Flame-retardant polyurethane hot melt adhesive with excellent water resistance and preparation method of hot melt adhesive

A technology of polyurethane hot-melt adhesive and flame-retardant polyether, which is applied in the field of structural adhesives, can solve the problems of reducing the waterproof performance and chemical resistance of polyurethane hot-melt adhesive coatings, improve compatibility and solve solvent resistance. Performance, the effect of not easy to bubble

Inactive Publication Date: 2019-04-12
SHUNDE POLYTECHNIC
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These non-reactive system tackifying resins cannot participate in curing to form a cross-linked network, which easily reduces t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant polyurethane hot melt adhesive with excellent water resistance and preparation method of hot melt adhesive

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example one

[0028] It is a flame-retardant polyurethane hot melt adhesive with excellent waterproof performance, which is prepared by the following steps:

[0029] Step 1: Synthesis of hydroxy-terminated phosphorus-containing flame-retardant polyacrylic acid fluorinated copolymer

[0030] Mix 6 parts of trifluoroethyl acrylate TFMA, 15 parts of methyl methacrylate MMA, 25 parts of methoxyethyl methacrylate MMA, and 10 parts of 2-methyl-2-acrylic acid-2-hydroxyethyl The base ester phosphate HMP was dissolved in 50 parts of toluene, controlled at 60°C, under the protection of nitrogen, 2.8 parts of thermal initiator 4,4'-azobis(4-cyanopentanol) was added, and the polymerization reaction was 8 After hours, the toluene is removed by rotary evaporation, and the hydroxyl-terminated phosphorus-containing flame-retardant polyacrylic fluorinated copolymer is obtained. The hydroxyl-terminated phosphorus-containing flame-retardant polyacrylic fluorinated copolymer contains an average ...

Example Embodiment

[0033] Example two

[0034] It is a flame-retardant polyurethane hot melt adhesive with excellent waterproof performance, which is prepared by the following steps:

[0035] Step 1: Synthesis of hydroxy-terminated phosphorus-containing flame-retardant polyacrylic acid fluorinated copolymer

[0036] Combine 12 parts of trifluoroethyl acrylate TFMA, 15 parts of methyl methacrylate MMA, 20 parts of methoxyethyl methacrylate MMA, and 15 parts of 2-methyl-2-acrylic acid-2-hydroxyethyl The base ester phosphate HMP is dissolved in 80 parts of toluene, controlled at 65°C, and under the protection of nitrogen, 1.3 parts of thermal initiator 4,4'-azobis(4-cyanopentanol) are added, and the polymerization reaction is 10 After hours, the toluene was removed by rotary evaporation to obtain a hydroxy-terminated phosphorus-containing flame-retardant polyacrylic fluorinated copolymer. The hydroxyl-terminated phosphorus-containing flame-retardant polyacrylic fluorinated copolymer contains an average o...

Example Embodiment

[0039] Example three

[0040] It is a flame-retardant polyurethane hot melt adhesive with excellent waterproof performance, which is prepared by the following steps:

[0041] Step 1: Synthesis of hydroxy-terminated phosphorus-containing flame-retardant polyacrylic acid fluorinated copolymer

[0042] 16 parts of trifluoroethyl acrylate TFMA, 27 parts of methyl methacrylate MMA, 17 parts of methoxyethyl methacrylate MMA, and 22 parts of 2-methyl-2-acrylic acid-2-hydroxyethyl Base ester phosphate HMP is dissolved in 90 parts of toluene, controlled at 75°C, and under the protection of nitrogen, 0.6 parts of thermal initiator 4,4'-azobis(4-cyanopentanol) is added, and the polymerization reaction is 14 After hours, the toluene is removed by rotary evaporation, and the hydroxyl-terminated phosphorus-containing flame-retardant polyacrylic fluorinated copolymer is obtained. The hydroxyl-terminated phosphorus-containing flame-retardant polyacrylic fluorinated copolymer contains an average of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a flame-retardant polyurethane hot melt adhesive with excellent water resistance and a preparation method of the hot melt adhesive. The hot melt adhesive is characterized by comprising the following components: 5-25 parts of a polyether diol, 1-35 parts of a liquid polyester diol, 1-40 parts of a flame-retardant polyether polyol, 1-50 parts of a crystalline polyester diol,5-40 parts of a hydroxyl-terminated phosphorus-containing flame-retardant polyacrylic acid fluorine-containing copolymer, 10-50 parts of isocyanate, 0.1-2 parts of a catalyst, 0.2-3 parts of an antioxidant and 0.1-4 parts of a silane coupling agent. According to the method provided by the invention, hydroxyl-terminated poly(trifluoroethyl acrylate-random-methyl methacrylate-random-methoxyethyl methacrylate-random-2-methyl-2-acrylic acid-2-hydroxyethyl ester phosphate) is firstly synthesized, the hydroxyl-terminated poly(trifluoroethyl acrylate-random-methyl methacrylate-random-methoxyethyl methacrylate-random-2-methyl-2-acrylic acid-2-hydroxyethyl ester phosphate) is added into a polyurethane prepolymer, a fluorine-containing acrylate copolymer chain segment and a reactive flame retardantare introduced, and therefore the water resistance, chemical resistance and flame retardancy of the polyurethane colloid are further improved.

Description

technical field [0001] The invention belongs to the technical field of structural adhesives, in particular to a flame-retardant polyurethane hot-melt adhesive with excellent waterproof performance and a preparation method thereof, which is mainly used in the electronics and electrical industry, automobile industry, textile and shoemaking industry, food packaging industry, wood materials Structural bonding fields such as processing and furniture industry. Background technique [0002] Polyurethane hot melt adhesive is a new generation of structural adhesive that can provide excellent bonding performance. It is a type of hot melt adhesive made of polyurethane prepolymer as the main material and various additives. Polyurethane hot-melt adhesives are easy to use and environmentally friendly, and their performance is comparable to solvent-based hot-melt adhesives. In the past ten years, polyurethane hot melt adhesives have been rapidly developed and widely used in high-end field...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J175/08C09J11/06C08G18/48C08G18/42C08G18/62
CPCC08G18/4063C08G18/42C08G18/4804C08G18/6225C09J11/06C09J175/08C08K5/54
Inventor 唐秋实刘锋陈燕舞路风辉霍应鹏彭琦林雯雯洪银娜马倩琳
Owner SHUNDE POLYTECHNIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap