts of additive and 1 part of antioxidant. Wherein the curing agent adopts m-xylylenediamine, the plasticizer adopts dibutyl phthalate, the preservative adopts dehydroacetic acid, and the cellulose adopts hydroxypropyl methylcellulose, and the The stabilizer adopts calcium-zinc stabilizer, the additive adopts high-density polyethylene, and the antioxidant adopts thiobisphenol antioxidant.

[0033] The preparation method of the above-mentioned insulating material comprises the steps of:

[0034] (1) Weigh each raw material accord...

Embodiment 2

[0039]An insulating material for cable joints, the insulating material comprises the following raw materials in proportion by weight: 65 parts of epoxy resin, 28 parts of polyvinyl chloride, 19 parts of curing agent, 17 parts of zeolite powder, and 12 parts of silicone resin , 12 parts of plasticizer, 10 parts of phenolic resin, 8 parts of asbestos powder, 8 parts of preservative, 7 parts of cellulose, 6 parts of silicon carbide, 4 parts of stabilizer, 3 parts of additive and 1 part of antioxidant. Wherein the curing agent adopts m-xylylenediamine, the plasticizer adopts dibutyl phthalate, the preservative adopts dehydroacetic acid, and the cellulose adopts hydroxypropyl methylcellulose, and the The stabilizer adopts calcium-zinc stabilizer, the additive adopts high-density polyethylene, and the antioxidant adopts thiobisphenol antioxidant.

[0040] The preparation method of the above insulating material is the same as that of Example 1.

Embodiment 3

[0042] An insulating material for cable joints, the insulating material comprises the following raw materials in parts by weight: 70 parts of epoxy resin, 30 parts of polyvinyl chloride, 22 parts of curing agent, 18 parts of zeolite powder, and 13 parts of silicone resin , 13 parts of plasticizer, 11 parts of phenolic resin, 9 parts of asbestos powder, 9 parts of preservative, 8 parts of cellulose, 7 parts of silicon carbide, 5 parts of stabilizer, 3 parts of additive and 1 part of antioxidant. Wherein the curing agent adopts m-xylylenediamine, the plasticizer adopts dibutyl phthalate, the preservative adopts dehydroacetic acid, and the cellulose adopts hydroxypropyl methylcellulose, and the The stabilizer adopts calcium-zinc stabilizer, the additive adopts high-density polyethylene, and the antioxidant adopts thiobisphenol antioxidant.

[0043] The preparation method of the above insulating material is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical insulatoraaaaaaaaaa
Login to view more

Abstract

The invention discloses an insulating material for a cable joint and a preparation method thereof. The insulating material is prepared from the following raw materials in parts by weight: 60-80 partsof epoxy resin, 25-35 parts of polyvinyl chloride, 15-25 parts of a curing agent, 15-20 parts of zeolite powder, 10-15 parts of silicone resin, 10-15 parts of a plasticizer, 8-14 parts of phenolic resin, 6-12 parts of asbestos powder, 6-12 parts of a preservative, 5-10 parts of cellulose, 4-9 parts of silicon carbide, 3-7 parts of a stabilizer, 2-5 parts of an additive and 1-3 parts of an antioxidant. The insulating material prepared by the method has good corrosion resistance, high-temperature resistance, good adhesive property and insulating property, good strength and toughness and low-temperature cold resistance, and the flame retardant property of the insulating material reaches V0 grade. The insulating material is quite low in manufacturing cost, and can meet the insulating demand onan existing cable joint.

Description

technical field [0001] The invention relates to the technical field of cable manufacturing, in particular to an insulating material used for cable joints and a preparation method thereof. Background technique [0002] Wires and cables are important materials for electric power and telecommunications. Cable fireproof coatings are suitable for flame retardant treatment of wires and cables in power plants, industrial and mining, telecommunications and civil buildings, and can also be used for combustible substrates in wood structures, metal structures and underground projects. Fire protection of other objects. The cable joint is connected in the middle or terminal of the cable, and connects the segmented cables into a whole connection device, which is used to lock and fix the incoming and outgoing lines, so as to keep the cable sealed and the line smooth, so as to ensure the normal operation of the cable. [0003] At present, the existing insulating materials used for cable jo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L27/06C08L83/04C08L61/06C08L1/28C08L23/06C08K13/04C08K7/12C08K3/34C08K5/12H01B3/40
CPCC08L63/00C08L2201/02C08L2201/08C08L2203/202C08L2205/035C08L2207/062H01B3/40C08L27/06C08L83/04C08L61/06C08L1/284C08L23/06C08K13/04C08K7/12C08K3/34C08K5/12
Inventor 李铁钉
Owner 贵州安众成电线电缆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap