Preparation method of wearproof, acidproof and non-toxic artificial transplanted article film

An implant and artificial technology, applied in the direction of coating, metal material coating process, ion implantation plating, etc., can solve the problem of "three-body" wear and other problems, achieve the effect of reducing thermal stress, improving stability, and inhibiting interface corrosion

Active Publication Date: 2019-02-19
FUJIAN UNIV OF TECH
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the long-term service in the body of the prosthesis modified by the DLC film surface, the corrosion medium (such as Cl － 、PO4 3－ ) reaches the film / metal matrix interface through the pores of the DLC film, corrodes the interface layer, and causes the diamond-like film to peel off, and the film fragments produced at the same time will cause severe "three-body" wear and accelerate the failure of the artificial joint prosthesis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of wearproof, acidproof and non-toxic artificial transplanted article film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1, a method for preparing a wear-resistant, acid-resistant and non-toxic artificial graft film layer, the film layer includes a bonding layer, a transition layer and a surface layer sequentially arranged on the surface of the friction partner of the artificial graft from the inside to the outside, The bonding layer is a nickel-titanium layer, the transition layer is a titanium-doped diamond-like layer with zirconium elements, and the surface layer is a zirconium-doped diamond-like layer;

[0018] The preparation method comprises the following steps:

[0019] 1) Forming of the adhesive layer: using the metal-metal artificial implant as the substrate, the nickel target and the titanium target are sputter-deposited on the surface of the artificial implant friction partner by magnetron sputtering to form an adhesive bond. Layer coating, and then use laser cladding method to melt the above adhesive layer coating, so as to form the adhesive layer;

[0020] 2) Form...

Embodiment 2

[0027] Embodiment 2, a method for preparing a wear-resistant, acid-resistant and non-toxic artificial graft film layer, the film layer includes a bonding layer, a transition layer and a surface layer sequentially arranged on the surface of the friction partner of the artificial graft from the inside to the outside, The bonding layer is a nickel-titanium layer, the transition layer is a titanium-doped diamond-like layer with zirconium elements, and the surface layer is a zirconium-doped diamond-like layer;

[0028] The preparation method comprises the following steps:

[0029] 1) Forming of the adhesive layer: using the metal-metal artificial implant as the substrate, the nickel target and the titanium target are sputter-deposited on the surface of the artificial implant friction partner by magnetron sputtering to form an adhesive bond. Layer coating, and then use laser cladding method to melt the above adhesive layer coating, so as to form the adhesive layer;

[0030] 2) Form...

Embodiment 3

[0037] Embodiment 3, a method for preparing a wear-resistant, acid-resistant and non-toxic artificial graft film layer, the film layer includes a bonding layer, a transition layer and a surface layer sequentially arranged on the surface of the friction partner of the artificial graft from the inside to the outside, The bonding layer is a nickel-titanium layer, the transition layer is a titanium-doped diamond-like layer with zirconium elements, and the surface layer is a zirconium-doped diamond-like layer;

[0038] The preparation method comprises the following steps:

[0039] 1) Forming of the adhesive layer: using the metal-metal artificial implant as the substrate, the nickel target and the titanium target are sputter-deposited on the surface of the artificial implant friction partner by magnetron sputtering to form an adhesive bond. Layer coating, and then use laser cladding method to melt the above adhesive layer coating, so as to form the adhesive layer;

[0040] 2) Form...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a wearproof, acidproof and non-toxic artificial transplanted article film. The film comprises a bonding layer, a transitional layer and a surface layersequentially arranged on the surface of an artificial transplanted article friction couple from inside to outside; and the preparation method comprises the following steps: 1, forming the bonding layer; 2, forming the transitional layer; and 3, forming the surface layer. With adoption of the preparation method, metallurgical bonding of all coatings can be precisely controlled, the coating stripping problem is solved, gradients are sequentially formed among the coatings, generation of thermal stress is reduced and the service life of a false tooth film is greatly prolonged.

Description

technical field [0001] The invention relates to the field of artificial graft film preparation, in particular to a method for preparing a wear-resistant, acid-resistant and non-toxic artificial graft film. Background technique [0002] Joint replacement is currently the most direct and effective means of treating joint diseases. With the growth of the national economy, the demand for artificial joints in our country continues to increase. The artificial joint has been successfully applied in clinical practice. Its friction pair is a (convex) head-(concave) socket structure. Through the relative movement of the joint head-joint socket, the hip joint rotation, rotation, swing and other motion modes are respectively realized to realize the function of the joint. , to replace the diseased organ of the patient. The artificial joint needs to serve in the body for a long time (more than 10 years, even more than 30 years). During the service process, the (convex) head-(concave) soc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/06C23C14/16C23C14/35C23C14/58A61L27/30
CPCA61L27/303A61L27/306A61L2420/02A61L2420/08A61L2430/24C23C14/0605C23C14/165C23C14/345C23C14/352C23C14/5813
Inventor 简明德刘成武黄卫东
Owner FUJIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com