Photocatalytic high-pressure decorative board and preparation method thereof

A technology for photocatalysis and decorative panels, applied in the field of decorative panels, can solve the problems of narrow use range, human harm, and the inability to effectively and continuously remove pollutants, and achieve the effect of wide application and safety assurance.

Active Publication Date: 2019-04-02
河南永威复合新材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem addressed by the present invention is: in the prior art, the pollution caused by indoor and outdoor decoration boards cannot be efficiently and continuously removed, and the formaldehyde, organic pollutants, bacteria, mold and other pollutants carried in the decoration process cannot be effectively removed. Continuous removal; the residence needs long-term ventilation before living, but there will still be formaldehyde, organic pollutants and other harmful substances volatilized after living, causing long-term harm to the human body; the commonly used photocatalyst titanium dioxide can only be used at specific wavelengths It is used under certain conditions, and the scope of use is very narrow, so it cannot be better applied in decoration materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photocatalytic high-pressure decorative board and preparation method thereof
  • Photocatalytic high-pressure decorative board and preparation method thereof
  • Photocatalytic high-pressure decorative board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] A composite photocatalyst, which is prepared from the following raw materials in parts by weight: 60% of meteorological titanium dioxide with a particle size of 5-10nm, 40% of hydrophilic silicon dioxide with a particle size of 10-20nm, and 40% of the above-mentioned raw materials The total mass of 0.3% tripolyindenyltriarylamine organic dyes;

[0070] The preparation method of the composite photocatalyst comprises the following steps: mixing meteorological titanium dioxide with a particle size of 5-10 nm and hydrophilic silicon dioxide with a particle size of 10-20 nm according to a mass ratio of 60:40, and mixing uniformly Finally, adding 0.3% tripolyindenyl triarylamine organic dyes and mixing uniformly to obtain a photosensitizer mixture, and then adding a 15% polyvinyl alcohol aqueous solution to the photosensitizer mixture Mix and stir evenly (the mass of the polyethylene energy-producing aqueous solution is 5 times the mass of the photosensitizer mixture), and th...

Embodiment 2

[0072] A composite photocatalyst, which is prepared from the following raw materials in parts by weight: 65% of meteorological titanium dioxide with a particle size of 5-10nm, 35% of hydrophilic silicon dioxide with a particle size of 10-20nm, and The total mass of 0.3% tripolyindenyltriarylamine organic dyes;

[0073] The preparation method of this composite photocatalyst is the same as that of Example 1.

Embodiment 3

[0075] A composite photocatalyst, which is prepared from the following raw materials in parts by weight: 70% of meteorological titanium dioxide with a particle size of 5-10nm, 30% of hydrophilic silicon dioxide with a particle size of 10-20nm, and 30% of the above-mentioned raw materials The total mass of 0.3% tripolyindenyltriarylamine organic dyes;

[0076] The preparation method of this composite photocatalyst is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a photocatalytic high-pressure decorative board and a preparation method thereof. The photocatalytic high-pressure decorative board is prepared through high-temperature and high-pressure one-time molding from a base board layer, an adhesive layer and a photocatalytic decorative layer. The photocatalytic decorative layer has a compound photocatalyst plate layer. The high-pressure decorative board has a photocatalytic function, so that the product can degrade various indoor harmful substances, such as formaldehyde and organic pollutants, generated during decoration process. The decorative board not only can avoid long-time ventilation of a newly-decorated room, but also can continuously degrade and remove the harmful substances generated from decorative materials. Thedecorative board avoids damage on human body and influence on environment due to the harmful substances generated from decorative materials and has excellent application prospect.

Description

technical field [0001] The invention belongs to the technical field of decorative plates. In particular, it relates to a photocatalytic high-voltage decorative plate and a preparation method thereof. Background technique [0002] At present, my country's interior decoration materials are mainly made of paints, coatings, soft decoration materials wallpaper, wall coverings and decorative panels. Among them, paints and coatings mostly contain volatile organic pollutants such as benzene and toluene, and heavy metals such as lead, mercury, chromium, and cadmium, which have great potential harm to the health of users or occupants, and also have great harm to the surrounding environment; Wallpapers and wall coverings have defects such as not waterproof, not moisture-proof, easy to fall off when the humidity is high, and easy to mold. Moreover, most of the glue used for pasting is a benzene solution of rubber adhesives. Volatile solvents have great harm to the human body. ; Most o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B29/00B32B29/06B32B37/06B32B37/10B32B37/12B32B38/00B32B38/08E04F13/075
CPCB32B29/005B32B29/06B32B37/06B32B37/10B32B37/12B32B38/0004B32B38/08B32B2250/26B32B2255/12B32B2255/26B32B2260/028B32B2260/046B32B2307/7145B32B2307/7265B32B2317/122B32B2317/125B32B2601/00E04F13/0866
Inventor 任太平徐明华卢泓楠刘玉秀陈佳音
Owner 河南永威复合新材料有限公司