Emulation flower composite material, and preparation method thereof
A composite material and flower technology, which is applied in the field of simulated flower composite materials and its preparation, can solve the problems affecting the overall performance of flowers, poor hand feel and gloss, excessive distortion of flowers, etc., and achieve perfect mechanism system, good gloss, and improved The effect of mechanical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0029] A simulated flower composite material of the present embodiment includes the following raw materials by weight:
[0030] 50 parts of TPE, 10 parts of EVA, 10 parts of PE, 10 parts of organic rice husk ash, 4 parts of organic fillers, 2 parts of nano titanium dioxide, 5 parts of graphene, 3 parts of modified masterbatch, 1 part of clay powder, casein 1 part of solution and 15 parts of octamethylcyclotetrasiloxane.
[0031] The preparation method of the organic rice husk ash of the present embodiment is that the rice husk is first fired at a temperature of 800° C. to obtain rice husk ash, and then the rice husk ash is mixed with γ-aminopropyl methyl dimethoxy The base silane was added to the reaction kettle according to the weight ratio of 1:3, the reaction pressure was 2MPa, the reaction temperature was 85°C, and then a magnetic field was introduced for a time of 40s, the reaction was completed, and then washed with water to obtain organic rice husks Ash.
[0032] The ...
Embodiment 2
[0041] A simulated flower composite material of the present embodiment includes the following raw materials by weight:
[0042] 80 parts of TPE, 30 parts of EVA, 30 parts of PE, 20 parts of organic rice husk ash, 8 parts of organic fillers, 5 parts of nano titanium dioxide, 10 parts of graphene, 6 parts of modified masterbatch, 3 parts of clay powder, casein 2 parts of solution and 25 parts of octamethylcyclotetrasiloxane.
[0043] The preparation method of the organic rice husk ash of the present embodiment is that the rice husk is first fired at a temperature of 1200° C. to obtain rice husk ash, and then the rice husk ash is mixed with γ-aminopropyl methyl dimethoxy The base silane was added to the reaction kettle at a weight ratio of 1:3, the reaction pressure was 3MPa, the reaction temperature was 95°C, and then a magnetic field was introduced for a time of 60s, the reaction was completed, and then washed with water to obtain organic rice husks Ash.
[0044] The magnetic...
Embodiment 3
[0053] A simulated flower composite material of the present embodiment includes the following raw materials by weight:
[0054] 65 parts of TPE, 20 parts of EVA, 20 parts of PE, 15 parts of organic rice husk ash, 6 parts of organic filler, 3.5 parts of nano titanium dioxide, 7.5 parts of graphene, 4.5 parts of modified masterbatch, 2 parts of clay powder, casein 1.5 parts of solution and 20 parts of octamethylcyclotetrasiloxane.
[0055] The preparation method of the organic rice husk ash of the present embodiment is that the rice husk is first fired at a temperature of 1000° C. to obtain rice husk ash, and then the rice husk ash is mixed with γ-aminopropyl methyl dimethoxy The base silane was added to the reaction kettle at a weight ratio of 1:3, the reaction pressure was 2.5 MPa, and the reaction temperature was 90 °C, and then a magnetic field was introduced for 50 s, the reaction was completed, and then washed with water to obtain organic rice. Shell ash.
[0056] The ma...