Plastic for effectively inhibiting breeding of bacteria and preparation method of plastic

A technology for inhibiting bacteria and plastics, which is applied in the field of plastics that effectively inhibit the growth of bacteria and its preparation, to achieve the effects of improving quality, improving safety, and preventing flammability

Inactive Publication Date: 2019-02-05
ANHUI GUOTAI PACKING PRINTING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in daily life, a considerable number of harmful bacteria exist and multi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A plastic that effectively inhibits the growth of bacteria comprises the following raw materials in parts by weight:

[0019] 90 parts of polypropylene, 4 parts of metallocene polyethylene, 3 parts of epoxy soybean oil, 4 parts of stearyl alcohol, 2 parts of vinyltriethoxysilane, 2 parts of nano zirconium phosphate, 3 parts of corn straw fiber, 3 parts of seaweed fiber 1 part, 2 parts of bitter almond oil, 3 parts of nano palygorskite, 10 parts of antibacterial agent, 1 part of antimony trioxide, 1 part of potassium sorbate.

[0020] The antibacterial agent is composed of chitosan, silver-loaded zeolite and nanometer copper powder with a mass ratio of 1:3:4.

[0021] The preparation method of the above-mentioned plastics that can effectively inhibit the growth of bacteria is to weigh each raw material according to the proportion, mix, melt and knead, and extrude and granulate.

Embodiment 2

[0023] A plastic that effectively inhibits the growth of bacteria comprises the following raw materials in parts by weight:

[0024] 102 parts of polypropylene, 5 parts of metallocene polyethylene, 4 parts of epoxy soybean oil, 5 parts of stearyl alcohol, 3 parts of vinyltriethoxysilane, 3 parts of nano zirconium phosphate, 4 parts of corn straw fiber, 5 parts of seaweed fiber 3 parts of bitter almond oil, 5 parts of nano palygorskite, 12 parts of antibacterial agent, 2 parts of antimony trioxide, and 2 parts of potassium sorbate.

[0025] The antibacterial agent is composed of chitosan, silver-loaded zeolite and nanometer copper powder with a mass ratio of 1:4:3.

[0026] The preparation method of the above-mentioned plastics that can effectively inhibit the growth of bacteria is to weigh each raw material according to the proportion, mix, melt and knead, and extrude and granulate.

Embodiment 3

[0028] A plastic that effectively inhibits the growth of bacteria comprises the following raw materials in parts by weight:

[0029] 110 parts of polypropylene, 6 parts of metallocene polyethylene, 5 parts of epoxy soybean oil, 7 parts of stearyl alcohol, 4 parts of vinyltriethoxysilane, 4 parts of nano zirconium phosphate, 6 parts of corn straw fiber, 6 parts of seaweed fiber 5 parts of bitter almond oil, 6 parts of nano palygorskite, 16 parts of antibacterial agent, 3 parts of antimony trioxide, and 3 parts of potassium sorbate.

[0030] The antibacterial agent is composed of chitosan, silver-loaded zeolite and nanometer copper powder with a mass ratio of 1:5:2.

[0031] The preparation method of the above-mentioned plastics that can effectively inhibit the growth of bacteria is to weigh each raw material according to the proportion, mix, melt and knead, and extrude and granulate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to plastic for effectively inhibiting the breeding of bacteria. The plastic is prepared from the following raw materials in parts by weight: 90 to 110 parts of polypropylene, 4 to 6 parts of metallocene polyethylene, 3 to 5 parts of epoxidized soybean oil, 5 to 7 parts of octadecanol, 2 to 4 parts of triethoxyvinylsilane, 2 to 4 parts of nano zirconium phosphate, 3 to 6 partsof corn straw fiber, 3 to 6 parts of seaweed fiber, 2 to 5 parts of bitter almond oil, 3 to 6 parts of nano palygorskite, 10 to 16 parts of an antibacterial agent, 1 to 3 parts of a flame retardant and 1 to 3 parts of a preservative. The plastic provided by the invention has good comprehensive performance; antimony trioxide is used as the flame retardant so that the disadvantage that the plasticis combustible in an application process is prevented and the safety of the plastic is improved. The antibacterial agent composed of chitosan, silver-loaded zeolite and nano copper powder is added torealize the effect of inhibiting or killing the bacteria, so that the breeding of the bacteria is avoided and the quality of the plastic is further improved.

Description

technical field [0001] The invention relates to a plastic and a preparation method thereof, in particular to a plastic which can effectively inhibit bacterial growth and a preparation method thereof. Background technique [0002] Toys play an important role in children's lives, and toys are children's friends. Plastics used to make toys must be safe, healthy and non-toxic. But in daily life, quite a few harmful bacteria exist and multiply on the surface of plastic products, and cause various diseases through contact. As people's awareness of health and environmental protection continues to increase, there is a demand for "bacteriostasis and sterilization" for toy plastic parts that are frequently in contact with in daily life. Contents of the invention [0003] The object of the present invention is to provide a plastic that effectively inhibits the growth of bacteria and a preparation method thereof. [0004] In order to achieve the above object, the present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/06C08L91/00C08L97/02C08L5/08C08L5/00C08K13/06C08K9/12C08K3/08C08K3/22
CPCC08K2003/0806C08K2003/085C08K2201/011C08L23/12C08L2201/02C08L2205/02C08L2205/025C08L2205/035C08L2205/16C08L23/06C08L91/00C08L97/02C08L5/08C08L5/00C08K13/06C08K9/12C08K3/08C08K3/2279
Inventor 焦国平
Owner ANHUI GUOTAI PACKING PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap