Heat insulation polyurethane wood paint and preparation method thereof

A technology of heat insulation and polyurethane paint, applied in the direction of coating, etc., can solve the problems of low heat insulation performance and chemical stability, reduce the possibility of spots and spots, high opacity, improve leveling and The effect of uniformity

Inactive Publication Date: 2019-05-10
广东顺德三阳化学有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides a preparation method of heat-insulating polyurethane wood lacquer, which has the advantages of being able to effectively improve the heat-insulating and heat-insulating performance of polyurethane wood lacquer, and solves the problems of heat-insulating and heat-preserving polyurethane wood lacquer. Problems with low performance and chemical stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: A heat-insulating polyurethane wood paint, comprising the following raw materials in proportions by weight: 6 parts of defoaming agent, 16 parts of polyvinylidene fluoride, 7 parts of leveling agent, 15 parts of pitch-based carbon fiber, and dispersant 5 parts, 24 parts of titanium dioxide, 4 parts of drier, 20 parts of aluminum carbonate fiber, 3 parts of coupling agent and 30 parts of polyurethane paint thinner. The polyurethane paint thinner is composed of cyclohexanone, butyl acetate and xylene according to Made with ratios of 0.7, 0.9 and 1.2.

[0024] Another technical problem to be solved by the present invention is to provide a preparation method of heat-insulating polyurethane wood varnish, comprising the following steps:

[0025] 1) Add 30 parts of polyurethane paint thinner, 24 parts of titanium dioxide and 7 parts of leveling agent into the dispersion tank in sequence and stir with a mixer, mix and stir for ten minutes at a speed of 1000 rpm, a...

Embodiment 2

[0029]Embodiment 2: A heat-insulating polyurethane wood paint, comprising the following raw materials in proportions by weight: 5 parts of defoaming agent, 15 parts of polyvinylidene fluoride, 6 parts of leveling agent, 10 parts of pitch-based carbon fiber, and dispersant 4 parts, 22 parts of titanium dioxide, 3 parts of drier, 18 parts of aluminum carbonate fiber, 2 parts of coupling agent and 25 parts of polyurethane paint thinner, polyurethane paint thinner is made of cyclohexanone, butyl acetate and xylene according to Made in ratios of 0.4, 0.7 and 1.1.

[0030] Another technical problem to be solved by the present invention is to provide a preparation method of heat-insulating polyurethane wood varnish, comprising the following steps:

[0031] 1) Add 25 parts of polyurethane paint thinner, 22 parts of titanium dioxide and 6 parts of leveling agent into the dispersion tank in sequence and stir with a mixer, mix and stir for ten minutes at a speed of 1000 rpm, and reserve ...

Embodiment 3

[0035] Embodiment 3: A heat-insulating polyurethane wood paint, including the following raw materials in proportions by weight: 7 parts of defoaming agent, 7 parts of polyvinylidene fluoride, 8 parts of leveling agent, 20 parts of pitch-based carbon fiber, and dispersant 6 parts, 26 parts of titanium dioxide, 5 parts of drier, 22 parts of aluminum carbonate fiber, 4 parts of coupling agent and 35 parts of polyurethane paint thinner, polyurethane paint thinner is made of cyclohexanone, butyl acetate and xylene according to 1, 1.1 and 1.3 ratios are made.

[0036] Another technical problem to be solved by the present invention is to provide a preparation method of heat-insulating polyurethane wood varnish, comprising the following steps:

[0037] 1) Add 35 parts of polyurethane paint thinner, 26 parts of titanium dioxide and 8 parts of leveling agent into the dispersion tank in sequence and stir with a mixer, mix and stir for ten minutes at a speed of 1000 rpm, and reserve the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of coatings, and discloses heat insulation polyurethane wood paint which comprises, by weight, 5-7 parts of defoaming agents, 15-17 parts of polyvinylidenefluoride, 6-8 parts of leveling agents, 10-20 parts of pitch-based carbon fibers, 4-6 parts of dispersing agents, 22-26 parts of titanium dioxide, 3-5 parts of driers, 18-22 parts of aluminum carbonate fibers, 2-4 parts of coupling agents and 25-35 parts of polyurethane paint thinners. The heat insulation performance and the chemical stability of the heat insulation polyurethane wood paint can beeffectively improved, the service life of the wood paint can be effectively prolonged, the wood paint has excellent wear resistance and flexibility, high tensile strength and impact resistance, excellent ultraviolet resistance, high energetic radiation property, oxidation resistance and chemical stability and excellent weather resistance, the drying speed of the heat insulation polyurethane woodpaint can be effectively increased, construction progress is accelerated, construction efficiency is increased, and the use performance of the wood paint can be effectively improved.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a heat-insulating polyurethane wood varnish and a preparation method thereof. Background technique [0002] Wood paint refers to a type of resin paint used on wood products, including polyester and polyurethane paint, which can be divided into water-based and oil-based, and can be divided into high-gloss, semi-matte and matte according to gloss, and can be divided into furniture according to use. Lacquer and floor paint, etc. Natural wood lacquer is commonly known as lacquer, and it is also known as "national lacquer". The juice cut from the lacquer tree is called raw lacquer or original barrel lacquer, and the white cloth to filter out impurities is called raw lacquer. [0003] Polyurethane paint is polyurethane paint. It has strong paint film, full luster, strong adhesion, water resistance, wear resistance and corrosion resistance. It is widely used in high-grade wood furnitur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/16C09D7/20C09D7/61
Inventor 任国华宋林娜
Owner 广东顺德三阳化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More