High-water-resistance sucker facial tissue and preparation method thereof

A water-based, straw-based technology, applied in the field of papermaking, can solve problems such as ink absorption, achieve good printability, enhance paper strength, and improve the effect of wet strength

Inactive Publication Date: 2019-04-16
ZHEJIANG HENGDA NEW MATERIAL CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a high water resistance straw tissue and its preparation method, to overcome the hydrophilicity of the paper itself and ink absorption probl...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0021] A preparation method of highly water-resistant straw backing paper, comprising the following steps:

[0022] Step 1: Mix and pulp the bleached softwood pulp and bleached hardwood pulp. After disc grinding and beating, the pulp is pumped to the pulp tank, the filler suspension is added and mixed evenly, then pumped to the pulp tank, and nanocellulose is added. , cationic starch and alum, mixed evenly and then pumped to the milling pool. After the slurry is thickened and slag removed, sizing agent is added at the outlet of a section of fine pulp, and wet strength agent, retention aid and stripping agent are continuously added online at the inlet of the pressure screen. After spraying, it enters the headbox;

[0023] Bleached coniferous wood pulp and bleached hardwood pulp are mixed according to the ratio of (4:6)~(7:3), the soaking time before beating is 1~2h, the beating concentration is 4.5~5.0%, and the beating degree is 36~39°SR ;

[0024] The filler suspension is m...

Embodiment 1

[0034]Step 1: Mix and pulp bleached softwood pulp and bleached hardwood pulp in a ratio of 4:6. The soaking time before beating is 1 hour, the beating concentration is 4.5%, and the beating degree is 39°SR. The material is pumped to the slurry tank; add talcum powder filler suspension, the suspension concentration is 8%, and the filling amount is 5%, and after mixing evenly, pump it to the slurry tank; add TEMPO oxidized microfibrillated cellulose 0.3% ( For absolute dry fiber consumption), cationic starch 0.3% (for absolute dry fiber consumption) and alum 0.2% (for absolute dry fiber consumption), after mixing evenly, pump it to the papermaking pool; Add 0.6% of anion-dispersed rosin glue (for absolute dry fiber) at the outlet of good pulp; continuously add 0.4% of polyamide epichlorohydrin (for absolute dry fiber) and 0.05% of polyacrylamide (for absolute dry fiber) at the inlet of the pressure screen fiber consumption) and cationic polymer wax emulsion 0.01% (to absolute dr...

Embodiment 2

[0038] Step 1: Mix and pulp bleached softwood pulp and bleached hardwood pulp in a ratio of 5:5. The soaking time before beating is 1.5 hours, the beating concentration is 4.6%, and the beating degree is 36°SR. After disc grinding and beating, Pump the slurry to the slurry tank; add kaolin filler suspension, the suspension concentration is 12%, and the filling amount is 10%, mix well and pump to the slurry tank; add esterified modified microfibrillated cellulose 0.2 % (to the absolute dry fiber dosage), 0.4% cationic starch (to the absolute dry fiber dosage) and 0.15% of alum (to the absolute dry fiber dosage), mix well and then pump to the papermaking pool; after the slurry is thickened and slag removed, Add 0.4% of anion-dispersed rosin gum (to the absolute dry fiber consumption) at the outlet of a section of good pulp; continuously add 0.5% of polyamide epichlorohydrin (to the absolute dry fiber consumption) and 0.07% of polyacrylamide (to the absolute dry fiber consumption)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-water-resistance sucker facial tissue and a preparation method thereof. The high-water-resistance sucker facial tissue comprises the following steps that 1, bleached needle wood pulp and hardwood pulp are mixed to be beat, filling, nano-crystalline cellulose, a sizing agent, a wet strength agent, a retention aid and others are added, and fiber pulp capable of being loaded onto a net can be prepared through residue removal and adjustment for thickening; 2, after being formed and squeezed by a fourdrinier wire paper machine, the fiber pulp is rapidly dried through alarge-diameter drying cylinder, starch and a binary surface sizing agent of polyamide polyurea resin are compounded to conduct a surface sizing process, and the high-water-resistance sucker facial tissue is prepared through drying, press polish and rolling. The prepared sucker facial tissue has good water resistance and wet strength, and can effectively prevent liquid from permeating and have goodink adaptability, and all indexes meet the safety standards of national food package materials.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a highly water-resistant straw tissue and a preparation method thereof. Background technique [0002] With the improvement of economic level and quality of life, food packaging materials are widely used in commodities, which also brings about the increasingly serious problem of white pollution. Polystyrene, polypropylene, polyvinyl chloride and other plastic products are difficult to degrade after being discarded, causing serious pollution to the environment. With the implementation of the national ban on plastics, plastic tableware is gradually eliminated by the market. Paper materials are an excellent substitute for plastics due to their recyclable and degradable advantages. In recent years, it has gradually seized the food packaging market and has a broad prospect. [0003] Plastic has always been the main material for straws due to its good plasticity and thermosetting ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H17/25D21H17/29D21H17/66D21H21/06D21H21/10D21H21/20D21H17/67
CPCD21H17/25D21H17/29D21H17/66D21H17/67D21H21/06D21H21/10D21H21/20
Inventor 伊财富徐冰丁济正杨菊红张海波
Owner ZHEJIANG HENGDA NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products