A kind of preparation method of single crystal ternary cathode material

A cathode material and single crystal technology, which is applied in the field of single crystal ternary cathode material preparation, can solve the problems of structural lithium extraction, excessive by-product gas, increase experimental complexity, etc., and achieve thermal stability improvement, capacity and voltage improvement. , the effect of improving the electrochemical performance

Active Publication Date: 2021-04-27
CNGR ADVANCED MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, "A Preparation Method of High Voltage Single Crystal Lithium-ion Ternary Cathode Material" with application number 201711173950 and "A Doped Micron-scale Single Crystal Ternary Cathode Material and Its Preparation Technology" with application number 201610443127 In the preparation method disclosed in the Chinese patent, there are many by-product gases in the preparation process, and the annealing temperature is too high, which will easily cause the structural lithium to come out and cause too much residual lithium on the surface of the structure, etc., and the steps are complicated.
At present, there is still a preparation scheme, such as the Chinese patent of "Single Crystal Ternary Cathode Material and Its Preparation Method and Lithium-ion Battery" with application number 201710652580, which discloses the use of lithium source and nickel-cobalt-manganese source in the complexing agent Co-precipitation increases the difficulty of the precursor process; and the preparation of the precursor depends on the one-step or multi-step mixing of lithium salts, which also increases the complexity of the experiment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of single crystal ternary cathode material
  • A kind of preparation method of single crystal ternary cathode material
  • A kind of preparation method of single crystal ternary cathode material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] A method for preparing a single crystal ternary positive electrode material, comprising the following steps:

[0029] S1: Mix lithium oxide with three oxides of nickel, cobalt and manganese in proportion and ball mill; the mass ratio of Li:Ni:Co:Mn is (1.02~1.12):(0.75~0.95):(0.01~0.10): (0.02~0.20), the high nickel content ensures that the capacity of the positive electrode material is high enough. Nickel oxides are NiO, Ni 3 o 4 , NiO 2 、Ni 2 o 3 At least one of the cobalt oxides is Co 3 o 4 、CoO 2 、Co 2 o 3 At least one of the manganese oxides is MnO, Mn 3 o 4 , MnO 2 , Mn 2 o 3 at least one of the During the implementation process, the mass ratio of ball to material used in ball milling is (1~3):1, the speed of ball mill is between 150~250 rpm, and the milling time is 1~4h. The material can be fully mixed evenly, and the particle size of the material after ball milling is 0.5 μm to 3 μm, which is easier to form a new single crystal structure.

[003...

Embodiment 1

[0035] NiO, Co 2 o 3 , Mn 2 o 3 and Li 2 O was mixed and ball milled in proportion; where the molar ratio of Li:Ni:Co:Mn was 1.08:0.84:0.03:0.13. During the implementation process, the mass ratio of ball to material used in the ball mill was 3:1, the speed of the ball mill was 175rpm, and the ball milling time was 3h. The ball-milled product was sintered in an air atmosphere, specifically, the temperature was raised to 490° C. at a rate of 3° C. / min and then kept for 6 hours. Then sinter in an oxygen atmosphere, specifically, the temperature is raised to 750° C. at a rate of 3° C. / min and then kept for 20 hours. Finally, it was naturally cooled to room temperature to obtain a composition of LiNi 0.84 co 0.03 mn 0.13 o 2 single crystal ternary cathode material.

example 2

[0037] NiO, Co 3 o 4 , Mn 3 o 4 and Li 2O was mixed and ball milled in proportion; where the molar ratio of Li:Ni:Co:Mn was 1.06:0.90:0.03:0.07. During the implementation process, the mass ratio of ball to material used in the ball mill was 2.5:1, the speed of the ball mill was 210rpm, and the ball milling time was 4h. The ball-milled product was sintered in an oxygen atmosphere, specifically, the temperature was raised to 550° C. at a rate of 3° C. / min and then kept for 5 hours. Then sintering under an oxygen atmosphere, specifically, the temperature was raised to 730° C. at a rate of 3° C. / min and then kept for 20 hours. Finally, it was naturally cooled to room temperature to obtain a composition of LiNi 0.90 co 0.03 mn 0.07 o 2 single crystal ternary cathode material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a single crystal ternary positive electrode material in the technical field of lithium ion batteries, which comprises mixing and ball milling lithium oxide and three oxides of nickel, cobalt and manganese in proportion; The first sintering is carried out at ℃; the product after the first sintering is then sintered at 650-780°C for the second time; finally, it is naturally cooled to room temperature to obtain a single crystal ternary cathode material. The present invention directly uses oxides as raw materials, avoiding the phenomenon of gas generation when hydroxides or carbonates are used as raw materials, thereby greatly improving the consistency of the atmosphere, the stability of heat and the cracking of structures; the present invention also By directly mixing lithium oxide with nickel, cobalt, and manganese oxides, it can be mixed evenly. The particle size of the sintered raw material is small, and the elements are evenly mixed, which provides the conditions for forming single crystal at a lower temperature.

Description

technical field [0001] The invention relates to the technical field of lithium ion batteries, in particular to a method for preparing a single crystal ternary positive electrode material. Background technique [0002] Lithium-ion batteries have great prospects for application in new energy vehicles due to their high capacity, low pollution, and high power. The ternary nickel-cobalt lithium manganese oxide has a good development as the positive electrode of lithium-ion batteries due to its strong comprehensive performance. space. The mainstream structure of the currently prepared ternary nickel cobalt lithium manganese oxide is still secondary particles of different particle sizes, and its performance under high magnification and high working voltage is still not ideal, because the structure consistency and stability of the secondary particles sex is relatively poor. Synthesizing ternary cathode materials with a single crystal structure is a good solution, but the current m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/525
CPCC01G53/006C01P2004/03C01P2006/11C01P2006/12C01P2006/40H01M4/505H01M4/525H01M10/0525Y02E60/10
Inventor 管剑訚硕罗标刘辉
Owner CNGR ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap